Quick drying glue spray

A glue spraying and drying technology, which is applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of insufficient drying, narrow application range, and improvement of adhesion, and achieve good temperature resistance and dryness. Fast and strong effect

Inactive Publication Date: 2017-01-11
无锡万能胶粘剂有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the temperature resistance of the currently used spray glue is not good, the drying is not fast enough, the adhesion force needs to be improved, and the application range is narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A fast-drying spray gel made from the following components: ethyl caprate, 2-[3-(1,3-dioxolan-2-yl)-1-hydroxypropylphenyl ]-Ethyl 2-methylpropionate, (R)-2-Hydroxy-4-phenylbutyric acid ethyl ester, 3,5-dicaffeoylquinic acid, luteolin-7-O-malonyl Glucoside, vinyl chloride-vinyl acetate plastics and polyethylene terephthalate, the weight content of each component is: 17 parts of ethyl caprate, 2-[3-(1,3-dioxolane 29 parts of ethyl (alk-2-yl)-1-hydroxypropylphenyl]-2-methylpropionate, 31 parts of ethyl (R)-2-hydroxy-4-phenylbutyrate, 3,5- 26 parts of dicaffeoyl quinic acid, 12 parts of luteolin-7-O-malonyl glucoside, 51 parts of vinyl chloride-vinyl acetate plastic and 38 parts of polyethylene terephthalate.

Embodiment 2

[0015] A fast-drying spray gel made from the following components: ethyl caprate, 2-[3-(1,3-dioxolan-2-yl)-1-hydroxypropylphenyl ]-Ethyl 2-methylpropionate, (R)-2-Hydroxy-4-phenylbutyric acid ethyl ester, 3,5-dicaffeoylquinic acid, luteolin-7-O-malonyl Glucoside, vinyl chloride-vinyl acetate plastics and polyethylene terephthalate, the weight content of each component is: 24 parts of ethyl caprate, 2-[3-(1,3-dioxolane 36 parts of ethyl (alk-2-yl)-1-hydroxypropylphenyl]-2-methylpropionate, 37 parts of ethyl (R)-2-hydroxy-4-phenylbutyrate, 3,5- 34 parts of dicaffeoyl quinic acid, 18 parts of luteolin-7-O-malonyl glucoside, 57 parts of vinyl chloride-vinyl acetate plastic and 45 parts of polyethylene terephthalate.

Embodiment 3

[0017] A fast-drying spray gel made from the following components: ethyl caprate, 2-[3-(1,3-dioxolan-2-yl)-1-hydroxypropylphenyl ]-Ethyl 2-methylpropionate, (R)-2-Hydroxy-4-phenylbutyric acid ethyl ester, 3,5-dicaffeoylquinic acid, luteolin-7-O-malonyl Glucoside, vinyl chloride-vinyl acetate plastics and polyethylene terephthalate, the weight content of each component is: 10 parts of ethyl caprate, 2-[3-(1,3-dioxolane 22 parts of ethyl (alk-2-yl)-1-hydroxypropylphenyl]-2-methylpropionate, 25 parts of ethyl (R)-2-hydroxy-4-phenylbutyrate, 3,5- 18 parts of dicaffeoyl quinic acid, 6 parts of luteolin-7-O-malonyl glucoside, 45 parts of vinyl chloride-vinyl acetate plastic and 30 parts of polyethylene terephthalate.

[0018] The beneficial effects of the quick-drying spray glue of the present invention are: the present invention has good temperature resistance, fast drying, and strong bonding force, and is suitable for large-area bonding of wood, fireproof board, plastic skin EVA,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a quick drying glue spray. The glue spray is prepared from, by weight, 10-24 parts of ethyl decanoate, 18-40 parts of 2-[3-(1, 3-dioxolane-2-radical)-1-hydroxypropyl phenyl]-ethyl-2-methylpropanoate, 25-37 parts of (R)-2-4-phenyl ethyl butyrate, 16-36 parts of 3, 5-dicaffeoyl-quinic acid, 5-19 parts of luteolin-7-O-malonyl glucoside, 45-57 parts of vinyl chloride-vinyl acetate plastic, and 30-45 parts of polyethylene glycol terephthalate. The quick drying glue spray has the advantages of good temperature resistance, quick drying and strong adhesion force, accordingly the quick drying glue spray is suitable for the large-area bonding of wood, fireproof board, plastic leather EVA, sponge, paperboard, cloth product and the like.

Description

technical field [0001] The invention relates to the field of glue spraying, in particular to a fast-drying glue spraying. Background technique [0002] The concept of adhesive: Adhesive is a substance that firmly bonds various solid materials together by interfacial action (chemical force or physical force). It is also called adhesive or adhesive, referred to as "glue". [0003] Adhesives are widely used in various fields of the national economy, such as construction, packaging, aerospace, aviation, electronics, automobiles, machinery and equipment, medical and health care, and textiles. [0004] However, the temperature resistance of the currently used spray glue is not good, the drying is not fast enough, the adhesion force needs to be improved, and the application range is narrow. Contents of the invention [0005] The main technical problem to be solved by the present invention is to provide a fast-drying spray glue, which has good temperature resistance, fast drying ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J127/06C09J167/02C09J11/06
CPCC09J127/06C08K2201/014C08L2201/08C09J11/06C08L67/02C08K5/101C08K5/1345C08K5/1545
Inventor 杜晓南
Owner 无锡万能胶粘剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com