Satin nickel solution and nickel plating process thereof

A satin nickel solution technology, which is applied in the field of electroplating nickel, can solve the problems of insufficient adhesion strength, softness, and poor gloss effect of the satin nickel coating

Inactive Publication Date: 2016-05-25
YIDONG ELECTRONICS CHANGSHU
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the satin nickel coating still has the phenomenon of insufficient adhesion strength, poor gloss effect, and not soft

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Nickel satin solution comprises the following formula: nickel sulfate, weight ratio 280g / L; nickel chloride, weight ratio 42g / L; boric acid, weight ratio 31g / L; brightener propynyl alcohol propoxy compound, volume ratio 3ml / L L, to provide better gloss and flatness for the coating; the surfactant succinate salt anionic surfactant, with a volume ratio of 8ml / L, makes the satin nickel coating produce a pearlescent effect; the softener propynyl sodium sulfonate , the volume ratio is 1ml / L, which helps to improve the gloss of the coating in the low current density area; the displacement agent sodium allyl sulfonate, the volume ratio is 2ml / L, which makes the satin nickel coating more uniform and reduces the probability of missing plating .

[0023] In order to ensure the nickel plating effect of the satin nickel solution, the nickel plating process includes the following steps:

[0024] Step 1, using 500 mesh sand to carry out frosting treatment on the surface of the mater...

Embodiment 2

[0027] Nickel satin solution comprises the following formulations: nickel sulfate, weight ratio 380g / L; nickel chloride, weight ratio 58g / L; boric acid, weight ratio 38g / L; brightener propanesulfonic acid pyridinium salt, volume ratio 7ml / L , to provide better gloss and smoothness for the coating; the surfactant is composed of succinate salt anionic surfactant, carboxylate anionic surfactant, and quaternary ammonium salt anionic surfactant, and the addition ratio is 5 :2:3, the total volume ratio of the three surfactants is 15ml / L, which makes the satin nickel coating produce a pearlescent effect; the softener sodium propynyl sulfonate, with a volume ratio of 5ml / L, helps to improve the low current density area Glossiness of the coating; sodium salt of hydroxyl compound sulfonate as a displacement agent, with a volume ratio of 2ml / L, which makes the satin nickel coating more uniform and reduces the probability of missing plating.

[0028] In order to ensure the nickel plating ...

Embodiment 3

[0032] Nickel satin solution, including the following formulations: nickel sulfate, weight ratio 340g / L; nickel chloride, weight ratio 53g / L; boric acid, weight ratio 34g / L; brightener diethylpropargylamine sulfate, volume ratio 4.2 ml / L, to provide better gloss and smoothness for the coating; the surfactant is composed of succinate salt anionic surfactant, carboxylate anionic surfactant, quaternary ammonium salt anionic surfactant, adding The ratio is 5:2:3, the total volume ratio of the three surfactants is 10ml / L, which makes the satin nickel coating produce a pearlescent effect; the softener propynyl sulfonate, the volume ratio is 2ml / L, which helps to improve the The glossiness of the coating in the current density area; the displacement agent hydroxyethyl isothiourea internal salt, the volume ratio is 2.5ml / L, which makes the satin nickel coating more uniform and reduces the probability of missing plating; the water-soluble fiber, the weight ratio is 1g / L, length 2mm, i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a satin nickel solution and a nickel plating process thereof. The formula of the satin nickel solution comprises the following components in proportion by weight and volume: 280g / L-380g / L of nickel sulfate, 42g / L-58g / L of nickel chloride, 31g / L-38g / L of boric acid, 3ml / L-7ml / L of a brightener, 8ml / L-15ml / L of a surfactant, 1ml / L-5ml / L of a softening agent, 2ml / L-4ml / L of a walking agent, and 0.2g / L-10g / L of water soluble fiber, wherein the length of the water soluble fiber is 2mm-4mm. For guaranteeing the nickel plating effect of the satin nickel solution, the nickel plating process comprises the following steps: (1) polishing the surface of the to-be-nickel plated material by virtue of 500-1000-mesh sand, so as to increase the specific surface area and roughness of the surface of the to-be-nickel plated material and the adhesive force of a satin nickel plated layer; and (2) carrying out surface nickel plating by taking the to-be-nickel plated material as a cathode and a nickel plate as an anode, so as to guarantee the use effects of the brightener, the surfactant, the softening agent, the walking agent and the water soluble fiber, wherein the temperature is controlled at 42-48 DEG C, the pH value is controlled at 3-5, and the electric current density is controlled at 3A / dm<2>-8A / dm<2>.

Description

technical field [0001] The invention relates to the field of electroplating nickel, in particular to a nickel satin solution and a nickel plating process thereof. Background technique [0002] Sardine nickel, also known as pearl nickel, satin nickel, pitted nickel, is a coating with gorgeous appearance, fine and soft color, low internal stress and good corrosion resistance. It is a good protective decorative coating. The satin nickel plating process first appeared in the 1950s and developed rapidly after the 1990s. Sardine nickel can be directly used as a protective decorative coating, or it can be plated with other metals on the pearl nickel, such as chromium, gold, silver, etc., and its protective decorative effect is stronger. At present, satin nickel coating has been widely used in automobile decoration, electronic products, daily hardware, stationery and other industries. [0003] At present, the satin nickel coating still has the phenomenon of insufficient adhesion s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/16C25D3/12C25D5/34
CPCC25D3/16C25D3/12C25D5/34
Inventor 夏红禄
Owner YIDONG ELECTRONICS CHANGSHU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More