Songguan Yuebai Ge kiln glaze material

Abstract

The invention relates to porcelain, in particular to a preparation method of Ge porcelain, comprising the steps: preparing glaze material: according to parts by weight, comprising 200-500 parts of Baoxi Wutou glaze earth, 70-100 parts of quartz powder, 20-50 parts of Mudaikou purple clay, 180-230 parts of limestone, 150-200 parts of potassium feldspar, 100-170 parts of kaolin and 80-100 parts of talcum powder, ball-milling to obtain powder 120-200 in mesh; preparing a clay base, forming a porcelain base, drying, biscuiting, applying inner and outer glaze, and burning the glaze to obtain a finished product. The method is characterized in that the glaze material in step 1 also comprises 1-100 parts of graphene and 1-100 parts of dysprosium oxide.

Description

technical field [0001] The invention belongs to the field of porcelain, and in particular relates to a Song Guanyue Baige kiln glaze. Background technique [0002] Ge Kiln is one of the five famous kilns in the Song Dynasty. There is such a description in "Ge Gu Yao Lun" in the Ming Dynasty: "Ge Kiln patterns take ice cracks and eel blood as the top, followed by plum blossom ink patterns. "Unfortunately, the kiln site of Song Ge Kiln has not been discovered by people so far. We can only interpret the history of Ge Kiln from the handed down works. The important feature of Ge glaze porcelain is the glaze cracking, which is a natural cracking phenomenon that occurs on the glaze. Cracking was originally a defect in the firing of porcelain. Later, people mastered the law of cracking and consciously made it crack, thus producing a unique aesthetic feeling. The enamel of the Ge glaze porcelain in the Song Dynasty is shiny and smooth, and the glaze surface of the whole body is int...

AI Technical Summary

Problems solved by technology

[0005] At present, in the porcelain of Fangge Kiln, the probability of ice cracking and eel blood is very low, and most of them are fine grains. The mechanism is still unknown