Cable material with impact performance enhanced by methyl methacrylate copolymer

A technology of methyl methacrylate and impact properties, applied in the direction of insulating cables, cables, circuits, etc., can solve problems such as environmental pollution, reduce the modulus of composite materials, and achieve poor impact resistance and toughness, interface compatibility The effect of improving the performance and improving the dispersibility

Inactive Publication Date: 2016-12-21
ANHUI ZHONGRUN CABLE GRP SHARES CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the thermoplastic polyurethane elastomer improves the toughness of the polyvinyl chloride material, it also reduces the modulus of the composite material at the same time, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A cable material with enhanced impact performance of methyl methacrylate copolymer, prepared from the following raw materials in parts by weight (kg): thermoplastic polyurethane elastomer 60, polyvinyl chloride 35, stearic acid 0.1, calcium benzoate 5, Mercaptan methyl tin heat stabilizer 0.8, titanate coupling agent 1310.2, epoxy soybean oil 19, molybdenum disulfide 2, polysiloxane emulsion 3, sodium dodecylbenzene sulfonate 0.1, nonylphenol poly Oxyethylene ether 0.08, methyl methacrylate 3, butyl acrylate 9, ammonium persulfate 0.1, appropriate amount of deionized water.

[0015] The cable material for enhancing the impact performance of a methyl methacrylate copolymer is made by the following specific steps:

[0016] (1) Put calcium benzoate into a high-speed mixer, heat to 100°C, add stearic acid and titanate coupling agent 131, stir at 1000 rpm for 20 minutes, and discharge for use;

[0017] (2) Add polyvinyl chloride into the high-speed mixer, add mercaptan meth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cable material with impact performance enhanced by methyl methacrylate copolymer. The cable material is prepared from, by weight, 60-65 parts of thermoplastic polyurethane elastomer, 35-40 parts of polyvinyl chloride, 0.1-0.12 part of stearic acid, 5-6 parts of calcium benzoate, 0.8-1 part of thio methyl tin thermal stabilizer, 0.2-0.3 part of titanate coupling agent 131, 19-20 parts of epoxy soybean oil, 2-3 parts of molybdenum disulfide, 3-4 parts of polysiloxane emulsion, 0.1-0.2 part of sodium dodecyl benzene sulfonate, 0.08-0.1 part of nonyl phenol polyoxyethylene ether, 3-4 parts of methyl methacrylate, 9-10 parts of butyl acrylate, 0.1-0.12 part of ammonium persulfate and a proper amount of water. The cable material solves the problem that existing cable materials are low in impact resistance and tenacity and has high heat resistance and size stability, and a process is convenient for industrial mass production and can be widely used in the field of cable material processing.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a cable material in which a methyl methacrylate copolymer enhances impact performance. Background technique [0002] Polyvinyl chloride (PVC) is characterized by high withstand voltage and insulation resistance, and has properties such as flame retardancy, oil resistance, weather resistance, and chemical resistance, but its dielectric constant and dielectric loss are large, and its cold resistance is poor. Plastic has the characteristics of low price, large usage, and excellent performance in all aspects. It is mainly used in insulation, semi-conductive shielding and sheathing of various wires and cables for wires and cables below 1kV and local communication cables. Thermoplastic polyurethane elastomers have the characteristics of plastic reprocessing and rubber elasticity, and are excellent in cold resistance, abrasion resistance and antibacterial properties. Thermoplas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L27/06C08L91/00C08L83/04C08L33/08C08K13/06C08K9/04C08K5/098C08K5/09C08K5/58H01B3/30H01B3/44H01B7/18
CPCC08L75/04C08L2201/08C08L2203/202C08L2205/035C08L2207/04H01B3/302H01B3/443H01B7/18C08L27/06C08L91/00C08L83/04C08L33/08C08K13/06C08K9/04C08K5/098C08K5/09C08K5/58
Inventor 洪生华胡桂芝陆秀忠
Owner ANHUI ZHONGRUN CABLE GRP SHARES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap