Preparation method of high strength antibacterial environmental protection fabric
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of fabric and environmental protection technology, applied in the direction of dyeing, textile, biochemical fiber treatment, etc., can solve the problems that cannot meet the needs of people's clothing, single function of fabric, poor comfort, etc., to achieve increased antibacterial effect, firm color, and low cost Effect
Inactive Publication Date: 2018-05-25
TIANJIN SAIYUAN HEALTH PROD
View PDF0 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] With the continuous development of textile technology, the textile industry has developed a lot of functional fiber fabrics. In addition, people's requirements for fabrics are getting higher and higher. Traditional fabrics have single functions, low grades, poor comfort, especially antibacterial, and cannot meet the requirements. people's demand for clothing
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0017] Example 1: A high-strength antibacterial and environmentally friendly fabric is blended with 45% of superfine denier polypropylene fiber, 35% of cotton fiber, 10% of chitosan fiber, 5% of silver fiber and 5% of soybean protein fiber by weight to obtain warp; Get calamine fiber 55%, bamboo fiber 35% and milk protein fiber 10% by weight and carry out blending, obtain weft thread;
[0018] A preparation method of a high-strength antibacterial environment-friendly fabric, comprising the steps of:
[0019] a. Soak the warp and weft threads in the antibacterial solution for 6-10 hours, take them out and dry them at 50-60°C for 15-20 minutes. Scutellaria baicalensis and Houttuynia cordata are crushed and decocted in water for 6 hours;
[0020] b. Woven the warp and weft into a fabric with a 1 / 2 right twill weave structure;
[0021] c. Degumming the completed fabric, dyeing with plant dyeing agent, putting the fabric into the plant dyeing agent at a liquor ratio: 1:25, at a t...
example 2
[0026] Example 2: A high-strength antibacterial and environmentally friendly fabric is blended with 45% of superfine denier polypropylene fiber, 35% of cotton fiber, 10% of chitosan fiber, 5% of silver fiber and 5% of soybean protein fiber by weight to obtain warp; Get calamine fiber 55%, bamboo fiber 35% and milk protein fiber 10% by weight and carry out blending, obtain weft thread;
[0027] A preparation method of a high-strength antibacterial environment-friendly fabric, comprising the steps of:
[0028] a. Soak the warp and weft threads in the antibacterial solution for 6-10 hours, take them out and dry them at 50-60°C for 15-20 minutes. Scutellaria baicalensis and Houttuynia cordata are crushed and decocted in water for 7 hours;
[0029] b. Woven the warp and weft into a fabric with a 1 / 2 right twill weave structure;
[0030] c. Degumming the completed fabric and dyeing with plant dyeing agent, put the fabric into the plant dyeing agent at a bath ratio of 1:30, at a te...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a preparation method of a high strength antibacterial environmental protection fabric. The fabric is prepare from that, by weight, 45% super fine denier polypropylene fiber, 35% cotton fiber, 10% chitosan fiber, 5% silver fiber and 5% soybean protein fiber are blended to obtain warp; by weight, 55% galamina fiber, 35% bamboo fiber and 10% milk protein fiber are blended to obtain weft. The high strength antibacterial environmental protection fabric not only makes a product have a good antibacterial property, protect the skin, but also has strong moisture absorption and permeability, an antibacterial finishing liquid is adopted, the antibacterial effect of the fabric is further increased, in dyeing process, all natural plant stains are adopted, after fixation, the dyeing is uniform, color cannot fade, the process is simple and the color is firm; the fabric adopts natural materials throughout the whole process, is environmental friendly and low in cost, the designof the fabric is novel and the grade of the fabric is high, and the product has good comfort degree and high added value.
Description
【Technical field】 [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of a high-strength antibacterial and environment-friendly fabric. 【Background technique】 [0002] With the continuous development of textile technology, the textile industry has developed a lot of functional fiber fabrics. In addition, people's requirements for fabrics are getting higher and higher. Traditional fabrics have single functions, low grades, poor comfort, especially antibacterial, and cannot meet the requirements. People's demand for clothing. [0003] Calamine fiber has good spinnability, uniform dyeability, and the woven fabric has strong moisture absorption and breathability, smooth hand feeling, strong anti-ultraviolet radiation and anti-Escherichia coli, Staphylococcus aureus and Candida albicans have significant antibacterial effect. [0004] Polypropylene fiber has the lightest specific gravity among fibers and can float on...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more