Graphene in-situ modified polyurethane and method for manufacturing synthetic leather with high physical properties
A technology of graphene modification and in-situ modification, which is applied in textiles and papermaking, can solve the problems of inability to improve the performance of polyurethane and synthetic leather, and achieve obvious innovation, improve quality level, and improve heat resistance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example 1: Manufacture of dry synthetic shoe upper leather
[0032] (1) Modification of graphene (parts by weight)
[0033] Add 10 parts of enhanced graphene to 90 parts of propylene glycol methyl ether acetate, add 10 parts of KH-550 silicone coupling agent, and react at 70°C for 24 hours to obtain lipophilic modified graphene;
[0034] (2) Preparation of graphene in-situ modified polyurethane slurry (parts by weight);
[0035] ① Preparation of surface treatment agent: add 1.0 part of modified graphene to 100 parts of polyurethane for surface treatment with a solid content of 20%, appropriate amount of wetting and leveling agent, defoamer, thickener and other additives and color paste to mix evenly , To obtain the surface treatment agent modified in situ of graphene;
[0036] ②Preparation of surface layer slurry: In 100 parts of polyurethane solution for surface layer with 30% solid content, add 0.5 part of modified graphene, appropriate amount of leveling agent, defoamer, thic...
Example Embodiment
[0042] Example 2: Manufacturing of wet synthetic sofa leather
[0043] (1) Modification of graphene (parts by weight)
[0044] Add 5 parts of enhanced graphene and 5 parts of thermally conductive graphene to 90 parts of dimethylformamide, 5 parts of KH-560 silicone coupling agent, and react at 70°C for 24 hours to obtain lipophilic modified graphene ;
[0045] (2) Preparation of graphene in-situ modified polyurethane slurry (parts by weight);
[0046] ①Preparation of surface treatment agent: add 0.8 part of modified graphene to 100 parts of polyurethane for surface treatment with 25% solid content, appropriate amount of wetting and leveling agent, defoamer, thickener and other additives and color paste are mixed evenly , To obtain the surface treatment agent modified in situ of graphene;
[0047] ②Preparation of surface layer slurry: in 100 parts of polyurethane solution for surface layer with 30% solid content, add 0.4 part of modified graphene, appropriate amount of leveling agent,...
Example Embodiment
[0053] Example 3: Manufacturing of dry-process car seat leather
[0054] (1) Modification of graphene (parts by weight)
[0055] Add 10 parts of enhanced graphene to 45 parts of propylene dimethyl formamide and 45 parts of glycol methyl ether acetate, add 10 parts of KH-602 silicone coupling agent, and react at 70°C for 24 hours to obtain lipophilic modification. Sexual graphene;
[0056] (2) Preparation of graphene in-situ modified polyurethane slurry (parts by weight);
[0057] ① Preparation of surface treatment agent: add 0.7 part of modified graphene to 100 parts of polyurethane for surface treatment with 20% solid content, appropriate amount of wetting and leveling agent, defoamer, thickener and other additives, and color paste are mixed evenly , To obtain the surface treatment agent modified in situ of graphene;
[0058] ②Preparation of surface layer slurry: In 100 parts of polyurethane solution for surface layer with 30% solid content, add 0.5 part of modified graphene, approp...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap