180results about How to "Good acid corrosion resistance" patented technology

The invention discloses a composite acupuncture filter bag used for smoke treatment of a ceramic kiln. Short fibers and base fabrics are acupunctured by adopting non-woven acupuncture technology to form a composite acupuncture plain felt, the plain felt is soaked and coated by adopting a surface chemical treatment agent, and then the plain felt is dried and cured at a high temperature and is tailored and sewn to form the filter bag, wherein the base fabrics adopt 30-count alkali-free glass fiber woven fabrics; the short fibers for acupuncture comprise polypropylene fibers, polyphenylene sulfide fibers and 80-count short glass fiber yarns; and the surface chemical treatment agent comprises polytetrafluoroethylene emulsion, polyacrylic ester emulsion, coupling agent, antistatic agent and water. The invention provides the composite acupuncture filter bag used for the smoke treatment of the ceramic kiln, which has the advantages of moisture resistance, good acid corrosion resistance, long service life, high strength of the base fabrics and lower production cost. The problems of poor moisture resistance, poor corrosion resistance, low strength, short service life and high production cost of the filter bag in the prior art are solved. The filter bag is suitable for dust removal and purification treatment for the smoke of the ceramic kiln.

The invention relates to a fracturing proppant used for oil and gas wells, which is prepared with the following materials by weight: 80 to 88 portions of low content bauxite, 1 to 4 portions of manganese ore, 2 to 3 portions of potash feldspar, 2 to 4 portions of solid soluble glass, 1 to 5 portions of calcium mountain meal, and 1 to 5 portions of French chalk. The quality of the fracturing proppant is stable; the break resistance is high; the acid corrosion resistance is high; the volume density is low; the fracturing proppant can effectively prop up fracture, and significantly improve the permeability in the fracture so that oil and gas flow smoothly, and the oil productivity is improved. In addition, the raw materials and the preparation method are simple, and low requirements are proposed about the raw materials, and the fracturing proppant is prepared simply.

This invention relates to iron-base soft magnetic particles with high non-oxidation used in magnetic rheological liquid and its preparation method, which utilizes TEOS hydrolytic condensation reaction to cover a layer of SiO2 film on the magnetic particle surface to prepare magnetic composite particles, which have good non-oxidation performance, acid corrosion resistance and rather high magnetic strength.

The present invention relates to one kind of strong acid resistant inner anticorrosive paint and its production process. The paint is produced through adding epoxy resin into mixed solvent one xylene, diacetone alcohol and cyclohexanone; adding phenolic resin, chrome green, precipitated barium sulfate, graphite, PTFE, polyacrylate copolymer solution, polymethyl alkyl siloxane solution and polyamdie wax via mixing; and grinding. The paint may be coated to inner wall of acid gas pipeline and high sulfur matter conveying pipeline for preventing corrosion.

The invention relates to sulfuric acid dew point corrosion resistant steel, belonging to the technical field of metal materials. The steel comprises the following components by mass: 0.05-0.1% of C, 0.1-0.35% of Si, 0.3-0.8% of Mn, 0-0.02% of P, 0-0.01% of S, 0.5-1.0% of Cr, 0.2-0.5% of Cu, 0.04-0.1% of Sb, 0.01-0.06% of Ti, 0.0004-0.001% of Ca and the balance Fe. The steel obviously improves the acid corrosion resistance under the premise of ensuring mechanical property of the steel, not only resists sulfuric acid dew point corrosion but also resists atmospheric corrosion and has obvious substantial characteristics and prominent progress compared with the prior art.

The invention relates to an acid corrosion resistant chloroprene rubber which is completely made of crude chloroprene rubber so as to greatly enhance the acid corrosion resistance of the sizing material. Barium sulfate and kaolin are added to enhance the acid corrosion resistance of the sizing material. Plasticizer SUNDEX790 is added to replace the traditional ester plasticizer to improve the acid resistance of the sizing material because the plasticizer SUNDEX790 has good compatibility with the chloroprene rubber and can not be easily extracted by acid corrosion. In addition, because the plasticizer SUNDEX790 has a flash point higher than 230 DEG C and superior high-temperature aging performance, so that the thermal aging performance of the chloroprene rubber is enhanced. The rubber stopper produced from the chloroprene rubber can meet the requirements for production and using, and the durability of the rubber stopper is three times better than that of the product made according to the traditional formula, thus prolonging the service life of the product so as to lower the production cost. The chloroprene rubber can also be used for producing rubber tubes, rubber strips, rubber plates, rubber linings and other relevant acid resistant rubber products.

The invention discloses a preparation method of an anisotropic conductive macromolecule composite thin film. The preparation method includes following steps: 1), uniformly adding carbon nanotubes coated with nano ferroferric oxide magnetic particles into a polyaniline-N-methylpyrrolidinone solution according to a mass percentage of 0.5-15%, and stirring well to obtain a carbon nanotube/ferroferric oxide-polyaniline solution; 2), adding the nanotube/ferroferric oxide-polyaniline solution into a polyurethane solution, and stirring well to obtain a carbon nanotube/ferroferric oxide-polyaniline-polyurethane solution; 3), dropping the carbon nanotube/ferroferric oxide-polyaniline-polyurethane solution onto a glass sheet for casting to form a thin film, putting the obtained thin film in a magnetic field for magnetic orientation, and drying at high temperature to obtain the anisotropic conductive macromolecule composite thin film. The preparation method is simple and easy to implement, high in result repeatability and easy to control.

The invention discloses an acidic corrosion-resistant X65 seamless steel pipeline and a manufacturing method thereof. The acidic corrosion-resistant X65 seamless steel pipeline comprises, by weight, 0.08-0.16% of C, 0.15-0.35% of Si, 1.0-1.6% of Mn, 0.02-0.05% of Al, 0.03-0.049% of V, 0.01-0.04% of Ti, 0.20-0.30% of Cu, 0.20-0.30% of Ni, less than or equal to 0.015% of P and less than or equal to 0.005% of S. When C content is less than or equal to 0.12%, CE<Pcm> is less than or equal to 0.25 and when C content is greater than 0.12%, CE<IIW> is less than or equal to 0.42. According to the manufacturing method of the acidic corrosion-resistant X65 seamless steel pipeline, a continuous rolling method is used, a pipe blank is heated to a temperature of 1200-1300 DEG C through an annular furnace, a tube knockout temperature is in a range of 1190-1240 DEG C and a sizing temperature is in a range of 820-850 DEG C, in quenching and tempering treatment, a quenching heating temperature is in a range of 890-910 DEG C, a quenching medium is water, thermal insulation time is greater than or equal to 30min, a tempering temperature is in a range of 580-620 DEG C, thermal insulation time is greater than or equal to 50min, and heating straightening and flaw detection examination are carried out at a temperature greater than or equal to 400 DEG C.

Provided are acid-corrosion-resistant high-strength low-nickel duplex stainless steel and a manufacturing method thereof. The duplex stainless steel comprises the chemical components by the weight percentage: 0.01-0.06% of C, 0.20-0.50% of Si, 3.0-3.8% of Mn, 21.0-22.0% of Cr, 1.0-1.5% of Ni, 0.15-0.20% of N, 0.40-0.60% of Mo, 2.0-3.0% of Cu, less than or equal to 0.05% of Co, less than or equal to 0.01% of Sn, less than or equal to 0.01% of Pb, less than or equal to 0.5% of the total amount of W, B, Nb, Ti, Co, Al and V, and the balance Fe and inevitable impurities, wherein the ratio of Cu% to Mo% is 5 to 1. The duplex stainless steel has pitting corrosion resistance equivalent to that of S32101 and has acid corrosion resistance superior to that of the S32101, the corrosion resistance in boric acid and other acidic conditions is further improved, the risk of corrosion occurrence is reduced, and the yield strength is increased by 20% or more than that of the conventional S32101; the alloy cost is equivalent to that of the S32101; and ordinary raw materials can be used for smelting products satisfying nuclear power material standards.

