Organic anti-static sheet material composition and preparation method thereof

An antistatic and composition technology, which is applied in the field of organic antistatic sheet composition and its preparation, can solve the problems of few reports on pure organic sheets, poor antistatic effect, and high production cost, and achieve excellent antistatic performance, The effect of convenient preparation and low price

Inactive Publication Date: 2016-09-28
JIN BAOLI TECH SUZHOU
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One way to eliminate static electricity is to use antistatic fillers for modification, but the currently commonly used antistatic sheets have the problems of high production cost and poor antistatic effect; and there are few reports on pure organic sheets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The raw materials are weighed and placed in a container, ball milled and mixed uniformly; then put into a sheet extruder and extruded at 210-225°C to obtain an organic antistatic sheet; the raw material of the organic antistatic sheet composition Consists of components in parts by weight:

[0037] Norbornene 100

[0038] Dimethyl bridge octahydronaphthalene 25

[0039] Methyl methacrylate 26

[0040] Dimethylmethoxysilane 18

[0041] 4,4-Binaphthalenediamine 18

[0042] 4-amino-2,2,6,6-tetramethylpiperidine 12

[0043] Alkyl glucamide 13

[0044] Polyethylene 29.

Embodiment 2

[0046] The raw materials are weighed and placed in a container, ball milled and mixed uniformly; then put into a sheet extruder and extruded at 210-225°C to obtain an organic antistatic sheet; the raw material of the organic antistatic sheet composition Consists of components in parts by weight:

[0047] Norbornene 100

[0048] Dimethyl bridge octahydronaphthalene 23

[0049] Methyl methacrylate 22

[0050] Dimethylmethoxysilane 18

[0051] 4,4-Binaphthalenediamine 18

[0052] 4-amino-2,2,6,6-tetramethylpiperidine 12

[0053] Alkyl glucamide 13

[0054] Polyethylene 29.

Embodiment 3

[0056] The raw materials are weighed and placed in a container, ball milled and mixed uniformly; then put into a sheet extruder and extruded at 210-225°C to obtain an organic antistatic sheet; the raw material of the organic antistatic sheet composition Consists of components in parts by weight:

[0057] Norbornene 100

[0058] Dimethyl bridge octahydronaphthalene 25

[0059] Methyl methacrylate 26

[0060] Dimethylmethoxysilane 15

[0061] 4,4-Binaphthalenediamine 18

[0062] 4-amino-2,2,6,6-tetramethylpiperidine 10

[0063] Alkyl glucamide 12

[0064] Polyethylene 29.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organic anti-static sheet material composition and a preparation method thereof. All raw materials are weighed and put in a vessel and ball-milled to be mixed to be uniform; the ball-milled materials are put into a sheet material extrusion machine, and an organic anti-static sheet material is obtained through extrusion at 210 DEG C to 225 DEG C. The organic anti-static sheet material composition is prepared from norbornene, dimethanooctahydronaphthalene, methyl methacrylate, dimethyl methoxy silicane, 4,4-dinaphthalene diamine, 4-amino-2,2,6,6-tetramethyl piperidine, N-acyl-N-methyl glucamine and polyethylene. According to the organic anti-static sheet material composition and the preparation method thereof, low molecular weight monomers or compounds are added for modification on the basis of olefin polymers, the raw materials are easy to obtain, preparation is convenient, the cost is low, and the prepared sheet material has the excellent anti-static property and can be used for products with the anti-static requirement.

Description

Technical field [0001] The invention belongs to the technical field of organic materials, and particularly relates to an organic antistatic sheet composition and a preparation method thereof. Background technique [0002] Nanoparticle / polymer composite materials combine the properties of inorganic nanoparticles, such as optical, electrical, and mechanical properties, and polymer properties, such as solubility, easy film formation, chemical activity, and environmental responsiveness. His interest is increasing day by day. However, to develop and utilize these properties of inorganic particles, it is necessary to solve the agglomeration problem of nano-inorganic particles in the polymer matrix. Any object itself is charged with static electricity, and its accumulation will affect or even harm life or industrial production, interfere with normal production operations, and even cause fire and explosion of combustibles. Therefore, it must be guided or eliminated. One way to elimina...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/36C08K5/5415C08F8/32C08F110/02C08J3/24
CPCC08F8/32C08J3/247C08J2323/36C08K5/5415C08F110/02C08L23/36
Inventor 李明华
Owner JIN BAOLI TECH SUZHOU