A technology of AZ31-RE and wrought magnesium alloy, which is applied in the field of alloys, can solve problems such as low safety factor, serious environmental pollution, and magnesium residue, and achieve the effects of reducing production cost, reducing residue rate, and refining grains

Inactive Publication Date: 2016-08-03
HARBIN UNIV OF SCI & TECH
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of melting and refining, it is necessary to add covering agent, refining agent or other atmosphere for special protection, so that a large amount of materials will be oxidized and burned, and a large amount of magnesium remains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing AZ31-RE wrought magnesium alloy
  • Method for preparing AZ31-RE wrought magnesium alloy
  • Method for preparing AZ31-RE wrought magnesium alloy

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0050] Example one

[0051] The cold pressing die 100 and the extrusion die 200 are used in the process of preparing the AZ31-RE wrought magnesium alloy provided in this embodiment, see figure 1 with figure 2 . Among them, the cold pressing die 100 includes a cold pressing punch 101, a cold pressing inner sleeve 102, a cold pressing sleeve 103, and a pressure pad 104; the extrusion die 200 includes an extrusion punch 201, an extrusion inner sleeve 202, and an extrusion die. Sleeve 203 and mold 204. The diameter of the cold press punch 101 is 4 mm smaller than the diameter of the extrusion punch 201, and the inner diameter of the cold press inner sleeve 102 is 4 mm smaller than the inner diameter of the extrusion inner sleeve 202.

[0052] The method for preparing AZ31-RE wrought magnesium alloy provided in this embodiment includes the following steps:

[0053] a. Machining of AZ31 magnesium alloy and Mg-RE master alloy: Use a lathe to process AZ31 magnesium alloy into the first c...

Example Embodiment

[0062] Example two

[0063] In the method for preparing the AZ31-RE wrought magnesium alloy provided in this embodiment, the processing size of the AZ31 magnesium alloy in step a is different from that in the first embodiment, and the other steps are the same as the embodiment. In this embodiment, the processed size of the AZ31 magnesium alloy is 3mm×2.2mm×0.5mm.

Example Embodiment

[0064] Example three

[0065] In the method for preparing AZ31-RE wrought magnesium alloy provided in this embodiment, the mass ratio of the first scrap to the second scrap is different from that of the first embodiment, and the other steps are the same as the first embodiment. In this embodiment, the mass ratio of the first scrap to the second scrap is 99.5:0.5, and the mass percentage of rare earth elements in the prepared AZ31-RE wrought magnesium alloy is 0.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing an AZ31-RE wrought magnesium alloy, and relates to the technical field of alloys. The method comprises the following steps that a, a first scrap material and a second scrap material are mixed, cold pressing is conducted, and a blank is obtained, wherein the first scrap material is an AZ31 magnesium alloy scrap material, the second scrap material is an Mg-RE intermediate alloy scrap material, and the mass ratio of the first scrap material to the second scrap material is 4-299:1; b, the blank is subjected to heat extrusion, and then cold pressing is conducted, wherein heat extrusion comprises the step that the blank is subjected to heat preservation at the temperature ranging from 350 DEG C to 400 DEG C for 10-20 min; and c, the step b is repeatedly conducted at least one time, and then heat extrusion of the step b is conducted again. According to the method for preparing the AZ31-RE wrought magnesium alloy, oxidization of raw materials can be effectively reduced, the burnout rate of the raw materials is reduced, and pollution to the environment can be effectively reduced.

Description

technical field [0001] The invention relates to the field of alloy technology, in particular to a method for preparing an AZ31-RE deformed magnesium alloy. Background technique [0002] AZ31 is the most widely used wrought magnesium alloy among magnesium alloys. It has a fine and dense structure, high strength and good ductility, and is suitable for plastic deformation processing, such as extrusion, stamping, rolling, forging, drawing, etc. It has significant advantages in automotive, national defense, aviation, aerospace, electronics and other industrial fields, showing great application prospects. [0003] The content of alloying elements in AZ31 magnesium alloy is low, and the second phase Mg 17 al 12 The amount is small and cannot be strengthened by heat treatment. Usually, the performance of AZ31 magnesium alloy is improved by adding elements such as rare earth Nd, Ce, Y, La, etc., that is, AZ31-RE wrought magnesium alloy is prepared. After adding rare earth element...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/04C22C23/02C22C23/06
CPCB22F2998/10C22C1/0408C22C23/02C22C23/06B22F3/02B22F2003/208
Inventor 胡茂良王殿君许红雨王晔吉泽升
Owner HARBIN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap