A kind of tial-based self-lubricating composite material and preparation method thereof

A composite material and lubricating phase technology, applied in the field of new TiAl-based self-lubricating composite materials and their preparation, to achieve the effect of reducing synthesis cost, small friction coefficient and good lubricating performance

Inactive Publication Date: 2018-01-12
WUHAN UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, liquid lubrication is limited by service temperature, thermal oxygen treatment and surface coating are limited by service time, so the above method is not suitable for working environments with high temperature or long service time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tial-based self-lubricating composite material and preparation method thereof
  • A kind of tial-based self-lubricating composite material and preparation method thereof
  • A kind of tial-based self-lubricating composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] In the following examples, the WS-containing 2 The hollow sphere powders are composed of lubricating phase WS 2 and glassy phase, composed of WS 2 Prepared from powder and aqueous solution of sodium silicate containing auxiliary reagents. The present invention provides a specific preparation method, but does not limit its preparation method, and the WS-containing 2 The hollow sphere powder of is also suitable for the present invention.

[0035] The present invention provides containing WS 2 The preparation method of the hollow spherical powder is: select WS 2The powder is added to the sodium silicate aqueous solution containing auxiliary reagents to form a mixed solution, and the resulting mixed solution is dried and then subjected to high-temperature melting treatment with oxygen-acetylene, and the molten droplet-shaped reactant is collected in water for condensation, and the upper layer of the collected water floats The particulate matter, after drying, is the re...

Embodiment 1

[0038] A new type of TiAl-based self-lubricating composite material, with TiAl alloy doped with trace elements as the matrix, graphene nanosheets and WS-containing 2 The hollow spheres are the reinforcing phase and the lubricating phase. Among them, graphene nanosheets are 0.5wt.% of the mass of the matrix, containing WS 2 The quality of the hollow sphere is 3.0wt.% of the mass of the matrix; the WS-containing 2 The hollow sphere powder consists of a lubricating phase WS 2 Composed of and glass phase; the thickness of the graphene nanosheet is 20nm-2μm, and the particle size is 5-200μm; the matrix is ​​composed of Ti, Al, Cr, Nb, B in a molar ratio of 48:47:2: 2:1 composition.

[0039] Such as figure 1 Shown, a kind of preparation method of novel TiAl base self-lubricating composite material, it comprises the steps:

[0040] 1) According to the molar ratio of Ti:Al:Cr:Nb:B=48:47:2:2:1, weigh and select 10.70g Ti powder, 5.90g Al powder, 0.48g Cr powder, 0.86g Nb powder an...

Embodiment 2

[0047] A new type of TiAl-based self-lubricating composite material, with TiAl alloy doped with trace elements as the matrix, graphene nanosheets and WS-containing 2 The hollow spheres are the reinforcing phase and the lubricating phase. Among them, graphene nanosheets are 1wt.% of the mass of the matrix, containing WS 2 The quality of the hollow sphere is 4.0wt.% of the mass of the matrix; the WS-containing 2 The hollow sphere powder consists of a lubricating phase WS 2 and glass phase; the thickness of the graphene nanosheets is 20nm-2μm, and the particle size is 5-200μm; the TiAl matrix is ​​composed of Ti, Al, Cr, Nb, and B in a molar ratio of 48:47:2 :2:1 composition.

[0048] A kind of preparation method of novel TiAl-based self-lubricating composite material, it comprises the steps:

[0049] 1) According to the molar ratio of Ti:Al:Cr:Nb:B=48:47:2:2:1, weigh and select 10.70g Ti powder, 5.90g Al powder, 0.48g Cr powder, 0.86g Nb powder and 0.05 g B powder is used a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel TiAl base self-lubricating composite. The novel TiAl base self-lubricating composite is characterized in that a TiAl base serves as a matrix, and graphene nanosheets and hollow spheres containing WS2 serve as an enhancing phase and a lubricating phase. The graphene nanosheets account for 0.5-1.5 wt.% of the matrix by mass, and hollow spheres containing WS2 account for 3.0-5.0 wt.% of the matrix by mass. A preparing method of the novel TiAl base self-lubricating composite comprises the following steps that elementary substance powder is weighed according to the mole ratio of elements contained in the TiAl base to serve as matrix materials, the graphene nanosheets and the hollow spheres containing WS2 are weighed according to the proportion, the materials are evenly mixed and then subjected to spark plasma sintering, and the novel TiAl base self-lubricating composite is obtained. With the graphene nanosheets and the hollow spheres containing WS2 as the enhancing phase and the lubricating phase, the TiAl base self-lubricating composite is high in compactness, good in mechanical property and high in abrasion relieving and resisting performance.

Description

technical field [0001] The invention relates to the field of solid self-lubricating composite materials, in particular to a novel TiAl-based self-lubricating composite material and a preparation method. Background technique [0002] TiAl alloy has excellent characteristics such as low density, high specific strength, corrosion resistance, high temperature oxidation resistance and high temperature mechanical properties, and is considered to be a new generation of lightweight and high temperature resistant structural materials. Parts made of TiAl alloy can work stably and efficiently at higher service temperatures. Therefore, the application of TiAl alloy in the industrial field will have a great development prospect. Lin Junpin et al. reported that TiAl alloys have been applied in Boeing 787 engines, and some countries in Japan and Europe have used TiAl alloys to make exhaust valves. At the same time, the application field of TiAI alloy is constantly expanding, not only in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C14/00C22C32/00C22C1/05C22C1/10
CPCC22C1/05C22C14/00C22C32/0089
Inventor 史晓亮邹佳亮杨慷沈桥黄玉春张奥章桥新
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com