Wood wax oil timber modifier and preparation method thereof

A technology of improver and wood wax oil, which is applied in the direction of wood impregnation, impregnated wood, wood processing utensils, etc., can solve problems such as moisture resistance, fast growth speed, and physical hazards, and achieve color retention, simple production process, and not easy to deform. Effect

Inactive Publication Date: 2016-08-24
董学明
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Artificial fast-growing and high-yield forest timber mainly includes fir, masson pine, larch, poplar, paulownia and other tree species. Low hardness, no corrosion resistance, no moisture resistance, easy deformation and cracking and other defects limit its application range. Generally, it can only be used in the production of low value-added semi-finished products such as plywood, particleboard and fiberboard, but not in solid wood floors and solid wood furniture. Value-added wood products
Some wood-improving products on the market contain toxic ingredients such as triphenyl and formaldehyde, which can cause great harm to the body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] In the embodiment of the present invention, the composition of wood wax oil wood improver according to mass percentage includes: tung oil 28%, camphor oil 12%, rosin modified resin 17%, orange oil 10%, glass powder 6%, ethanol 27% .

[0017] The preparation method of described wood wax oil wood improver, concrete steps comprise:

[0018] (1) raw materials are weighed according to mass percentage respectively;

[0019] (2) Put tung oil, camphor oil, rosin modified resin, orange oil, and glass powder into the reaction kettle and polymerize at a high temperature of 270°C for 1 hour;

[0020] (3) After cooling down to 70°C, add ethanol and stir evenly to dilute it, and cool to room temperature to obtain the finished product.

Embodiment 2

[0022] In the embodiment of the present invention, the composition of wood wax oil wood improver according to mass percentage includes: 30% of tung oil, 10% of camphor oil, 20% of rosin modified resin, 10% of orange oil, 5% of glass powder, and 25% of ethanol .

[0023] The preparation method of described wood wax oil wood improver, concrete steps comprise:

[0024] (1) raw materials are weighed according to mass percentage respectively;

[0025] (2) Put tung oil, camphor oil, rosin modified resin, orange oil, and glass powder into the reaction kettle and polymerize at a high temperature of 280°C for 1.5 hours;

[0026] (3) After cooling down to 80°C, add ethanol and stir evenly to dilute it, and cool to room temperature to obtain the finished product.

Embodiment 3

[0028] In the embodiment of the present invention, the composition of wood wax oil wood improver according to mass percentage includes: tung oil 32%, camphor oil 8%, rosin modified resin 22%, orange oil 10%, glass powder 4%, ethanol 24% .

[0029] The preparation method of described wood wax oil wood improver, concrete steps comprise:

[0030] (1) raw materials are weighed according to mass percentage respectively;

[0031] (2) Put tung oil, camphor oil, rosin modified resin, orange oil, and glass powder into the reaction kettle, and polymerize at a high temperature of 290° C., and the reaction time is 2 hours;

[0032] (3) After cooling down to 90°C, add ethanol and stir evenly to dilute it, and cool to room temperature to obtain the finished product.

[0033] After the present invention enters the amorphous region of wood, it is adsorbed on the hydroxyl group of the amorphous region of wood through hydrogen bonding to make the wood swell. In the process of hot pressing, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood wax oil timber modifier and a preparation method thereof. The modifier comprises the following components by mass percentage: 28-32% of tung oil, 8-12% of camphor wood oil, 17-22% of rosin-modified resin, 9-11% of orange oil, 4-6% of glass powder, and 22-27% of ethanol. The preparation method comprises the following steps: the tung oil, the camphor wood oil, rosin-modified resin, orange oil, and glass powder are placed in a reaction vessel, are subjected to a polymerization at the high temperature of 260-300 DEG C, then cooled to the temperature of 70-90 DEG C, ethyl alcohol is added for being stirred, and then the materials are cooled to the room temperature to obtain the product. The preparation method has simple process, the modifier does not contain toxic components such as triphenyl, formaldehyde and heavy metals, has no pungent smell, can keep original color when used on the timber, has the advantages of anticorrosion, insect resistance, non moisture absorption, non moistening, non deformation, and no influence on glues and paints.

Description

technical field [0001] The invention relates to the technical field of wood functional improvement, in particular to a wood wax oil wood improver and a preparation method thereof. Background technique [0002] With the depletion of natural forest resources and the implementation of the national natural forest protection project, artificial fast-growing and high-yield forest timber will become the main way to alleviate the contradiction between my country's timber supply and demand in the future. Artificial fast-growing and high-yield forest timber mainly includes fir, masson pine, larch, poplar, paulownia and other tree species. Low hardness, no corrosion resistance, no moisture resistance, easy deformation and cracking and other defects limit its application range. Generally, it can only be used in the production of low value-added semi-finished products such as plywood, particleboard and fiberboard, but not in solid wood floors and solid wood furniture. Added value millwo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52
Inventor 董学明
Owner 董学明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com