Blocked polyisocyanate water dispersion, fiber processing agent composition, and fabric

一种多异氰酸酯、二异氰酸酯的技术，应用在封端多异氰酸酯的水分散体、纤维处理剂组合物以及布帛领域，能够解决拒水性降低等问题，达到机械稳定性优异、水分散稳定性良好、高洗涤耐久性的效果

Inactive Publication Date: 2016-10-12
ASAHI KASEI KK
View PDF12 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, fluororesins having a perfluoroalkyl group having 6 or less carbon atoms may lower performance such as water repellency after repeated washing compared to fluororesins having a carbon number of 8 or more, and it is urgently desired to maintain the performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blocked polyisocyanate water dispersion, fiber processing agent composition, and fabric
  • Blocked polyisocyanate water dispersion, fiber processing agent composition, and fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0150] Although the present invention will be specifically described with reference to the following examples and the like, the present invention is not limited thereto.

[0151] (1) Viscosity measurement:

[0152] The viscosity was measured using the following device.

[0153] Device: RE-80R (manufactured by Toki Sangyo Co., Ltd.)

[0154] Rotor: cone plate 1°34'×R24

[0155] Measuring temperature: 25°C

[0156] (2) Determination of number average molecular weight:

[0157] The number average molecular weight is a polystyrene standard number average molecular weight measured by gel permeation chromatography using the following apparatus.

[0158] Device: HLC-802A (manufactured by Tosoh Corporation)

[0159] Column: G1000HXL×1 (manufactured by Tosoh Corporation)

[0160] G2000HXL×1 (manufactured by Tosoh Corporation)

[0161] G3000HXL×1 (manufactured by Tosoh Corporation)

[0162] Carrier gas: tetrahydrofuran

[0163] Flow rate: 0.6mL / min

[0164] Sample concentratio...

manufacture example 1

[0222] (Manufacture example 1: Manufacture of polyisocyanate)

[0223] Make a nitrogen atmosphere in a 4-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen blowing pipe, drop in 1000 parts by mass of HDI, 22 parts by mass of trimethylolpropane (molecular weight 134) as a trihydric alcohol, and The temperature in the reactor was maintained at 90° C. for 1 hour while stirring to perform urethanization. Thereafter, the temperature of the reaction solution was kept at 60° C., an isocyanuration catalyst tetramethylammonium octanoate was added, and when the conversion ratio reached 48%, phosphoric acid was added to stop the reaction. Thereafter, after filtering the reaction liquid, unreacted HDI was removed by a thin film distillation apparatus.

[0224] The obtained polyisocyanate had a viscosity at 25° C. of 25,000 mPa·s, an isocyanate group content of 19.9% ​​by mass, a number average molecular weight of 1080, and an isocyanate average functi...

manufacture example 2

[0225] (Production example 2: Production of polyisocyanate)

[0226] A nitrogen atmosphere was made in a 4-necked flask equipped with a stirrer, a thermometer, a reflux condenser, a nitrogen blowing pipe, and a dropping funnel, and 1000 parts by mass of HDI was added, and the temperature inside the reactor was kept at 70° C. under stirring. An isocyanurate catalyst tetramethylammonium octanoate was added, and when the yield reached 40%, phosphoric acid was added to stop the reaction. After filtering the reaction solution, unreacted HDI was removed using a thin film evaporator.

[0227] The viscosity of the obtained polyisocyanate at 25° C. was 2700 mPa·s, the content of isocyanate was 21.7%, the number average molecular weight was 660, and the average number of functional groups of isocyanate was 3.4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size distributionaaaaaaaaaa
particle size distributionaaaaaaaaaa
water contact angleaaaaaaaaaa
Login to View More

Abstract

The invention provides a blocked polyisocyanate water dispersion, a fiber processing agent composition, and fabric. The purpose of the present invention is to provide: a blocked polyisocyanate water dispersion having favorable water dispersion stability, capable of achieving high coating strength, exhibiting excellent mechanical stability as a fluorine-doped fiber processing agent, and capable of producing a fabric having high washability; and a fiber processing agent composition containing the same. The blocked polyisocyanate water dispersion contains water and a blocked polyisocyanate at least having component units (1-3), and has an average dispersed particle diameter of the blocked polyisocyanate of phi=1-250nm, wherein the component units (1-3) are a polyisocyanate unit having at least one type of diisocyanate monomer unit selected from a group consisting of aliphatic diisocyanate monomers and alicyclic diisocyanate monomers, 2) a polyethylene oxide unit having a hydroxyl group on one end, and 3) a blocking agent unit.

Description

[0001] This application is a divisional application of a Chinese patent application with an application date of October 23, 2012, an application number of 201280050501.X, and an invention title of "Aqueous Dispersion of Blocked Polyisocyanate, Fiber Treatment Agent Composition, and Fabric". technical field [0002] The present invention relates to an aqueous dispersion of blocked polyisocyanate, a fiber treatment composition containing the same, and a fabric treated with the fiber treatment composition. Background technique [0003] Fiber treatment agents are used to impart various functions to fibers. Examples of its functions include: water and oil repellency for preventing adhesion of water and oil; texture for making clothes comfortable to wear; and prevention of deformation of sewn products. [0004] Among these, a composition containing a fluororesin having a perfluoroalkyl group having 8 or more carbon atoms was used as a fiber treatment agent for imparting water repe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/70C08G18/79C08G18/80C08G18/02C08G18/18C08G18/28C09D175/06C09D175/08D06M15/277D06M15/568D06M15/572D06M15/576
CPCC08G18/706C08G18/022C08G18/1875C08G18/283C08G18/285C08G18/792C08G18/8025C09D175/04D06M15/277D06M15/568D06M15/572D06M15/576D06M2200/12C09D175/06C09D175/08
Inventor 三轮祐一朝比奈芳幸
Owner ASAHI KASEI KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com