The invention relates to a preparation method and application of aluminum-containing alloy powder. The preparation method utilizes the characteristic that an initial alloy solidification structure contains a matrix phase and a dispersed particle phase, and removes the matrix phase through reaction of an acid solution, so that the dispersed particle phase is separated out, and the aluminum-containing alloy powder is obtained. The preparation method is simple in process, can be used for preparing nano-scale, sub-micron-scale, micron-scale and millimeter-scale aluminum-containing alloy powder with different morphologies, and can be applied to the fields of photoelectronic devices, wave-absorbing materials, catalysts, 3D metal printing, metal injection molding, anticorrosive coatings and the like.

The invention discloses waterproof concrete and a preparation method thereof, wherein the waterproof concrete is prepared from the following components in parts by weight: 300 to 350 parts of cement,600 to 700 parts of fine aggregate, 900 to 1000 parts of coarse aggregate, 100 to 120 parts of an admixture, 8 to 10 parts of an additive, 25 to 30 parts of a waterproof agent and 130 to 150 parts ofwater, wherein the preparation method of the waterproof agent comprises: taking 40-60 parts by weight of modified basalt fiber and 5-7 parts by weight of disproportionated potassium rosinate, uniformly stirring, adding 30-40 parts by weight of a UEA expanding agent, 3-5 parts by weight of sodium dodecyl sulfate and 3-5 parts by weight of ferrous sulfate, and uniformly stirring to obtain the waterproof agent. The waterproof concrete provided by the invention has excellent water resistance, excellent permeability resistance and excellent acid corrosion resistance.

The invention discloses a preparation method of a high-strength waterproof color ardealite brick, which comprises the steps of selecting materials by a conventional method and mixing to obtain a mixed raw material of an ardealite brick; adding pigment and stirring; adding water and stirring; making the mixed slurry into a brick blank by a hydraulic vibration forming machine; curing with saturated steam to obtain a finished product. The color ardealite brick prepared by the method disclosed by the invention has the advantages of uniform tone, low cost, high strength, good water resistance and corrosion resistance and good durability and is suitable for wall construction and pavement construction. In the method disclosed by the invention, by improving the raw materials and method, the problems that the utilization rate of the ardealite brick is low in the prior art, the cost of the color brick is high and the color brick is not strong enough and not durable and the raw materials of the ardealite brick are not easily mixed with the pigment and consequently the tone is not uniform and the strength is not high are solved; meanwhile, the problems of unsatisfactory water resistance and durability of the ardealite brick are solved unexpectedly, a new path of ardealite utilization is created, and the problems of high cost and quality defect of color bricks are solved.

The invention discloses acid-proof ink for protecting an integrated touch screen and a preparation method of the acid-proof ink. The acid-proof ink comprises components A to F. The component A contains polystyrene-polyurethane-unsaturated polyester resin; the polystyrene-polyurethane-unsaturated polyester resin is synthesized by virtue of a molecular design, and a controllable design of the structure and properties of a material is realized. A three-dimensional network structure is formed by virtue of chemical reaction between the film-forming components A and B, so that the acid resistance and the high temperature resistance of the ink, and the strippability of a film can be improved, and the protection effect of the ink to a substrate can be enhanced; (2) the acid corrosion resistance of the ink is further improved. The protective ink is excellent in acid resistance, excellent in film-forming property and excellent in film adhesion, and can be stripped completely after use; besides, the ink is excellent in high temperature resistance.

