Preparing method for aluminum oxide two-dimensional photonic crystal

A two-dimensional photonic crystal, alumina technology, applied in electrolytic coatings, surface reaction electrolytic coatings, coatings, etc., can solve the problems of good crystallinity, high degree of order, and many fractures, achieving high controllability, The effect of good crystallinity and high degree of order

Inactive Publication Date: 2016-08-24
NANYANG NORMAL UNIV
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the preparation of photonic crystals mostly adopts the method of self-assembly template combined with sol-gel. The above-mentioned method has the following disadvantages: 1. Poor controllability in the process of self-assembly template
2. Many fractures during high temperature sintering
However, the preparation of photonic crystals by the template method still cannot fully meet the requirements of high controllability, less fracture, high degree of order, and good crystallinity of photonic crystal samples.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method for aluminum oxide two-dimensional photonic crystal
  • Preparing method for aluminum oxide two-dimensional photonic crystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to clearly understand the technical solution of the present invention, its detailed structure will be presented in the following description. Obviously, the implementation of the embodiments of the invention is not limited to specific details familiar to those skilled in the art. The preferred embodiments of the present invention are described in detail below, and there may be other implementations besides those described in detail.

[0022] The present invention will be described in further detail below in conjunction with the accompanying drawings and embodiments.

[0023] refer to figure 1 and figure 2 , as shown in the figure, discloses a preparation method of aluminum oxide two-dimensional photonic crystals, the first is the pretreatment and polishing of the aluminum sheet: the aluminum sheet is cut into small pieces of 1╳2 cm, in a tube furnace at a high temperature of 500 Annealed for 4 h under the protection of nitrogen to relieve the stress generat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing method for an aluminum oxide two-dimensional photonic crystal. The preparing method includes the following steps that an aluminum sheet is pretreated and subjected to anode electrochemical polishing; first-time anodizing is conducted; a first-time oxide film is removed; and second-time anodizing and chambering treatment are conducted. The requirements for high controllability, small fractures, a high degree of order and good crystallinity of a photonic crystal sample in the preparing process of the two-dimensional photonic crystal are met.

Description

technical field [0001] The invention belongs to the technical field of photonic crystals, and in particular relates to a method for preparing aluminum oxide two-dimensional photonic crystals. Background technique [0002] In recent years, photonic crystals have shown great application prospects in zero-threshold lasers, quantum computers, optical waveguides, and optical switches. According to the geometric characteristics of photonic crystals for light modulation, they can be divided into: one-dimensional photonic crystals, two-dimensional photonic crystals, and three-dimensional photonic crystals. Since the refractive index satisfies the periodic arrangement in two dimensions, and the other dimension is evenly distributed, two-dimensional photonic crystals have more arrangements, so two-dimensional photonic crystals are widely used in optical waveguides, photonic crystal fibers, and fluorescence enhancement. As a dielectric material, alumina has low plasma absorption and h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/12C25D11/16C25F3/20
CPCC25D11/12C25D11/16C25F3/20
Inventor 朱永胜王银花刘旭焱徐秀梅卢志文
Owner NANYANG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap