Preparation method of antibacterial and wear-resistant material for filling teeth

A wear-resistant material and tooth filling technology, applied in dental preparations, dentistry, dental prostheses, etc., can solve the problems of limited wear resistance and mechanical strength of polymer resin, limited service life of dental resin materials, and clinical life of less than 6 years. , to achieve the effect of enhanced wear resistance, high yield and easy operation

Inactive Publication Date: 2016-10-12
SUZHOU COSMETIC MATERIALS
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the oral microenvironment is complex and affected by many factors
The survey results of the National Dental Institute of the United States show that more than 50% of the existing resin restorations need to be replaced, and the clinical life of the resin bonding restoration is less than 6 years. The annual expenditure for replacing defective bonding restorations in the United States alone is as high as $5 billion
However, due to volume shrinkage during the polymerization of dental resins, the incidence of secondary caries in patients is high, and the wear resistance and mechanical strength of polymer resins are limited, which greatly limits the service life of dental resin materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A method for preparing an antibacterial and wear-resistant material for filling teeth, said method comprising the following steps: first weighing the following raw materials in parts by weight: 30 parts of polyvinyl chloride resin, 6 parts of polyhydroxyethyl methacrylate, keratin 6 parts, 3 parts of polydiallyl dimethyl ammonium chloride, 3 parts of dodecyl dimethyl amine oxide, 12 parts of inorganic filler, 6 parts of silver source compound, 2 parts of cobalt dioxide, 4 parts of poly-L-lactic acid -8 parts, 3 parts of stabilizer, 2 parts of antioxidant, grind all raw materials except double distilled water, stabilizer, antioxidant and silver source compound into fine powder with particle size of 800~1200 mesh, mix well , to obtain a powder mixture; then dissolve the stabilizer, antioxidant and silver source compound in double distilled water, stir and mix uniformly to obtain a solution; then add the powder mixture to the solution, and heat Stir under the condition of ...

Embodiment 2

[0016] A method for preparing an antibacterial and wear-resistant material for filling teeth, the method comprising the following steps: first weighing the following raw materials in parts by weight: 50 parts of polyvinyl chloride resin, 13 parts of polyhydroxyethyl methacrylate, keratin 15 parts, 5 parts of polydiallyl dimethyl ammonium chloride, 6 parts of lauryl dimethyl amine oxide, 15 parts of inorganic filler, 13 parts of silver source compound, 5 parts of cobalt dioxide, 8 parts of poly-L-lactic acid 6 parts, 6 parts of stabilizer, 4 parts of antioxidant, each raw material except double-distilled water, stabilizer, antioxidant and silver source compound is all ground into particle diameter and is the fine powder of 800~1200 meshes, mixes evenly, obtains Powder mixture; then dissolve the stabilizer, antioxidant and silver source compound in double distilled water, and mix evenly with magnetic stirring to obtain a solution; then add the powder mixture to the solution, at a...

Embodiment 3

[0018] A method for preparing an antibacterial and wear-resistant material for filling teeth, said method comprising the following steps: first weighing the following raw materials in parts by weight: 40 parts of polyvinyl chloride resin, 9 parts of polyhydroxyethyl methacrylate, keratin 11 parts, 4 parts of polydiallyl dimethyl ammonium chloride, 5 parts of lauryl dimethyl amine oxide, 14 parts of inorganic filler, 11 parts of silver source compound, 3 parts of cobalt dioxide, 6 parts of poly-L-lactic acid 4 parts, 4 parts of stabilizer, 3 parts of antioxidant, each raw material except double distilled water, stabilizer, antioxidant and silver source compound is all ground into particle diameter and is the fine powder of 800~1200 meshes, mixes evenly, obtains powder mixture; then dissolve the stabilizer, antioxidant and silver source compound in double distilled water, stir and mix evenly to obtain a solution; then add the powder mixture to the solution, at a temperature of 50...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an antibacterial and wear-resistant material for filling teeth. The preparation method comprises the following steps: firstly, weighing various raw materials, grinding partial raw materials into fine powder which is 800-1200 meshes in grain size, and uniformly mixing the fine powder, so that a powder mixture is obtained; then, dissolving rest raw materials in double distilled water, and conducting magnetic stirring and uniform mixing, so that a solution is obtained; and adding the powder mixture to the solution, and conducting stirring until the mixture is formed as uniform cream, so that the antibacterial and wear-resistant material is prepared. According to the scheme, the wear resistance of the prepared antibacterial and wear-resistant material is improved by 180%, and the teeth, which are repaired with the use of the material, are firmer and are more durable. The antibacterial and wear-resistant material is simple and convenient to use, free from any toxic and side effects, safe and free from health risks; and the preparation method has the characteristics of being simple in process, easy to operate, high in yield, low in environmental pollution and the like.

Description

technical field [0001] The invention relates to a preparation method of an antibacterial and wear-resistant material for filling teeth. technical background [0002] Teeth are the organs that humans use to chew food. Teeth are the hardest organ in the human body. Generally speaking, teeth are white and hard in texture. The various shapes of teeth are suitable for many purposes, including tearing, grinding food. The pronunciation of human language is closely related to the upper and lower teeth in the front row of the mouth. Teeth are the hardest organs in the human body and are divided into three parts: crown, neck and root. Divided into enamel, dentin, pulp and so on. The main ingredient is calcium hydroxyphosphate: the basic calcium phosphate, the main component of human teeth. [0003] Commonly known as caries and tooth decay, caries is a bacterial disease, which can be secondary to pulpitis and periapical periodontitis, and even cause alveolar bone and jaw inflamma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K6/087A61K6/083A61K6/02A61K6/891
CPCA61K6/80A61K6/802A61K6/887A61K6/891C08L67/04C08L27/06C08L33/14C08L39/00
Inventor 金仲恩全春兰张帆喻国贞欧阳智琨陈晋纳
Owner SUZHOU COSMETIC MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products