A chemical anticorrosion teflon coating is prepared from the following materials in parts by weight: 32 to 36 parts of silicon oxide sol, 10 to 16 parts of zirconia sol, 20 to 30 parts of teflon, 10 to 15 parts of epoxy resin, 10 to 15 parts of phenolic resin, 5 to 8 parts of kieselguhr, 5 to 10 parts of ultrafine ceramic powder, 5 to 10 parts of glass powder, 1 to 3 parts of carbon black, 20 to 30 parts of modified amine hardener, 10 to 20 parts of xylene, 10 to 20 parts of n-butyl alcohol and 1 to 3 parts of defoamer. The coating is used for chemical equipment inner wall anticorrosion, is convenient for construction, effectively resists the corrosion of strong corrosive exhaust gases (such as gases of SO2, NOx, HF and HCL) to a steel inner wall, and also effectively resists the corrosion of strong corrosive liquids (strong corrosive materials such as H2SO4, HCL and HF); meanwhile a paint film formed by the coating has higher abrasive resistance, temperature tolerance and heat and cold shock resistance.

The invention relates to a sound absorbing material with tail gas clean-up function and a preparation method thereof. The preparation method comprises the following step: by using continuous basalt fibers as a raw material, carrying out acid etching and high-temperature activation to modify the continuous basalt fibers. The method is simple and easy to operate. The sound absorbing material prepared by the preparation method has the advantages of high impact resistance, high temperature resistance, high acid resistance, favorable sound absorbing property and the like, and has the tail gas clean-up function.

The invention discloses an X52 seamless pipeline steel pipe with sour corrosion resistance and a manufacturing method of the X52 seamless pipeline steel pipe. The X52 seamless pipeline steel pipe comprises, by weight percent, 0.08%-0.16% of C, 0.15%-0.35% of Si, 1.0%-1.6% of Mn, 0.021%-0.05% of Al, 0.03%-0.049% of V, 0.21%-0.30% of Cu, 0.21%-0.30% of Ni, smaller than or equal to 0.015% of P, smaller than or equal to 0.005% of S, and the balance iron and inevitable impurities. When C is smaller than or equal to 0.12%, the carbon equivalent CEPcm is smaller than or equal to 0.25%, and when C is larger than 0.12%, CEIIW is smaller than or equal to 0.43. A continuous rolling method is adopted in the manufacturing method of the seamless pipeline steel pipe, in other words, a pipe blank obtained after continuous casting and continuous rolling is heated to 1,200 DEG C-1,300 DEG C through an annular furnace, the temperature ranges from 1,190 DEG C to 1,240 DEG C after punching, and the sizing temperature is controlled to range 820 DEG C to 850 DEG C. The seamless steel pipe is high in economical efficiency and good in corrosion resistance and can be widely applied to the fields of oil and gas well pipeline pipes in the sour corrosion environment and the like.

The invention discloses concrete containing modified fibers and a preparation method thereof, and relates to the technical field of concrete. A technical key point of the concrete is that the concretecontaining the modified fibers comprises the following raw materials according to a weight ratio: 450-500 kg/m<3> of cement, 140-160 kg/m<3> of water, 1200-1300 kg/m<3> of sand, 15-20 kg/m<3> of a water reducing agent, 75-85 kg/m<3> of coal ash, 110-130 kg/m<3> of mineral powder, 110-130 kg/m<3> of silica fume, and 0.6-1 kg/m<3> of modacrylic fibers, wherein the modacrylic fibers comprise polyacrylonitrile fibers and an anti-corrosion coating sprayed on the surface of the polyacrylonitrile fibers. The method is capable of improving alkali corrosion resistance of the polyacrylonitrile fibers,prolonging service life of the concrete, and improving breaking strength, anti-cracking ability, and compressive strength of the concrete.

