The method for producing barium chloride by using barium sulfate barium slag

A production method and barium chloride technology, applied in the direction of calcium/strontium/barium chloride, calcium/strontium/barium halide, etc., can solve the problems of difficult feasibility and waste of resources, and achieve simple equipment structure and process, saving The effect of intermediate equipment and quick replacement

Active Publication Date: 2018-02-09
帕特克(武汉)科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It contains a considerable amount of acid-soluble barium, which will cause waste of resources if not recycled
Judging from the current papers and patents on the production of barium chloride by the barium slag method, it is only a general theoretical discussion, and there is no separation of impurities and particles brought by the slag, such as calcium, magnesium, sulfite, thiosulfate, etc. Propose methods that pose difficulties to the feasibility of putting into production implementation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • The method for producing barium chloride by using barium sulfate barium slag
  • The method for producing barium chloride by using barium sulfate barium slag
  • The method for producing barium chloride by using barium sulfate barium slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] In order to make the above-mentioned purposes, features and advantages of the present invention more obvious and understandable, the specific implementation modes of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the above-mentioned and other purposes, features and advantages of the present invention will be clearer. Like reference numerals designate like parts throughout the drawings. The drawings have not been drawn to scale, emphasis instead being placed upon illustrating the gist of the invention.

[0011] see figure 1 , the method that barium sulfate barium slag of the present invention produces barium chloride comprises the following steps:

[0012] S100: Send the barium slag into the ball mill through the barium slag conveying device, use the ball mill to grind the barium slag together with water or dilute barium chloride solution into a slurry; refer to figure 2 , the barium slag mechanized conve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing barium chloride through barium residues of barium sulfate. The method comprises the following steps of: S100, grinding the barium residues with water or a dilute barium chloride solution into slurry through a ball mill; S200, adding hydrochloric acid to the obtained slurry, performing a reaction so as to obtain a barium chloride mixed solution, and controlling the PH value of a terminal point to be 6.5-7.5; S300, performing filtering separation on the obtained mixed solution, abandoning residues, reusing the abandoned residues, enabling washing water to be used for the ball mill, and enabling a mixed clear solution to be used for a next working procedure; and S400, adding hydrogen peroxide to the solution obtained in the S300, and performing oxidation so that vulcanized sulfate ions and sulfinic acid ions are converted into sulfate ions to be removed, and bivalent iron ions are oxidized into ferric ions. According to the method disclosed by the invention, the barium residues are effectively utilized, and the purity of the prepared barium chloride is high.

Description

technical field [0001] The invention belongs to the field of chemical industry, in particular to a barium chloride production method. Background technique [0002] At present, the barium slag in the domestic barium salt industry is basically stored on site, or buried, and partially made into bricks and cement. It contains a considerable amount of acid-soluble barium, which will cause waste of resources if not recycled. Judging from the current papers and patents on the production of barium chloride by the barium slag method, it is only a general theoretical discussion, and there is no separation of impurities and particles brought by the slag, such as calcium, magnesium, sulfite, thiosulfate, etc. The proposed method brings difficulties to the feasibility of putting it into production. Contents of the invention [0003] Aiming at the defects of the prior art, the present invention provides a method for producing barium chloride, comprising the following steps: S100: use ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01F11/24
CPCC01F11/24
Inventor 丁淑暖
Owner 帕特克(武汉)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products