Light wear-resisting plastic material and preparing method thereof

A wear-resistant plastic and light-weight technology, applied in the field of materials, can solve the problems that the materials cannot meet the production performance and the wear resistance needs to be further improved, and achieve the effect of good toughness, good mechanical properties and excellent wear resistance

Inactive Publication Date: 2016-06-15
SUZHOU FUZHONG PLASTIC CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the most widely used material, plastic material has the advantages of light weight, strong chemical stability and easy processing and molding, but its wear resistance needs to be further improved
And with the continuous progress of all walks of life, a single material can no longer meet the needs of production performance. Therefore, it is necessary to improve its performance through the compounding of materials, and to make up for their respective deficiencies by optimizing the ratio of materials. Excellent performance to meet special needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A light wear-resistant plastic material, prepared from the following ingredients in parts by weight: 10 parts of polyether ether ketone, 20 parts of ultra-high molecular weight polyethylene, 20 parts of high-density polyethylene, 2 parts of stearamide, mullite 2 parts of powder, 1 part of calcium stearate, 1 part of nano-zinc oxide, 2 parts of γ-aminopropyltriethoxysilane, 1 part of γ-mercaptopropyltrimethoxysilane, 1 part of vinyltriethoxysilane 0.2 parts of dibutyl phthalate, 0.2 parts of dimethyl phthalate, 2 parts of isoamyl alcohol, 30 parts of absolute ethanol, and 20 parts of acetone.

[0023] The preparation method of the above-mentioned lightweight wear-resistant plastic material is as follows: first mix γ-aminopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, absolute ethanol and acetone, and use a magnetic stirrer at a speed of 60r / min Stir at low temperature for 20 minutes, then add mullite powder and nano-zinc oxide, stir for 20 minutes at a temperat...

Embodiment 2

[0025] A lightweight wear-resistant plastic material, prepared from the following ingredients in parts by weight: 12 parts of polyether ether ketone, 23 parts of ultra-high molecular weight polyethylene, 25 parts of high-density polyethylene, 3 parts of stearamide, mullite 3 parts of powder, 1.2 parts of calcium stearate, 1.5 parts of nano-zinc oxide, 3 parts of γ-aminopropyltriethoxysilane, 1.5 parts of γ-mercaptopropyltrimethoxysilane, 1.2 parts of vinyltriethoxysilane 0.25 parts of dibutyl phthalate, 0.3 parts of dimethyl phthalate, 3 parts of isoamyl alcohol, 35 parts of absolute ethanol, and 25 parts of acetone.

[0026] The preparation method of the above-mentioned lightweight wear-resistant plastic material is as follows: first mix γ-aminopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, absolute ethanol and acetone, and use a magnetic stirrer at a speed of 65r / min. Stir at low temperature for 25 minutes, then add mullite powder and nano-zinc oxide, stir for 30 m...

Embodiment 3

[0028] A light wear-resistant plastic material, prepared from the following ingredients in parts by weight: 15 parts of polyether ether ketone, 25 parts of ultra-high molecular weight polyethylene, 30 parts of high-density polyethylene, 2-5 parts of stearamide, molybdenum 3.5 parts of stone powder, 1.5 parts of calcium stearate, 2 parts of nano-zinc oxide, 3.5 parts of γ-aminopropyl triethoxysilane, 2 parts of γ-mercaptopropyl trimethoxysilane, vinyl triethoxy 1.5 parts of silane, 0.3 parts of dibutyl phthalate, 0.35 parts of dimethyl phthalate, 3.5 parts of isoamyl alcohol, 40 parts of absolute ethanol, and 30 parts of acetone.

[0029] The preparation method of the above-mentioned lightweight wear-resistant plastic material is as follows: first mix γ-aminopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, absolute ethanol and acetone, and use a magnetic stirrer at a speed of 70r / min Stir at low temperature for 30 minutes, then add mullite powder and nano-zinc oxide, st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a light wear-resisting plastic material and a preparing method thereof.The material is prepared through the steps that at first, gamma-aminopropyltriethoxysilane, gamma-trimethoxysilylpropanethiol, absolute ethyl alcohol and acetone are mixed and stirred through a magnetic stirring machine, then mullite powder and nanometer zinc oxide are added, and the mixture stands after being stirred, and is filtered, placed into an oven to be baked, and smashed to obtain powder; the components are mixed with polyetheretherketone, ultra-high molecular weight polyethylene, high-density polyethylene, stearamide, calcium stearate, vinyltriethoxysilane, dibutyl phthalate, dimethyl phthalate and isoamyl alcohol, dispersed through a high-speed dispersing machine, placed into the oven to be baked, then smashed, added into a double-screw extruder to be extruded and palletized, and finally loaded into an injection molding machine to be molded in an injection mode, so that the material is obtained.The light wear-resisting plastic material has the very good mechanical performance, the very good toughness and the excellent wear-resisting performance.

Description

technical field [0001] The invention relates to the field of materials, in particular to a lightweight wear-resistant plastic material and a preparation method thereof. Background technique [0002] With the rapid development of modern science and technology, the demand for materials from all walks of life is increasing, and the requirements for various performance indicators of materials are also getting higher and higher. As the most widely used material, plastic material has the advantages of light weight, strong chemical stability and easy processing and molding, but its wear resistance needs to be further improved. And with the continuous progress of all walks of life, a single material can no longer meet the needs of production performance. Therefore, it is necessary to improve its performance through the compounding of materials, and to make up for their respective deficiencies by optimizing the ratio of materials. Excellent performance to meet special needs. The in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L61/16C08K13/06C08K9/06C08K3/34C08K5/098C08K3/22C08K5/12
CPCC08L23/06C08K2201/011C08K2201/014C08L2205/025C08L2205/03C08L2207/062C08L2207/068C08L61/16C08K13/06C08K9/06C08K3/34C08K5/098C08K2003/2296C08K5/12
Inventor 史闵新
Owner SUZHOU FUZHONG PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com