A preparation process, graphene technology, applied in textiles, papermaking, fiber processing, etc., can solve problems such as uneven dispersion, unstable quality, and needle damage

Inactive Publication Date: 2017-01-04
JIANGSU XINKAISHENG ENTERPRISE DEV
View PDF9 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention also enables graphene to be applied in the textile field through a certain process to exert its special function. The fabric has excellent antistatic and conductive properties. There are two common conductive fibers on the market at present, one is similar to spinning masterbatch The conductive filament spun from conductive materials is added to it, but its quality is unstable due to uneven dispersion, high resistance, and unstable quality; the other is an all-metal conductive fiber similar to aluminum and stainless steel fibers, but its weaving also causes damage to the knitting needles, and Its material properties are different from those of polyester, and there are many defects on the fabric surface, which are difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A preparation process for graphene-coated fabrics, comprising the following steps:

[0018] 1) Plate making: make rubber plates according to the requirements of the coating pattern;

[0019] 2) Solution preparation: solvents include organic solvents with a mass fraction of 45-60% for dispersing graphene and cross-linking agents with a mass fraction of 35-40%; solutes include metal powders with a mass fraction of 3-5% and a mass fraction of 5-8 % of graphene powder, mix the solute and solvent, stir fully to make it evenly dispersed;

[0020] 3) Coating: Coat the uniformly dispersed graphene mixture on the fabric within 3 hours;

[0021] 4) Drying and setting: put the coated fabric into the oven, and control the temperature of each section of the oven;

[0022] 5) Aging: Curing the dried fabric and placing it at a constant temperature of 50-60°C for 24 hours to obtain the final product.

[0023] As a preference, in the above-mentioned graphene-coated fabric preparation...

Embodiment 1

[0025] As a preference, in the above graphene-coated fabric preparation process, the plate-making process in step 1) is engraved in a series circuit mode.

[0026] As a preference, step 2), solution preparation: the solvent includes an organic solvent with a mass fraction of 50% for dispersing graphene, and a crosslinking agent with a mass fraction of 40%; the solute has a metal powder with a mass fraction of 3%, and a mass fraction of 7%. graphene powder. Mix the solute and solvent and stir well to make it evenly dispersed.

[0027] As a preference, step 3), coating: the graphene mixture must be coated within 3 hours after dispersion, the coating control machine speed is 2m / min, the gluing scale is 0.3mm, and the coating thickness is 0.2mm.

[0028] As a preference, step 4), drying and shaping: control the oven temperature of each section to 60-80°C for the 1st-3rd section, 120-150°C for the 4th-6th section, and 90-110°C for the 7th-8th section.

[0029] As a preference, in...

Embodiment 2

[0033] As a preference, in the above graphene-coated fabric preparation process, the plate-making process in step 1) is used to make football grids.

[0034] As a preference, step 2), solution preparation: the solvent includes an organic solvent with a mass fraction of 52% of dispersed graphene, a crosslinking agent with a mass fraction of 36%; the solute has a metal powder with a mass fraction of 4%, and a mass fraction of 8% Graphene powder. Mix the solute and solvent and stir well to make it evenly dispersed.

[0035] As a preference, step 3), coating: the graphene mixture must be coated within 3 hours after dispersion, the coating control machine speed is 1m / min, the gluing scale is 0.4mm, and the coating thickness is 0.4mm.

[0036] As a preference, step 4), drying and shaping: control the oven temperature of each section to 60-80°C for the 1st-3rd section, 120-150°C for the 4th-6th section, and 90-110°C for the 7th-8th section.

[0037] As a preference, in step 5), rip...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation process of a graphene coating fabric. The preparation process comprises the following steps of 1 plate making, 2 solution preparation, 3 coating, 4 drying and shaping and 5 curing. The invention also provides a grapheneformula and a coating process thereof. The high electric and thermal conductivity properties of the textile fabric are improved, the washing resistance is improved, the anti-static-electricity and conductive functions of the fabric are excellent and durable, the fabric is better than conductive fiber commonly used in the market in effect, patterns can be designed for a coating, for example, micro circuit board carving, graphene can replace electric wires, circuit electrification can be formed on a garment material, various micro-electronic components are added to make intelligent clothes, and the fabric requirements of the scientific era are met.

Description

technical field [0001] The invention belongs to the field of textile fabric processing, in particular to a preparation process of a graphene-coated fabric. Background technique [0002] With the development of science and technology, new materials have been discovered and applied one after another. Among them, the appearance of graphene is known as the material that will change the 21st century, and it is known as the black gold in the material industry. Graphene is a two-dimensional crystal composed of carbon atoms with only one atomic thickness. Graphene is not only the thinnest material, but also the strongest material, with a fracture strength 200 times higher than the best steel. At the same time, it has good elasticity, and the stretching range can reach 20% of its own size. It is currently the thinnest and strongest material in nature. If a piece of graphene with an area of ​​1 square meter is used to make a hammock, it can bear a cat weighing one kilogram with a wei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/74
CPCD06M11/74
Inventor 张卫东奚炳华陈亮
Owner JIANGSU XINKAISHENG ENTERPRISE DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap