A kind of preparation method of protective clothing blended fabric

A technology of blended fabrics and protective clothing, applied in the processing of textile materials, melt spinning, liquid/gas/steam textile processing, etc., can solve the problems of poor anti-static ability, stuffy feeling when wearing, and the fabric does not absorb sweat, etc. To improve the thermal insulation performance, improve the effect, and improve the effect of antistatic

Active Publication Date: 2018-05-25
SHENZHEN ELLASSAY FASHION CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of protective clothing blended fabric
  • A kind of preparation method of protective clothing blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A preparation method of a protective clothing blended fabric, carried out according to the following steps:

[0047] Pretreatment: add wool and wool oil to wool and flax fiber, and let it stand for 18-24 hours for pretreatment;

[0048] Cotton blending: Send the pretreated raw materials into the cotton blender to mix wool and flax fibers;

[0049] Opening and cleaning: send the mixed wool and flax fibers to the cotton opener for opening and cleaning;

[0050] Carding: Carding the wool and flax fibers that have been opened and cleaned, the fiber bundles are completely decomposed into single fibers, and the remaining impurities are removed.

[0051] Yarn blending: Add modified polyester fiber to fully mix the fiber components to make a uniform raw sliver;

[0052] Drawing: the raw sliver is further processed into the mature sliver through the drawing process to improve the quality;

[0053] Roving: process the cooked sliver into rovings with the same count and differen...

Embodiment 2

[0067] A preparation method of a protective clothing blended fabric, carried out according to the following steps:

[0068] Pretreatment: add wool and wool oil to wool and flax fiber, and let it stand for 18-24 hours for pretreatment;

[0069] Cotton blending: Send the pretreated raw materials into the cotton blender to mix wool and flax fibers;

[0070] Opening and cleaning: send the mixed wool and flax fibers to the cotton opener for opening and cleaning;

[0071] Carding: Carding the wool and flax fibers that have been opened and cleaned, the fiber bundles are completely decomposed into single fibers, and the remaining impurities are removed.

[0072] Yarn blending: Add modified polyester fiber to fully mix the fiber components to make a uniform raw sliver;

[0073] Drawing: the raw sliver is further processed into the mature sliver through the drawing process to improve the quality;

[0074] Roving: process the cooked sliver into rovings with the same count and differen...

Embodiment 3

[0088] A preparation method of a protective clothing blended fabric, carried out according to the following steps:

[0089] Pretreatment: add wool and wool oil to wool and flax fiber, and let it stand for 18-24 hours for pretreatment;

[0090] Cotton blending: Send the pretreated raw materials into the cotton blender to mix wool and flax fibers;

[0091] Opening and cleaning: send the mixed wool and flax fibers to the cotton opener for opening and cleaning;

[0092] Carding: Carding the wool and flax fibers that have been opened and cleaned, the fiber bundles are completely decomposed into single fibers, and the remaining impurities are removed.

[0093] Yarn blending: Add modified polyester fiber to fully mix the fiber components to make a uniform raw sliver;

[0094] Drawing: the raw sliver is further processed into the mature sliver through the drawing process to improve the quality;

[0095] Roving: process the cooked sliver into rovings with the same count and differen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a blended fabric for protective clothing. The fabric is blended with modified polyester fiber, wool and flax fiber. Raw vermiculite powder is added to the polyester fiber in the preparation process of the modified polyester fiber, which not only has low cost , The improvement effect is good, and the whole preparation process is environmentally friendly; adding wool can improve the thermal insulation performance of the fabric; adding flax fiber can improve the antistatic and anti-ultraviolet properties of the fabric.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a preparation method of a protective clothing blended fabric. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort of polyester fibers and increase ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D01D5/08D01F1/10D03D15/00D01G9/00D01G15/02D06B9/00D06B3/10D03D15/217D03D15/233D03D15/283D03D15/47D03D15/50D03D15/533
CPCD01D5/08D01F1/10D01G9/00D01G15/02D02G3/04D03D15/00D06B3/10D06B9/00D03D15/533
Inventor 温余仓
Owner SHENZHEN ELLASSAY FASHION CO LTD