Lace printing sheet and double-fitting process thereof

A printing and sheet technology, applied in the field of lace printing sheet and its double lamination process, can solve the problems of poor wear resistance and anti-skid performance of lace printing sheet, poor color brightness and saturation of printing pattern, and poor overall performance, etc. The effect of exquisite pattern, low production cost and high production efficiency

Inactive Publication Date: 2016-12-14
DONGGUAN IUIU HOUSEHOLD PROD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing lace printing sheet products have always been produced by printing on the surface of the lace hollow pattern and then silk screen printing. Due to the limitation of the printing process of the hollow three-dimensional pattern, the color brightness and saturation of the printed pattern are relatively poor; and the existing lace The printing sheet has poor wear resistance and anti-skid performance, and the overall performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A lace printing sheet, comprising the following raw materials in parts by weight:

[0059] PVC resin 45 parts

[0060] Filling agent 55 parts

[0061] Plasticizer 23 parts

[0062] 2 parts heat stabilizer

[0063] Foaming agent 1 part

[0064] Lubricant 0.4 parts

[0065] Titanium dioxide 0.01 parts

[0066] Pigment powder 0.01 parts

[0067] Other additives 0.15 parts.

[0068] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin in a weight ratio of 8:1.

[0069] The filler is nano-active calcium carbonate with a particle diameter of 10 nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0070] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 20:3.

[0071] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and...

Embodiment 2

[0087] A lace printing sheet, comprising the following raw materials in parts by weight:

[0088] PVC resin 48 parts

[0089] Filling agent 58 parts

[0090] Plasticizer 25 parts

[0091] Heat stabilizer 2.5 parts

[0092] Foaming agent 1.5 parts

[0093] Lubricant 0.6 parts

[0094] Titanium dioxide 0.04 parts

[0095] Pigment powder 0.04 parts

[0096] Other additives 0.30 parts.

[0097] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin at a weight ratio of 9:1.

[0098] The filler is nano active calcium carbonate with a particle size of 30nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0099] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 22:3.

[0100] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and...

Embodiment 3

[0116] A lace printing sheet, comprising the following raw materials in parts by weight:

[0117] PVC resin 50 parts

[0118] Filling agent 60 parts

[0119] Plasticizer 29 parts

[0120] 3 parts heat stabilizer

[0121] Foaming agent 2 parts

[0122] Lubricant 0.7 parts

[0123] Titanium dioxide 0.08 parts

[0124] Pigment powder 0.08 parts

[0125] Other additives 0.45 parts.

[0126] The PVC resin is a mixture of ethylene-based PVC resin and calcium carbide-based PVC resin in a weight ratio of 10:1.

[0127] The filler is nano active calcium carbonate with a particle size of 50nm and treated with maleic anhydride grafted styrene-isoprene-styrene block copolymer.

[0128] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 25:4.

[0129] The heat stabilizer is a calcium-zinc composite heat stabilizer, and the calcium-zinc composite heat stabilizer is composed of calcium stearate, calcium ricinoleate, zinc stearate and zi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of sheets, in particular to a lace printing sheet and a double-fitting process thereof. The lace printing sheet is prepared from, by weight, 45-55 parts of PVC resin, 55-65 parts of filler, 23-35 parts of plasticizer, 2-4 parts of heat stabilizer, 1-3 parts of foaming agent, 0.4-1.0 part of lubricant, 0.01-0.15 part of titanium dioxide, 0.01-0.16 part of pigment powder and 0.15-0.70 part of other additives. The lace printing sheet is good in abrasion resistance, good in anti-slipping effect, delicate in texture, exquisite in pattern, gorgeous in color, smooth in surface and comfortable in hand feeling, also has the advantages of being environmentally friendly, non-toxic, waterproof, oilproof, high in cold resistance, antistatic, flame-retardant, easy to clean and the like and has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of sheets, in particular to a lace printing sheet and a double lamination process thereof. Background technique [0002] Existing lace printing sheet products have been produced by printing on the surface of the lace hollow pattern and then silk screen printing. Due to the limitation of the printing process of the hollow three-dimensional pattern, the color brightness and saturation of the printed pattern are relatively poor; and the existing lace The printed sheet has poor wear resistance and anti-skid performance, and the overall performance is poor. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present invention is to provide a lace printing sheet, which has good wear resistance, good anti-skid effect, fine texture, exquisite patterns, bright colors and smooth surface , comfortable to touch; also has the characteristics of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08L9/06C08L7/00C08K13/06C08K9/08C08K3/26C08K5/12C08K5/098C08K3/22C08K3/38C08J9/10
CPCC08J9/102C08J9/103C08J2203/04C08J2203/18C08J2327/06C08J2491/00C08K2201/003C08K2201/011C08K2201/014C08L27/06C08L2201/02C08L2201/04C08L2203/14C08L2205/025C08L2205/035C08L91/00C08L9/06C08L7/00C08K13/06C08K9/08C08K2003/265C08K5/12C08K5/098C08K2003/2241C08K3/2279C08K2003/387
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com