A double-sided printed gold clip flower placemat and its drawing process

A technology of printing gold and clipping flowers, applied in the field of placemats, can solve the problems of fading, short service life, easy scratching, etc., and achieve the effects of good resilience, easy cleaning, and improved dispersion.

Active Publication Date: 2018-05-22
DONGGUAN IUIU HOUSEHOLD PROD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]The printed patterns of existing plastic placemats are all printed on the surface of the plastic base layer, which is easy to scratch, fade, change color, and fade when used, and the service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A double-sided printed gold clip flower placemat and its drawing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A double-sided printed gold placemat, comprising the following raw materials in parts by weight:

[0057] PP resin 15 parts

[0058] PE resin 60 parts

[0059] Filler 10 parts

[0060] Compatibilizer 1 part

[0061] 1 part coupling agent

[0062] Lubricant 1 part

[0063] Enhancer 1 part

[0064] 1 part of other additives.

[0065] The PP resin is a homopolypropylene with a melt index of 20g / 10min under the test conditions of 230°C and 2.16KG.

[0066] The PE resin has a melt index of 0.6g / 10min and a density of 0.942g / cm 3 of linear low density polyethylene.

[0067] The filler is nano-active calcium carbonate with a particle diameter of 10 nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0068] The compatibilizer is a mixture of maleic anhydride grafted polypropylene and maleic anhydride grafted polyethylene in a weight ratio of 0.8:1.

[0069] The coupling agent is a mixture of a silane coupling agent and a titanate c...

Embodiment 2

[0085] A double-sided printed gold placemat, comprising the following raw materials in parts by weight:

[0086] PP resin 18 parts

[0087] PE resin 70 parts

[0088] Filler 15 parts

[0089] Compatibilizer 2 parts

[0090] 2 parts of coupling agent

[0091] Lubricant 1.5 parts

[0092] Enhancer 1.5 parts

[0093] 1.5 parts of other additives.

[0094] The PP resin is a homopolypropylene with a melt index of 40g / 10min under the test conditions of 230°C and 2.16KG.

[0095] The PE resin has a melt index of 0.7g / 10min and a density of 0.944g / cm 3 of linear low density polyethylene.

[0096] The filler is nano active calcium carbonate with a particle size of 30nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0097] The compatibilizer is a mixture of maleic anhydride grafted polypropylene and maleic anhydride grafted polyethylene in a weight ratio of 0.9:1.

[0098] The coupling agent is a mixture of a silane coupling agent and a t...

Embodiment 3

[0114] A double-sided printed gold placemat, comprising the following raw materials in parts by weight:

[0115] PP resin 20 parts

[0116] PE resin 80 parts

[0117] Filler 20 parts

[0118] Compatibilizer 3 parts

[0119] 3 parts of coupling agent

[0120] Lubricant 2 parts

[0121] Enhancer 2 parts

[0122] 2 parts of other additives.

[0123] The PP resin is a homopolypropylene with a melt index of 50 g / 10 min under the test conditions of 230° C. and 2.16 KG.

[0124] The PE resin has a melt index of 0.8g / 10min and a density of 0.945g / cm 3 of linear low density polyethylene.

[0125] The filler is nano active calcium carbonate with a particle size of 50nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0126] The compatibilizer is a mixture of maleic anhydride grafted polypropylene and maleic anhydride grafted polyethylene in a weight ratio of 1:1.

[0127] The coupling agent is a mixture of a silane coupling agent and a tita...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of table mat, and in particular, relates to a double-sided gold-printed pattern-interlaid table mat and a wire drawing process thereof. The double-sided gold-printed pattern-interlaid table mat comprises the following raw materials in parts by weight: 15-25 parts of PP resin, 60-100 parts of PE resin, 10-30 parts of a filling agent, 1-5 parts of a compatilizer, 1-5 parts of a coupling agent, 1-3 parts of a lubricant, 1-3 parts of an enhancer and 1-3 parts of other auxiliary agents. Patterns of the double-sided gold-printed pattern-interlaid table mat do not have colors lost and are not discolored and faded; the table mat has the advantages of being novel in patterns, clear and natural, bright in surface, unique in style, soft and comfortable in texture, free to roll and extend, easy to clean, arbitrary to bend, fold and roll, not easy to deform, non-cracked, non-toxic, safe, durable in use, good in corrosion resistance effect, and resistant to heavy pressure; the double-sided gold-printed pattern-interlaid table mat also has the advantages of good rebound resilience, aging resistance, insulation, flame retardancy, static prevention, high and low temperature resistance, wear resistance, acid and alkali resistance, dust prevention, skid resistance and the like, and has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of placemats, in particular to a double-sided gold-printed flower placemat and its wire drawing process. Background technique [0002] At present, in fast food restaurants, canteens, etc., dinner plates are used to hold food. Generally, a placemat is placed on the chassis of the dinner plate. The function of the placemat can be used for advertising and to avoid food or garbage Dirt the chassis directly for easy cleaning. [0003] The printed patterns of the existing plastic placemats are all printed on the surface of the plastic base layer, which is easy to scratch, fade, change color, and fade during use, and has a short service life. And placemat products are changing with each passing day, people are pursuing a faster and faster pace of life fashion, and have higher requirements for the style, comfort and comprehensive performance of placemats. Contents of the invention [0004] In order to overcome t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L23/12C08L51/06C08K13/06C08K9/04C08K3/26C08K5/54C08K5/10C08K9/10C08K7/10C08K7/14B29C69/00A47G23/00
CPCA47G23/00B29C69/00C08K2201/003C08K2201/011C08L23/0815C08L2201/02C08L2201/04C08L2201/08C08L2205/025C08L2205/035C08L2205/08C08L23/12C08L51/06C08K13/06C08K9/08C08K2003/265C08K5/54C08K5/10C08K9/10C08K7/10C08K7/14
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD