Plastic bag prepared from modified waste tire rubber powder

A technology for waste tire rubber and waste tires, which is applied in the field of plastic bags prepared from modified waste tire rubber powder, can solve problems such as waste of resources, and achieve the effects of improving tensile strength, improving surface properties, and improving compatibility.

Inactive Publication Date: 2016-08-24
BENGBU WEIGUANG PLASTIC PRODS
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In 2010, China produced about 250 million waste tires, and the recycling rate was only about 15%, less than 50% of that in western developed countries, resulting in a huge waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A plastic bag prepared from modified waste tire rubber powder, which is made of the following components in parts by weight: linear low density polyethylene 84, ABS resin 18, modified waste tire rubber powder 7, α-methylstyrene ring two Polymer 1, polyacrylamide 0.4, starch 6, rosin 3, acrylamide 2, C9 petroleum resin 1, bisphenol monoacrylate 0.8, polyvinyl alcohol 0.5;

[0021] The waste tire rubber powder is made of the following components in parts by weight: waste tire 20, bentonite 0.5, urea-formaldehyde resin 1, polylactic acid 0.8, calcium stearate 0.5, glycerin 3; the preparation of the modified waste tire rubber powder The method is:

[0022] 1) The bentonite is calcined at 486°C for 15 minutes, and the waste tires are crushed. After the crushed waste tires are mixed with bentonite and calcium hardate, they are put into a ball mill and ground for 30 minutes. The temperature is kept at 55- 57°C, mixture 1 was obtained;

[0023] 2) After mixing the urea-formal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a plastic bag prepared from modified waste tire rubber powder. The plastic bag is prepared from linear low density polyethylene, the modified waste tire rubber powder, alpha-methylstyrene cyclic dimer, polyacrylamide, starch, rosin, acrylamide, C9 petroleum resin, biphenol acrylate and polyvinyl alcohol. According to the plastic bag prepared from the modified waste tire rubber powder, the waste tire resources can be well utilized, the natural environment is protected, the resource utilization rate is increased, and the plastic bag has the advantages of being low in energy consumption, small in pollution and low in protection cost. The longitudinal tensile strength of the plastic bag can reach 17.1 MPa, and the transverse tensile strength of the plastic bag can reach 16.2 MPa. The plastic bag is bright in gloss, good in transparency, high in bearing capability and capable of meeting the requirements of consumers for containing more articles and using repeatedly.

Description

technical field [0001] The invention relates to the field of plastic production, in particular to a plastic bag prepared from modified waste tire rubber powder. Background technique [0002] With the gradual improvement of people's living standards and the rapid development of the logistics industry, the number of private cars and trucks in my country has increased year by year. The increase in the number of vehicles has driven the development of the economy, and the consumption and wear of automobile tires has also produced a lot of garbage - waste tires. A few years ago, waste tires were thrown away as garbage, which greatly polluted the environment we depend on for survival. The waste tires produced in China are increasing at a rate of 8% to 10% every year. In 2010, China produced about 250 million waste tires, and the recycling rate was only about 15%, less than 50% of that in Western developed countries, resulting in a huge waste of resources. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L55/02C08L21/00C08L61/24C08L67/04C08L3/02C08L29/04C08L33/26C08L93/04C08K5/00C08K5/01C08K5/20C08K5/098C08K5/134
CPCC08L23/0815C08L2201/08C08L2201/10C08L2203/16C08L2205/035C08L55/02C08L21/00C08L61/24C08L67/04C08L3/02C08L29/04C08L33/26C08L93/04C08K5/00C08K5/01C08K5/20C08K5/098C08K5/134
Inventor 李维光杨永志
Owner BENGBU WEIGUANG PLASTIC PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com