A technology of polyvinyl chloride and electrostatic film, applied to flat products, other household appliances, applications, etc., can solve the problems of poor self-adhesiveness and anti-static effect, achieve fast plasticization speed, good anti-static effect, and improve plasticity effect

Inactive Publication Date: 2016-10-26
DONGGUAN IUIU HOUSEHOLD PROD
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing electrostatic film has poor antistatic effect and poor self-adhesiveness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A polyvinyl chloride electrostatic film and a preparation method thereof, comprising the following raw materials in parts by weight

[0058] PVC resin 80 parts

[0059] Plasticizer 46 parts

[0060] 1 heat stabilizer

[0061] Antistatic agent 3 parts

[0062] 0.3 parts of gelling agent

[0063] Pigment powder 0.02 parts

[0064] Other additives 0.1 parts.

[0065] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin in a weight ratio of 8:1.

[0066] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 45:1.

[0067] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and zinc ricinoleate in a weight ratio of 2:0.5:2 : Mixture of 0.8 composition.

[0068] The antistatic agent is composed of stearyl dimethyl ammonium chloride, trihydroxyethylmethyl quatern...

Embodiment 2

[0084] A polyvinyl chloride electrostatic film and a preparation method thereof, comprising the following raw materials in parts by weight

[0085] PVC resin 90 parts

[0086] Plasticizer 53 parts

[0087] Heat stabilizer 1.5 parts

[0088] Antistatic agent 4 parts

[0089] 0.4 parts of gelling agent

[0090] Pigment powder 0.022 parts

[0091] Other additives 0.15 parts.

[0092] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin at a weight ratio of 9:1.

[0093] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 52:1.

[0094] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and zinc ricinoleate in a weight ratio of 2.5:0.8:2.5 : 0.9 composition mixture.

[0095] The antistatic agent is composed of stearyl dimethyl ammonium chloride, trihydroxyethylmet...

Embodiment 3

[0111] A polyvinyl chloride electrostatic film and a preparation method thereof, comprising the following raw materials in parts by weight

[0112] PVC resin 100 parts

[0113] 60 parts plasticizer

[0114] 3 parts heat stabilizer

[0115] Antistatic agent 5 parts

[0116] 0.5 parts of gelling agent

[0117] Pigment powder 0.025 parts

[0118] Other additives 0.2 parts.

[0119] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin in a weight ratio of 10:1.

[0120] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 58:2.

[0121] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and zinc ricinoleate in a weight ratio of 3:1:3 : 1 composition of the mixture.

[0122] The antistatic agent is composed of stearyl dimethyl ammonium chloride, trihydroxyethylmethy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal decomposition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of electrostatic film, and in particular, relates to a polyvinyl chloride electrostatic film and a preparation method thereof, wherein the polyvinyl chloride electrostatic film comprises the following raw materials in parts by weight: 80-120 parts of PVC resin, 46-73 parts of a plasticizer, 1-3 parts of a heat stabilizer, 3-7 parts of an anti-electrostatic agent, 0.3-0.7 part of a gelatinizing agent, 0.02-0.03 part of a pigment powder, and 0.1-0.3 part of other auxiliary agents. The polyvinyl chloride electrostatic film has high electrostatic resistance, has high anti-electrostatic effect and protection functions, has high self-adhesive performance, and has excellent stable performance under high temperature conditions; the polyvinyl chloride electrostatic film also has the advantages of being ultra thin, tough, transparent, self-adhesive, good in transparency, small in watermarks and the like, has fewer crystal points and low-temperature resistance, and has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of electrostatic films, in particular to a polyvinyl chloride electrostatic film and a preparation method thereof. Background technique [0002] Electrostatic film is a kind of non-static film, relying on the electrostatic adsorption of the product itself to adhere to the object for protection. It can be used on surfaces that are sensitive to adhesives or glue residues, such as glass, lenses, high-gloss plastic surfaces and acrylics. Very smooth finish. The existing electrostatic film has poor antistatic effect and poor self-adhesiveness. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present invention is to provide a polyvinyl chloride electrostatic film, which has high static resistance, good antistatic effect and protection function, and high self-adhesiveness. , has excellent stability under high temperature conditions; al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08L71/00C08K13/02C08K5/12C08K5/098C08K5/19C08K5/41C08K5/20C08K3/22C08K3/38B29D7/01
CPCB29D7/01C08L27/06C08L2201/04C08L2203/16C08L2205/02C08L2205/025C08L2205/035C08L91/00C08L71/00C08K13/02C08K5/12C08K5/098C08K5/19C08K5/41C08K5/20C08K2003/2241C08K3/2279C08K2003/387
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap