A kind of hygroscopic heating yarn and its preparation and dyeing method

A technology of moisture absorption and heating, yarn, applied in dyeing method, yarn, liquid/gas/steam yarn/filament treatment, etc., can solve the problems of complicated procedure and poor dyeing uniformity, achieve high dyeing uniformity and reduce dyeing cost , Improve the effect of dyeing uniformity

Inactive Publication Date: 2018-04-20
DONGHUA UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Composed of modified coffee charcoal polyester staple fiber and viscose staple fiber, it has the function of moisture absorption and heat generation, and at the same time solves the problems of complicated procedures and poor dyeing uniformity when ordinary coffee charcoal polyester and cellulose fibers are dyed at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hygroscopic heating yarn and its preparation and dyeing method
  • A kind of hygroscopic heating yarn and its preparation and dyeing method
  • A kind of hygroscopic heating yarn and its preparation and dyeing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A hygroscopic and heating yarn, which is composed of 20% modified coffee charcoal polyester staple fiber and 80% viscose staple fiber by mass fraction, wherein the total amount of modified coffee charcoal polyester staple fiber and viscose staple fiber is 100wt %. The section of the modified coffee charcoal polyester staple fiber is a hollow structure.

[0049] The viscose staple fiber has a length of 38mm, a denier of 1.33dtex, a breaking strength of 2.81cN / dtex, a breaking elongation of 19.1%, and an initial modulus of 49.29cN / dtex.

[0050] The preparation method of the described hygroscopic and heating yarn is:

[0051] 1. Preparation of modified coffee charcoal polyester staple fiber:

[0052] (1) Preparation of coffee charcoal

[0053] Use discarded coffee grounds, mix it with 50% mass concentration of phosphoric acid in a mass ratio of 2:1, soak at 100°C for 2 hours, take the impregnated coffee charcoal, and first dry it at 150°C for 3 hours. Then raise the t...

Embodiment 2

[0091] A multi-hygroscopic and heat-generating yarn, which is composed of 30% modified coffee charcoal polyester staple fiber and 70% viscose staple fiber in mass fraction, wherein the total amount of modified coffee charcoal polyester staple fiber and viscose staple fiber is 100% by weight. The section of the modified coffee charcoal polyester staple fiber is a hollow structure.

[0092] The viscose staple fiber has a length of 38mm, a denier of 1.33dtex, a breaking strength of 2.81cN / dtex, a breaking elongation of 19.1%, and an initial modulus of 49.29cN / dtex.

[0093] The preparation method of the described hygroscopic and heating yarn is:

[0094] 1. Preparation of modified coffee charcoal polyester staple fiber:

[0095] (1) Preparation of coffee charcoal

[0096] Use discarded coffee grounds, mix it with 50% mass concentration of phosphoric acid in a mass ratio of 2:1, soak at 100°C for 2 hours, take the impregnated coffee charcoal, and first dry it at 180°C for 1 hou...

Embodiment 3

[0133] A hygroscopic and heating yarn, composed of 40% modified coffee charcoal polyester staple fiber and 60% viscose staple fiber by mass fraction, wherein the total amount of modified coffee charcoal polyester staple fiber and viscose staple fiber is 100wt %. The section of the modified coffee charcoal polyester staple fiber is a hollow structure.

[0134] The viscose staple fiber has a length of 38mm, a denier of 1.33dtex, a breaking strength of 2.81cN / dtex, a breaking elongation of 19.1%, and an initial modulus of 49.29cN / dtex.

[0135] The preparation method of the described hygroscopic and heating yarn is:

[0136] 1. Preparation of modified coffee charcoal polyester staple fiber:

[0137] (1) Preparation of coffee charcoal

[0138] Use discarded coffee grounds, mix it with 50% mass concentration of phosphoric acid at a mass ratio of 2:1, soak at 100°C for 2 hours, take the impregnated coffee charcoal, and first dry it at 170°C for 2 hours, Then raise the temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides moisture-absorbing and heating yarn and a preparation and dyeing method thereof. The moisture-absorbing and heating yarn is characterized by consisting of modified coffee-carbon polyester staple fiber with the mass fraction of 20-40% and viscose staple fiber with the mass fraction of 60-80%, wherein the total amount of the modified coffee-carbon polyester staple fiber and the viscose short fiber is 100wt%. The moisture-absorbing and heating yarn and the preparation and dyeing method thereof provided by the invention have the advantages that because of the introduction of hydrophilic groups, the fiber moisture absorption rate can be increased; simultaneously, when dyeing with viscose, one-bath piece dyeing with active dye can be realized, so that the dyeing procedure is greatly reduced, the dyeing cost is reduced and the dyeing uniformity is improved. The moisture-absorbing and heating yarn can be widely applied to the field of clothing and is especially used for preparing textiles such as household underwear.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a moisture-absorbing and heating yarn and a preparation and dyeing method thereof. Background technique [0002] With the improvement of people's living standards, the functions of clothing are also developing towards diversification, not only being limited to simple covering and keeping warm. At the same time, people have higher and higher requirements for the comfort and environmental protection of clothing. This requires more processing space for clothing raw materials and can adapt to different needs. In order to wear comfortably and beautifully in winter, fabrics that absorb moisture and generate heat have emerged as the times require. And the key point of moisture absorption heating fabric is the preparation of moisture absorption heating yarn. The principle of moisture absorption and heat generation is: (1) The highly hydrophilic polar groups on the fiber molecules in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D06B3/04D06P1/38D06P3/85D01F6/92D01F1/10
CPCD01F1/10D01F6/92D02G3/045D06B3/04D06P1/38D06P3/008D06P3/8228D10B2201/24D10B2331/04D10B2401/022D10B2401/14
Inventor 王朝生朱艺超王华平吉鹏郑耀伟邢周明朴宏徐慧玲李益仁梁天元
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com