Large-size ceramic decorative sheet and formula process

A large-scale, formula-based technology, applied in covering/lining, construction, building construction, etc., can solve the problems of specification constraints, not much progress, and many wall joints, so as to improve construction efficiency and fast construction speed , the effect of fewer seams

Active Publication Date: 2016-06-15
MANLEY CHINA
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After a long history of development, architectural ceramics have introduced many modern technologies, and their quality, specifications and colors have made considerable progress, but the specifications have been restricted by technology and have not made much progress.
Due to the constraints of the specifications, there are too many joints on the decorated wall, which cannot give people a sense of integrity as much as possible.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large-size ceramic decorative sheet and formula process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] Embodiment: First, the raw materials are prepared according to the proportion, and then the raw materials are added with water and put into a ball mill to grind into a high-fineness slurry. After the slurry is ground, it is sent to the powder drying tower for spray drying after being sieved to remove iron, and the dried The powder is dry-pressed on the mold by a large hydraulic machine, and the formed large-scale ceramic plate body is sent to a drying kiln for drying; the ceramic body that has reached a certain degree of dryness is coated with the glaze bottom layer 2 and then the pattern layer 3 Inkjet printing, followed by a glaze finish 4. Finally, the large-scale ceramic slab body that has completed the previous process is sent to the roller kiln to be fired into a large-scale ceramic decorative sheet including the body layer 1, the glazed bottom layer 2, the pattern layer 3 and the glazed surface layer 4, and then After edging, sorting and packaging, it can be put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a large-size ceramic decorative sheet and a formula process.The large-size ceramic decorative sheet comprises a blank layer and a glaze layer.The blank layer comprises a front side and an adhesive side, the front side is a plane, and the adhesive side is a concave-convex side with grooves.The specification of the blank layer is at least 900 mm*1800 mm, and the thickness of the blank layer is 5.5 mm.The glaze layer comprises a glaze bottom layer, a pattern layer and a glaze surface layer, the front side of the blank layer is evenly covered with the glaze bottom layer, the pattern layer is printed on the upper side of the glaze bottom layer, the pattern layer and the glaze bottom layer are covered with the glaze surface layer, and the thickness of the glaze layer is at least 0.3 mm.Formulas include a blank layer formula, a glaze bottom layer formula and a glaze surface layer formula.Pressure of dry pressing in the technological process is 240 MPa, drying temperature is 120-286 DEG C, the drying period is 62 min, upper temperate of firing temperature is 1196 DEG C, lower temperature of firing temperature is 1193 DEG C, and the sintering period is 73 min.

Description

technical field [0001] The invention relates to a ceramic plate, in particular to a large-scale ceramic decorative thin plate and a formula process, belonging to the technical field of the ceramic industry. Background technique [0002] Architectural ceramics are already one of the important building decoration materials that are widely known to everyone. In the family of architectural ceramics, there are many varieties of designs and colors. It is not an exaggeration to describe them as exquisite. After a long history of development, architectural ceramics have introduced many modern technologies, and their quality, specifications and colors have made considerable progress, but the specifications have been restricted by technology and have not made much progress. Due to the constraints of the specifications, there are too many joints on the decorated wall, which cannot give people a sense of integrity as much as possible. Contents of the invention [0003] In order to so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F13/077C04B35/195C04B41/89C03C8/00
CPCC03C8/00C04B35/195C04B41/009C04B41/52C04B41/89C04B2235/3217C04B2235/3427C04B2235/349C04B2235/48E04F13/0866C04B41/504C04B41/5022
Inventor 程石明任富国李利方
Owner MANLEY CHINA