Machining forming manufacturing method for glass tin bath made of 5Cr2NiMnVSi magnesium alloy

A manufacturing method and processing and forming technology are applied in the field of processing and forming of Cr2NiMnVSi magnesium alloy and its glass tin bath, and glass tin bath. Easy maintenance, good corrosion resistance, good performance

Inactive Publication Date: 2016-05-18
WUXI HUAYE IRON & STEEL
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the past, glass tin baths were usually severely corroded due to unreasonable materials. Due to the high temperature of the glass liquid, a large amount of heat was generated, so the tin baths had a short life and needed to be replaced continuously, which stopped production and caused Huge loss of silence. At the same time, the tin bath is made of steel, which is of high quality. It is inconvenient for installation and maintenance, and the cost is still high. Therefore, the consumables are serious and the economic benefits are not good. Some companies have improved this steel tin bath. That is, after the tin bath is processed, aluminum oxide is sprayed on its instant noodles. Although the corrosiveness has been improved, the economic benefits have not been reduced in material application, and it is still difficult to overhaul and install, and there are still complex processes, high cost and poor quality. overweight problem,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] A manufacturing method for processing and forming a glass tin bath, the glass tin bath is made of 5Cr2NiMnVSi magnesium alloy, and its composition percentage content is: C1.74%, Ti0.37%, Sn2.62%, Mn0.42%, Cr1. 3%, Mo0.9%, Fe1.25%, V0.54%, Ni0.4%, and the rest are magnesium and its impurities. The following processing technology is adopted: (1) The glass tin bath blank is cast by integral casting method, Preparation of charge - smelting alloy - preheating mold - pouring - falling sand, the preheating mold temperature is 700 ° C, the pouring temperature is 1000 ° C, compacted by sand blasting method, (2) for the cast glass tin bath blank Carry out recrystallization annealing treatment, heat it to 800°C, keep it warm for 6-10h, slowly cool in the furnace to 500°C, and then quickly water-cool to recrystallize the deformed grains into uniform equiaxed grains, (3) After annealing The glass tin bath is used for milling and then finishing. Grinding is used. During the processin...

Embodiment 2

[0009] A method for manufacturing a glass tin bath. The glass tin bath is made of 5Cr2NiMnVSi magnesium alloy, and its composition percentages are: C1.93%, Ti0.57%, Sn3.87%, Mn0.54%, Cr4. 0%, Mo1.1%, Fe1.89%, V0.67%, Ni0.7%, and the rest are magnesium and its impurities. The following processing technology is adopted: (1) The glass tin bath blank is cast by integral casting method, Preparation of charge - smelting alloy - preheating mold - pouring - falling sand, preheating mold temperature is 750 ° C, pouring temperature is 1200 ° C, compacted by sand blasting method, (2) for the cast glass tin bath blank Carry out recrystallization annealing treatment, heat it to 840°C, keep it warm for 10h, slowly cool in the furnace to 560°C, and then quickly water-cool to recrystallize the deformed grains into uniform equiaxed grains. (3) For the annealed glass The tin bath is milled and then finished. Grinding is used. During the process, ice particles are sprayed to the cutting surface ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a machining forming manufacturing method for a glass tin bath made of 5Cr2NiMnVSi magnesium alloy and belongs to the technical field of machinery manufacturing. The machining forming manufacturing method for the glass tin bath is achieved through the following processes of blank casting, de-stressing, machining, quenching and high-temperature tempering, polishing and anticorrosion rust-proof treatment. According to the glass tin bath prepared through the manufacturing method, machining is easy, the structure is more reasonable, and the corrosion resistance and the oxidation resistance are improved greatly; the mechanical property is good, the service life is longer, the sealing performance is good, and the service life of the glass tin bath is further prolonged; the glass tin bath is suitable for high-speed and low-speed textile machinery, stable in work and high in reliability.

Description

technical field [0001] The method belongs to the technical field of mechanical manufacturing, and relates to a Cr2NiMnVSi magnesium alloy and a glass tin bath thereof. In particular, a method for processing and forming a glass tin bath made of 5Cr2NiMnVSi magnesium alloy material. Background technique [0002] In the past, glass tin baths were usually severely corroded due to unreasonable materials. Due to the high temperature of the glass liquid, a lot of heat was generated, so the tin baths had a short life and needed to be replaced continuously, which stopped production and caused Huge loss of silence. At the same time, the tin bath is made of steel, which is of high quality. It is inconvenient for installation and maintenance, and the cost is still high. Therefore, the consumables are serious and the economic benefits are not good. Some companies have improved this steel tin bath. That is, after the tin bath is processed, aluminum oxide is sprayed on the instant noodles...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C23/00C23F17/00B23P15/00C03B18/16
Inventor 张明
Owner WUXI HUAYE IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com