The invention discloses acid-corrosion-resistant repair mortar and a preparation method thereof. The acid-corrosion-resistant repair mortar comprises a mixture A, a mixture B and water, wherein the mixture A comprises the following components in parts by weight: 28-35 parts of cement; 8-12 parts of a mineral admixture, 4-5 parts of gypsum, 54-58 parts of fine sand, and 0.5-0.7 part of organic fiber, the mixture B is prepared from the following components in parts by weight: 0.03 to 0.05 part of a thixotropic agent, 0.03 to 0.05 part of a thickening time control agent, 0.7 to 0.9 part of hydrophobic rubber powder, 0.05 to 0.07 part of a tackifying water-retaining agent, 0.03 to 0.04 part of a compacting agent, and 0.05 to 0.07 part of a high-performance water reducing agent, the ratio of the weight part of the water to the total weight part of the mixture A and the mixture B is 0.13-0.17, and the cement is any one of aluminate cement, a mixture of aluminate cement and Portland cement and a mixture of aluminate cement and phosphate cement. According to the invention, aluminate cement is used as a main cementing material, and hydrophobic rubber powder and a compacting agent are used as auxiliary materials, so that the acid-corrosion-resistant repair mortar is prepared.

The invention discloses a high-temperature corrosion-resistant coating and a preparation method thereof, and a high-temperature corrosion-resistant material. The preparation method comprises the following steps: 1) providing the high-temperature corrosion-resistant coating so as to form a sol; 2) allowing the sol to generate a gelation reaction; 3) placing a substrate in the treated sol obtained in the step 2) so as to form a gel on the surface of the substrate; and 4) taking out the substrate with the surface formed with the gel, and subjecting the gel to drying treatment so as to form the high-temperature corrosion-resistant coating, wherein the step of drying treatment is performed in a drying box at 50 to 100 DEG C for 0.5 h to 10 h. According to embodiments of the invention, the preparation method for the high-temperature corrosion-resistant coating can form a coating with excellent wear resistance, acid corrosion resistance and high-temperature corrosion resistance on the surfaceof the substrate, has the advantages of simple and convenient preparation process, short production period, low cost and high safety, can realize large-scale production and application, and is also applicable to formation of a coating on the surface of a special-shaped part.

The invention relates to multi-functional acid-resistant concrete gel powder. The multi-functional acid-resistant concrete gel powder comprises the following components in percentage by weight: 45 to 80 percent of mineral admixture for basicity regulation and control, 12 to 35 percent of active volcanic ash substances, 5 to 10 percent of inert filler, 2 to 6 percent of reactive filler and 1 to 4 percent of active compound. The multi-functional acid-resistant concrete gel powder can remarkably improve the acid corrosion resistance of cement concrete, reduce the risks of surface burst, peeling and strength reduction of concrete under acid environment erosion conditions, and remarkably improve the permeability resistance and volume stability of concrete matrixes, is convenient to construct, and has a remarkable economic benefit. The multi-functional acid-resistant concrete gel powder can be widely applied to concrete works such as ports, wharves, plants, sewage treatment plants, tunnels, roads, bridges and civil buildings which serve in acid environments.

The invention provides a corrosion-resistant metal porous material and a preparation method and application thereof, and relates to the technical field of metal porous materials. The corrosion-resistant metal porous material comprises a metal porous material base material and a corrosion-resistant deposition layer metallurgically bonded on the surface of a porous framework of the metal porous material base material through chemical vapor deposition, wherein the corrosion-resistant deposition layer is a metal Ta layer or a metal Mo layer or an alternate composite layer of the metal Ta layer andthe metal Mo layer. The metal porous material can be bonded with Ta and Mo at a melting point far lower than that of Ta and Mo through chemical vapor deposition, and the chemical vapor deposition hashigh diffractivity, so that Ta and Mo can evenly and compactly surround the surface of the metal porous framework, and the corrosion resistance of the metal porous material is improved. The corrosion-resistant metal porous material has good corrosion resistance in sulfuric acid, hydrofluoric acid, hydrochloric acid, nitric acid and mixed acid of the sulfuric acid, the hydrofluoric acid, the hydrochloric acid and the nitric acid.