A kind of Tang Jun glaze with blue and white spots on black background and the process of using it to prepare Jun porcelain

Abstract

The invention relates to a blue-white-spot-on-black Tang Jun glaze and a process for preparing a Jun porcelain by using the blue-white-spot-on-black Tang Jun glaze. The blue-white-spot-on-black Tang Jun glaze comprises two parts such as a black background glaze and a blue-white-spot glaze, wherein the black background glaze and the blue-white-spot glaze are sequentially brushed on a fired billet, drying is performed, and oxidation atmosphere firing is performed during the whole process. According to the present invention, the bottom glaze having the specific formula and the spot glaze having the specific formula are used, and high temperature firing is performed to obtain the Jun porcelain with characteristics of stable color, uniform color and rich jade texture; the spot glaze position is fixed by using the two glazing manner, and the specific proportions of the talc and the bone meal are added in the formula of the glaze, such that the glaze layer cracking is uniform while the bursting is not easily produced; and the on-glaze-color or under-glaze-color coloring process used by the general spot porcelain is broken through, the economic value of the Jun porcelain is increased with the creation on the glaze color and the coating, the Jun porcelain as the Chinese characteristic represents the advanced level of the Chinese production process, and the social value of the Jun porcelain is improved.

Description

technical field

[0001] The invention relates to the field of ceramic manufacturing, in particular to a black-bottomed blue-and-white Tang Jun glaze and a process for preparing Jun porcelain using the same. Background technique

[0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family is rich, not as good as a piece of Jun porcelain". It is a unique national treasure porcelain in Huangdao Town, Pingdingshan City, Henan Province. Simple shapes, exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, and thousands of colors in the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc. The graphic colors and wonderful charm are endlessly changing. The first of the "Five Fa...

Examples

Embodiment 1

[0031] A black-bottom blue-white spot Tang Jun glaze, which is composed of a black-bottom glaze and a blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 42 parts of yellow feldspar, 18 parts of calcite, 25 parts of copper ore, 1 part of quartz sand, 1 part of bone meal, 5 parts of zinc oxide, 2 parts of frit, 10 parts of bentonite, 1 part of zirconium silicate, 3 parts of titanium oxide, 1 part of talc, 3 parts of calcium carbonate, 2 parts of magnesium carbonate, 0.2 part of potassium dichromate, 0.1 part of cobalt oxide and 0.3 part of sodium hydroxide, among which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0032] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0033] The process of making Jun porcelain using blue and white white Tang Jun glaze on a black background...

Embodiment 2

[0045] A black-bottom blue-white spot Tang Jun glaze, which is composed of a black-bottom glaze and a blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 43 parts of yellow feldspar, 20 parts of calcite, 26 parts of copper ore, 2 parts of quartz sand, 2 parts of bone meal, 6 parts of zinc oxide, 2.5 parts of frit, 11 parts of bentonite, 1.5 parts of zirconium silicate, 3.5 parts of titanium oxide, 1.5 parts of talc, 3.5 parts of calcium carbonate, 2.5 parts of magnesium carbonate, 0.3 parts of potassium dichromate, 0.2 parts of cobalt oxide and 0.35 parts of sodium hydroxide, of which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0046] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0047] The process of making Jun porcelain using blue and white white Tang Jun glaze on a...

Embodiment 3

[0059] A black-bottom blue-white spot Tang Jun glaze, which is composed of black bottom glaze and blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 47 parts of yellow feldspar, 21 parts of calcite, 27 parts of copper ore, 3 parts of quartz sand, 2 parts of bone meal, 6 parts of zinc oxide, 4 parts of frit, 11 parts of bentonite, 2 parts of zirconium silicate, 4 parts of titanium oxide, 2 parts of talc, 4 parts of calcium carbonate, 3 parts of magnesium carbonate, 0.5 parts of potassium dichromate, 0.3 parts of cobalt oxide and 0.4 parts of sodium hydroxide, among which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0060] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0061] The process of making Jun porcelain using blue and white white Tang Jun glaze on a black backgro...

technical field

[0001] The invention relates to the field of ceramic manufacturing, in particular to a black-bottomed blue-and-white Tang Jun glaze and a process for preparing Jun porcelain using the same. Background technique

[0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family is rich, not as good as a piece of Jun porcelain". It is a unique national treasure porcelain in Huangdao Town, Pingdingshan City, Henan Province. Simple shapes, exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, and thousands of colors in the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc. The graphic colors and wonderful charm are endlessly changing. The first of the "Five Fa...

Examples

Embodiment 1

[0031] A black-bottom blue-white spot Tang Jun glaze, which is composed of a black-bottom glaze and a blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 42 parts of yellow feldspar, 18 parts of calcite, 25 parts of copper ore, 1 part of quartz sand, 1 part of bone meal, 5 parts of zinc oxide, 2 parts of frit, 10 parts of bentonite, 1 part of zirconium silicate, 3 parts of titanium oxide, 1 part of talc, 3 parts of calcium carbonate, 2 parts of magnesium carbonate, 0.2 part of potassium dichromate, 0.1 part of cobalt oxide and 0.3 part of sodium hydroxide, among which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0032] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0033] The process of making Jun porcelain using blue and white white Tang Jun glaze on a black background...

Embodiment 2

[0045] A black-bottom blue-white spot Tang Jun glaze, which is composed of a black-bottom glaze and a blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 43 parts of yellow feldspar, 20 parts of calcite, 26 parts of copper ore, 2 parts of quartz sand, 2 parts of bone meal, 6 parts of zinc oxide, 2.5 parts of frit, 11 parts of bentonite, 1.5 parts of zirconium silicate, 3.5 parts of titanium oxide, 1.5 parts of talc, 3.5 parts of calcium carbonate, 2.5 parts of magnesium carbonate, 0.3 parts of potassium dichromate, 0.2 parts of cobalt oxide and 0.35 parts of sodium hydroxide, of which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0046] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0047] The process of making Jun porcelain using blue and white white Tang Jun glaze on a...

Embodiment 3

[0059] A black-bottom blue-white spot Tang Jun glaze, which is composed of black bottom glaze and blue-white spot glaze. The raw materials for forming the blue-white spot glaze are 47 parts of yellow feldspar, 21 parts of calcite, 27 parts of copper ore, 3 parts of quartz sand, 2 parts of bone meal, 6 parts of zinc oxide, 4 parts of frit, 11 parts of bentonite, 2 parts of zirconium silicate, 4 parts of titanium oxide, 2 parts of talc, 4 parts of calcium carbonate, 3 parts of magnesium carbonate, 0.5 parts of potassium dichromate, 0.3 parts of cobalt oxide and 0.4 parts of sodium hydroxide, among which the copper ore was taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0060] According to the weight ratio, the raw material of the black base glaze is black medicine soil taken from Huangdao Town, Jiaxian County, Pingdingshan City, Henan Province.

[0061] The process of making Jun porcelain using blue and white white Tang Jun glaze on a black backgro...