A cable material and corrosion-resistant technology, which is applied in the field of waterproof and corrosion-resistant cable materials, can solve problems such as performance changes and failure to meet safety regulations, and achieve improved processing performance, good anti-corrosion effect, and improved low-smoke self-extinguishing performance Effect

Inactive Publication Date: 2016-08-17
彭兰娟
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional cables can only meet the needs of conventional indoor and outdoor environments. For equipment that needs to work in water, the performance of conventional cables will change after a long period of use in the water environment, failing to meet the requirements of safety regulations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A waterproof and corrosion-resistant cable material, comprising the following raw materials in parts by weight: 100 parts of EPDM rubber, 6 parts of zinc stearate, 60 parts of zinc borate, 10 parts of alkylated diphenylamine, 4 parts of vinyltrimethoxysilane 5 parts, copper sulfate 5 parts, glass fiber 10 parts, bis-(tert-butylperoxyisopropyl) benzene 5 parts, waterproofing agent 20 parts.

Embodiment 2

[0011] A waterproof and corrosion-resistant cable material, comprising the following raw materials in parts by weight: 70 parts of EPDM rubber, 3 parts of zinc stearate, 80 parts of zinc borate, 6 parts of alkylated diphenylamine, 2 parts of vinyltrimethoxysilane 7 parts of copper sulfate, 5 parts of glass fiber, 10 parts of bis-(tert-butylperoxyisopropyl) benzene, and 10 parts of waterproofing agent.

Embodiment 3

[0013] A waterproof and corrosion-resistant cable material, comprising the following raw materials in parts by weight: 90 parts of EPDM rubber, 5 parts of zinc stearate, 70 parts of zinc borate, 8 parts of alkylated diphenylamine, 3 parts of vinyltrimethoxysilane 6 parts of copper sulfate, 8 parts of glass fiber, 3 parts of bis-(tert-butylperoxyisopropyl) benzene, and 15 parts of waterproofing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterproof and corrosion-resistant cable material, which comprises the following raw materials in parts by weight: 70-100 parts of EPDM rubber, 3-6 parts of zinc stearate, 60-80 parts of zinc borate, and alkylated diphenylamine 6‑10 parts, 2‑4 parts of vinyltrimethoxysilane, 5‑7 parts of copper sulfate, 5‑10 parts of glass fiber, 3‑10 parts of crosslinking agent, 10‑20 parts of waterproofing agent. The composition of the invention has a reasonable composition of raw materials, good corrosion resistance and waterproof performance, can work normally for a long time in a water environment, has strong wear resistance and aging resistance, and has a long service life.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a waterproof and corrosion-resistant cable material. Background technique [0002] With the development of society, wires and cables are more and more widely used in various fields. However, traditional cables can only meet the needs of conventional indoor and outdoor environments. For equipment that needs to work in water, the performance of conventional cables will change after a long period of use in the water environment, failing to meet safety requirements. In order to expand the scope of use of cables, cables must have multiple properties at the same time, not only have good waterproof performance, but also have corrosion resistance, wear resistance and anti-aging properties, which has become the development direction of cable materials. Contents of the invention [0003] Therefore, in order to solve the above problems, the present invention provides a waterproof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08K13/04C08K7/14C08K5/098C08K3/38C08K5/5425C08K3/30H01B3/28
CPCC08K13/04C08K3/30C08K3/38C08K5/098C08K5/5425C08K7/14C08K2003/3045C08K2003/387C08L2201/02C08L2201/22C08L2203/202H01B3/28
Inventor 彭兰娟
Owner 彭兰娟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap