Halogen-free flame-retardant nylon composite material

A nylon composite material and flame retardant technology, applied in the field of halogen-free flame retardant nylon composite materials, can solve the problems of secondary harm, endangering the human body, and a large amount of acid smoke, and achieve the effect of excellent impact resistance

Inactive Publication Date: 2016-09-07
TONGCHENG ZHONGHUI PLASTIC IND CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]In order to improve the flame retardancy of nylon materials, halogen flame retardants are usually added to the formula. Although this halogen flame retardant can play

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A halogen-free flame-retardant nylon composite material, weighed according to the raw materials in parts by weight: 10 parts of caprolactam, 90 parts of PA66 resin, 15 parts of PA6 resin, 5 parts of silicon carbide; 6 parts of melamine polyphosphate, acrylonitrile-butylene 10 parts of diene-styrene copolymer, 5 parts of dioctyl maleate, 5 parts of di-n-hexyl azelate, 1 part of modified nano-rare earth oxide, 2 parts of microencapsulated halogen-free flame retardant, accelerator 0.6 parts, 0.5 parts of activator, 0.5 parts of stabilizer, 3 parts of lead fumarate.

[0015] Prepare according to the following steps: (1) Weigh the above-mentioned raw materials according to the weight ratio, add them to a high-speed mixer and blend them for 5 minutes to obtain a mixture;

[0016] (2) the mixture obtained by step (1) is extruded through an extruder, cooled, pelletized and screened to obtain a nylon composite material; in the step (2), the process parameters of the twin-screw e...

Embodiment 2

[0018] A halogen-free flame-retardant nylon composite material, weighed according to the raw materials in parts by weight: 8 parts of caprolactam, 85 parts of PA66 resin, 10 parts of PA6 resin, 6 parts of silicon carbide; 7 parts of melamine polyphosphate, acrylonitrile-butylene 12 parts of diene-styrene copolymer, 8 parts of dioctyl maleate, 6 parts of di-n-hexyl azelate, 1 part of modified nano-rare earth oxide, 1 part of microencapsulated halogen-free flame retardant, accelerator 0.1 parts, 0.3 parts of activator, 0.3 parts of stabilizer, 2-3 parts of lead fumarate.

[0019] Prepare according to the following steps: (1) Weigh the above-mentioned raw materials according to the weight ratio, add them to a high-speed mixer and blend them for 5 minutes to obtain a mixture;

[0020] (2) the mixture obtained by step (1) is extruded through an extruder, cooled, pelletized and screened to obtain a nylon composite material; in the step (2), the process parameters of the twin-screw e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a halogen-free flame-retardant nylon composite material, and belongs to the technical field of high polymer materials. The halogen-free flame-retardant nylon composite material is prepared from, by weight, 5-10 parts of caprolactam, 70-90 parts of PA66 resin, 5-15 parts of PA6 resin, 5-8 parts of silicon carbide, 6-11 parts of melamine pyrophosphate, 10-15 parts of acrylonitrile-butadiene-styrene copolymers, 5-10 parts of dioctyl maleate, 5-10 parts of di-n-hexyl azelate, 0.2-3 parts of modified nanometer rare earth oxides, 1-5 parts of microencapsulated halogen-free flame retardant, 0.1-0.6 part of accelerator, 0.1-0.5 part of activator, 0.1-0.5 part of stabilizer and 2-3 parts of lead fumarate. The halogen-free flame-retardant nylon composite material has the following performance indexes that the tensile strength is larger than 140 MPa, the bending strength is larger than 220 MPa, the impact strength of a cantilever beam notch is larger than 24 kj/m<2>, the melt flow index is larger than 16 g/10 min, and the flame retardance reaches V-0(UL-94-1.6 mm). The high-temperature-resistant halogen-free flame-retardant nylon composite material not only has the barrier property, the dimensional stability, chemical resistance and high temperature resistance of high-temperature-resistant nylon, but also has the excellent impact resistance, flowability and flame retardant property.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a halogen-free flame-retardant nylon composite material. Background technique [0002] In order to improve the flame retardancy of nylon materials, halogen-based flame retardants are usually added to the formula. Although this halogen-based flame retardant can play a good flame-retardant effect, it will produce a large amount of acid smoke when the material is burned, causing Secondary hazards and endanger the human body. Therefore, halogen-containing nylon is gradually being ignored by people because it is not environmentally friendly. In view of this, it undoubtedly has positive practical significance for the development of halogen-free flame-retardant nylon materials, and the technical solutions to be introduced below are produced on this premise. Contents of the invention [0003] The object of the present invention is to provide a halogen-free flame...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L77/02C08L55/02C08K13/06C08K9/10C08K3/34C08K5/3492C08K9/00C08K3/22C08K3/02C08K3/32
CPCC08L77/06C08K2201/003C08K2201/011C08L2201/02C08L2201/08C08L2201/22C08L2205/02C08L2205/03C08L77/02C08L55/02C08K13/06C08K9/10C08K3/34C08K5/34922C08K9/00C08K2003/221C08K2003/026C08K2003/323
Inventor 潘卫兵
Owner TONGCHENG ZHONGHUI PLASTIC IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap