A kind of preparation method of composite chiffon fabric

A fabric and chiffon technology, which is applied in the preparation of composite chiffon fabrics, can solve the problems of chiffon fabrics such as moisture absorption and breathability, skin-friendly performance, and shielding effects that need to be strengthened, so as to achieve good dyeing effect, good shielding effect, and good moisture absorption breathable effect

Active Publication Date: 2018-03-09
浙江雅芬婷内衣有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as summer personal clothing, the moisture absorption and breathability, skin-friendly performance and shielding effect of chiffon fabrics still need to be strengthened.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of composite chiffon fabric, carried out according to the following steps:

[0031] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0032] B. Put the expanded vermiculite powder into water, add plant dyeing agent and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0033] C, drying the filter cake at 45°C for 12h, and then drying at 110°C for 3h to obtain nanoscale expanded vermiculite powder;

[0034] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turntable, and spin the polyester chips on a spinning m...

Embodiment 2

[0047] A preparation method of composite chiffon fabric, carried out according to the following steps:

[0048] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0049] B. Put the expanded vermiculite powder into water, add plant dyeing agent and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0050] C, drying the filter cake at 40°C for 10 hours, and then drying at 120°C for 2 hours to obtain nanoscale expanded vermiculite powder;

[0051] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turntable, and spin the polyester chips on a ...

Embodiment 3

[0064] A preparation method of composite chiffon fabric, carried out according to the following steps:

[0065] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0066] B. Put the expanded vermiculite powder into water, add plant dyes and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugal separation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0067] C, drying the filter cake at 50°C for 10h, and then drying at 100°C for 5h to obtain nanoscale expanded vermiculite powder;

[0068] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turntable, and spin the polyester chips on a spinning mac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing method of a compound chiffon fabric. Very good moisture absorbing, sweat releasing, skin-friendly and masking effects can be achieved by blending modified polyester fiber and blended Coolplus fiber. The fabric has a semitransparent and flickering effect and meets the romantic aesthetic taste of modern women.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a method for preparing a composite chiffon fabric. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort of polyester fibers and increase the added v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D01F6/92D01F1/10D01F1/06
CPCD01F1/06D01F1/10D01F6/92D02G3/04D10B2331/04D10B2501/00
Inventor 包新姐
Owner 浙江雅芬婷内衣有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com