A method of preparing for environmentally friendly skin -friendly polyester European yarn fabric

A technology for organza and fabrics, which is applied in the field of preparation of environmentally friendly and skin-friendly polyester organza fabrics, can solve the problems of being easily stained with dust, feeling sultry when wearing, and the fabrics do not absorb sweat, etc., and achieves improved dispersion effect and good dyeing effect. , good shading effect

Active Publication Date: 2018-11-13
徐州荣盛纺织整理有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of an environment-friendly skin-friendly polyester organza fabric is carried out according to the following steps:

[0029] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0030] B. Put the expanded vermiculite powder into water, add plant dyeing agent and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0031] C, drying the filter cake at 45°C for 12h, and then drying at 110°C for 3h to obtain nanoscale expanded vermiculite powder;

[0032] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turntable, and ...

Embodiment 2

[0044] A preparation method of an environment-friendly skin-friendly polyester organza fabric is carried out according to the following steps:

[0045] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0046] B. Put the expanded vermiculite powder into water, add plant dyeing agent and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0047] C, drying the filter cake at 40°C for 10 hours, and then drying at 120°C for 2 hours to obtain nanoscale expanded vermiculite powder;

[0048] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turnt...

Embodiment 3

[0060] A preparation method of an environment-friendly skin-friendly polyester organza fabric is carried out according to the following steps:

[0061] A, expanded vermiculite is pulverized, crosses 250 mesh sieves, obtains expanded vermiculite powder;

[0062] B. Put the expanded vermiculite powder into water, add plant dyeing agent and olive oil, conduct high-energy ball milling on the expanded vermiculite powder, accelerate the precipitation through centrifugation, separate the ultra-fine grinding sediment, send it back to the ultra-fine grinding link to participate in high-energy ball milling again ; Remove the slurry of the sediment, and obtain the filter cake by press filtration;

[0063] C, drying the filter cake at 50°C for 10h, and then drying at 100°C for 5h to obtain nanoscale expanded vermiculite powder;

[0064] D. Quantitatively add nano-scale expanded vermiculite powder and micron-scale pearl powder into molten polyester chips through a metering turntable, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a production method of an environmentally-friendly and skin-friendly polyster organza fabric. No chemical preparations are used in the whole production process, so the production method is an environmentally-friendly novel fiber production method. Polyester fibers are modified with expanded vermiculite powder, a plant dye and pearl powder, so woven organza has very good skin-friendly effect and a very good shielding effect, and the fabric has a semi-transparent effect, has a flickering effect, and accords with modern females' romantic aesthetic taste.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a preparation method of an environment-friendly skin-friendly polyester organza fabric. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort of poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/06D01F1/10D01D5/08
CPCD01D5/08D01F1/06D01F1/10D01F6/92
Inventor 包新姐
Owner 徐州荣盛纺织整理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com