FDY/POY different shrinkage combined filament yarn of biomass nylon 56 fiber/PET fiber and preparing method thereof

A technology of different shrinkage mixed fiber yarn and biomass nylon, which is applied in the direction of conjugated synthetic polymer artificial filament, etc., can solve the problems of poor hydrophilicity and softness of polyester, and achieve the improvement of fiber hydrophilicity and softness, and good mechanical properties performance, effect of good hydrophilic properties

Inactive Publication Date: 2016-07-27
DONGHUA UNIV +2
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] What the present invention is to solve is the problem of poor hydrophilicity and softness of polyester

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • FDY/POY different shrinkage combined filament yarn of biomass nylon 56 fiber/PET fiber and preparing method thereof
  • FDY/POY different shrinkage combined filament yarn of biomass nylon 56 fiber/PET fiber and preparing method thereof
  • FDY/POY different shrinkage combined filament yarn of biomass nylon 56 fiber/PET fiber and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A different shrinkage mixed fiber yarn in which biomass nylon 56 fiber is FDY fiber and PET fiber is POY fiber, and the mass ratio of biomass nylon 56 fiber and PET fiber is 1:9.

[0023] use as figure 1 The shown device prepares different shrinkage mixed filaments:

[0024] Biomass nylon 56 slices were crystallized at 130°C for 0.5h and dried at 150°C for 8h under the protection of nitrogen, and then melted and extruded into the spinning box at 270-290°C by a screw extruder. The temperature of the spinning box was 280°C. After being extruded and cooled by the second spinning assembly 4, the temperature of the first hot roller 5 is 60° C., and the speed is 1000 m / min. Then the temperature of the second hot roller 5' is 100°C, and the speed is 2800m / min to form a fully drawn yarn (FDY), and the fully drawn yarn is input into the doubling device 6. PET chips are crystallized at 150°C for 0.5h, dried at 160°C for 8h, melted and extruded by a screw extruder at 280°C to 30...

Embodiment 2

[0026] A kind of different shrinkage mixed fiber yarn in which biomass nylon 56 fiber is FDY fiber and PET fiber is POY fiber, and the mass ratio of biomass nylon 56 fiber and PET fiber is 1:1.

[0027] use as figure 1 The shown device prepares different shrinkage mixed filaments:

[0028] Biomass nylon 56 slices were crystallized at 130°C for 0.5h and dried at 150°C for 8h under the protection of nitrogen, and then melted and extruded into the spinning box through a screw extruder at 270-290°C. The temperature of the spinning box was 280°C. After the liquid is extruded and cooled by the second spinning assembly 4, the temperature of the first hot roller 5 is 60° C., and the speed is 1000 m / min. Then the temperature of the second hot roller 5' is 100°C, and the speed is 2800m / min to form a fully drawn yarn (FDY), and the fully drawn yarn is input into the doubling device 6. PET chips are crystallized at 150°C for 0.5h, dried at 160°C for 8h, melted and extruded by a screw ex...

Embodiment 3

[0030] A different-shrinkage mixed fiber yarn in which biomass nylon 56 fiber is FDY fiber and PET fiber is POY fiber, and the mass ratio of biomass nylon 56 fiber to PET fiber is 9:1.

[0031] use as figure 1 The shown device prepares different shrinkage mixed filaments:

[0032] Biomass nylon 56 slices were crystallized at 130°C for 0.5h and dried at 150°C for 8h under the protection of nitrogen, and then melted and extruded into the spinning box at 270-290°C by a screw extruder. The temperature of the spinning box was 280°C. After being extruded and cooled by the second spinning assembly 4, the temperature of the first hot roller 5 is 60° C., and the speed is 1000 m / min. Then the temperature of the second hot roller 5' is 100°C, and the speed is 2800m / min to form a fully drawn yarn (FDY), and the fully drawn yarn is input into the doubling device 6. PET chips are crystallized at 150°C for 0.5h, dried at 160°C for 8h, melted and extruded by a screw extruder at 280°C to 300...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses FDY / POY different shrinkage combined filament yarn of biomass nylon 56 fiber / PET fiber.The combined filament yarn is characterized by being prepared by spinning biomass nylon 56 fiber slices and PET slices; the biomass nylon 56 fiber is FDY fiber and the PET fiber is POY fiber, or the biomass nylon 56 fiber is POY fiber, and the PET fiber is FDY fiber.The difference between the boiling water shrinkage of the biomass nylon 56 fiber and that of the PET fiber is equal to or larger than 30%.According to the obtained FDY / POY different shrinkage combined filament yarn of the biomass nylon 56 fiber / PET fiber, the surfaces of tows curl slightly and naturally, hydrophily and softening property of the tows are obviously improved, and the FDY / POY different shrinkage combined filament yarn can be used for developing imitated cotton and imitated silk fabric.

Description

technical field [0001] The invention relates to a FDY / POY different shrinkage mixed fiber yarn of biomass nylon 56 fiber / PET fiber and a preparation method thereof. Background technique [0002] Different shrinkage mixed fiber yarn is a product formed by mixing fibers with different thermal shrinkage rates. When this type of mixed fiber yarn is heat treated in the subsequent dyeing and finishing process, the filament with a large thermal shrinkage rate will shrink to form a core filament, while the filament with a small shrinkage rate will produce fine and natural curls and float on the surface of the tow. , the tow cross-section will present a fluffy structure, and its fabric will have a full-bodied appearance. However, the current different shrinkage mixed fiber yarn is mainly formed by blending the fully drawn yarn (FDY) and pre-oriented yarn (POY) of PET fiber. PET fiber has high strength, high modulus, stable size, stable chemical properties, etc. advantage. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/12D01F8/14
CPCD01F8/12D01F8/14
Inventor 王学利俞建勇刘修才李乃强秦兵兵
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com