Fabric with cotton handfeel, woolen appearance and linen coolness and production process of fabric

A production process, a cool technology, applied in the field of cotton wool fabrics, can solve the problems of functionality, wearability, lack of style, poor moisture drainage performance, poor wrinkle resistance and other problems

Inactive Publication Date: 2016-10-26
HAIXI NEW TEXTILE MATERIAL OF JINJIANG IND TECH ACAD +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The development of high-grade summer multifunctional casual trousers fabrics mainly takes into account the following factors: (1) Seasonal factors: the summer weather is hot, the human body sweats more, sweat absorption and discharge are slower, and bacteria are prone to rapid reproduction and growth, causing the body to appear discomfort
(2) Fiber material factors: cotton fabrics are soft and skin-friendly, have a strong sense of comfort, and have good moisture absorption performance, but poor moisture drainage performance and poor wrinkle resistance; wool fiber fabrics have strong wool feeling, good elastic recovery, and strong three-dimensional sense of plumpness
If a single fiber material is used to produce summer trousers, there are always deficiencies in functionality, wearability and style.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: a kind of cotton wool feel hemp cool fabric, comprising microporous polyester fiber, wool fiber and polyester-based conductive fiber, the specification of microporous polyester fiber is 1.67dtex*38mm, and the weight percentage is 83.5%; the specification of wool fiber It is 1.85dtex*40mm, and the weight percentage is 15%; the specification of the polyester-based conductive fiber is 2.22dtex*40mm, and the weight percentage is 1.5%; the surface of the microporous polyester fiber has a length of 6-8 microns and a depth of about 2 microns. The micropores increase the specific surface area of ​​the fiber by 30-40%.

Embodiment 2

[0024] Embodiment 2: A kind of cotton wool feel hemp cool fabric, comprising microporous polyester fiber, wool fiber and polyester-based conductive fiber, the specification of microporous polyester fiber is 1.8dtex*35mm, and the weight percentage is 80%; the specification of wool fiber It is 1.9dtex*38mm, and the weight percentage is 18%; the specification of the polyester-based conductive fiber is 2dtex*40mm, and the weight percentage is 2%; the surface of the microporous polyester fiber is formed with a length of 6-8 microns and a depth of about 2 microns. Microporous, which increases the specific surface area of ​​the fiber by 30-40%.

[0025] A kind of production technology of cotton wool feeling hemp refreshing fabric, comprises the steps:

[0026] Dyeing process: modified polyester fiber→alkaline porosity scouring→60℃ warm water washing→polyester oligomer detergent cleaning→dyeing→60℃ hot water washing→reduction cleaning→cold water washing→dehydration→drying→preparation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
depthaaaaaaaaaa
depthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fabric with cotton handfeel, woolen appearance and linen coolness and a production process of the fabric. The fabric is prepared from microporous polyester fibers, wool fibers and polyester based conductive fibers, wherein the microporous polyester fibers is (1.5-1.8)dtex*(30-45)mm in specification and 80-85% in weight percentage; the wool fibers are (1.7-1.9)dtex*(35-50)mm in specification and 13-18% in weight percentage; the polyester based conductive fibers are (2-2.3)dtex*(30-45)mm in specification and 1-2% in weight percentage. The fabric has comprehensive functions and styles of cotton handfeel, woolen appearance and linen coolness.

Description

technical field [0001] The invention relates to a cotton wool-feeling hempy fabric and a production process thereof. Background technique [0002] The development of high-grade summer multifunctional casual trousers fabrics mainly takes into account the following factors: (1) Seasonal factors: the summer weather is hot, the human body sweats more, sweat absorption and discharge are slower, and bacteria are prone to rapid reproduction and growth, causing the body to appear discomfort. (2) Fiber material factors: Cotton fabrics are soft and skin-friendly, have a strong sense of comfort, and have good moisture absorption performance, but poor moisture drainage performance and poor wrinkle resistance; wool fiber fabrics have strong wool feeling, good elastic recovery, and strong plump three-dimensional effect. However, the moisture absorption performance is poor, it is easy to fluff and pilling, and the wool fabric needs to be dry-cleaned and difficult to take care of. The hemp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/00D02G3/04D06B3/02D06L1/12D06M11/38D06M15/564D06M101/12D06M101/32
CPCA41D31/00D02G3/04D06B3/02D06L1/12D06M11/38D06M15/564D06M2101/12D06M2101/32D06M2200/20D06M2200/50D10B2211/02D10B2331/04
Inventor 王忠宝林荣宗郑小佳李志坚王佳佳
Owner HAIXI NEW TEXTILE MATERIAL OF JINJIANG IND TECH ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap