Processing method of colorful compounded rubber floor

A technology of compound rubber and processing method, applied in household components, applications, household appliances, etc., can solve the problems of poor anti-skid performance, short service life, long construction period, etc., and achieve convenient and fast construction process, long service life, cost low effect

Inactive Publication Date: 2017-01-25
刘浩杰
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the most common pavement includes asphalt pavement, cement pavement and pavement pavement. Among them, the construction period of asphalt pavement and cement pavement is long, and the color is single, while the pavement paved with pavement can have multiple colors, but Short service life, heavy weight and poor anti-skid performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method of colorful compounded rubber floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Rubber material preparation: prepare rubber-plastic composite film and semi-finished rubber film according to 2030mm×1000mm. The rubber-plastic composite layer is made of 70 parts by weight of nitrile rubber: 30 parts by weight of PVC resin, mixed with auxiliary materials. The auxiliary material is white Carbon black, magnesium oxide, reinforcements and fillers. The rubber film is made of natural rubber, styrene-butadiene rubber and butadiene rubber after mixing with auxiliary materials, such as carbon black, calcium carbonate, anti-aging agent and other fillers.

[0023] (2) Forming and compounding: the above-mentioned rubber-plastic composite film and the semi-finished rubber film are pressed together and put into the mold together.

[0024] (3) Vulcanization: when vulcanized, the temperature is 140°C and the pressure is 20kg / cm 2 , the vulcanization time is 30 minutes, after the vulcanization, the above-mentioned plastic composite film and rubber film are formed...

Embodiment 2

[0029] (1) Rubber material preparation: prepare rubber-plastic composite film and semi-finished rubber film according to 2030mm×1000mm. The rubber-plastic composite layer is made of 70 parts by weight of nitrile rubber: 30 parts by weight of PVC resin, mixed with auxiliary materials. The auxiliary material is white Carbon black, magnesium oxide, reinforcements and fillers. The rubber film is made of natural rubber, styrene-butadiene rubber and butadiene rubber after mixing with auxiliary materials, such as carbon black, calcium carbonate, anti-aging agent and other fillers.

[0030] (2) Forming and compounding: the above-mentioned rubber-plastic composite film and the semi-finished rubber film are pressed together and put into the mold together.

[0031] (3) Vulcanization: when vulcanized, the temperature is 145°C and the pressure is 26kg / cm 2 , the vulcanization time is 35 minutes, after the vulcanization, the above-mentioned plastic composite film and rubber film are formed...

Embodiment 3

[0036] (1) Rubber material preparation: prepare rubber-plastic composite film and semi-finished rubber film according to 2030mm×1000mm. The rubber-plastic composite layer is made of 70 parts by weight of nitrile rubber: 30 parts by weight of PVC resin, mixed with auxiliary materials. The auxiliary material is white Carbon black, magnesium oxide, reinforcements and fillers. The rubber film is made of natural rubber, styrene-butadiene rubber and butadiene rubber after mixing with auxiliary materials, such as carbon black, calcium carbonate, anti-aging agent and other fillers.

[0037] (2) Forming and compounding: the above-mentioned rubber-plastic composite film and the semi-finished rubber film are pressed together and put into the mold together.

[0038] (3) Vulcanization: when vulcanized, the temperature is 150°C and the pressure is 30kg / cm 2 , the vulcanization time is 40 minutes, after the vulcanization, the above-mentioned plastic composite film and rubber film are formed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing method of a colorful compounded rubber floor. The processing method comprises the following processing steps of (1) preparing sizing materials: preparing a rubber-plastic compound rubber piece semi-finished product and a rubber-plastic piece semi-finished product;(2) forming and compounding: putting the two semi-finished products into a mold; (3)vulcanizing: vulcanizing for 30 to 40 minutes at the temperature of 140 to 150 DEG C and the pressure of 20 to 30kg / cm<2>, forming the two rubber pieces together after vulcanizing so as to obtain a compound rubber piece, and respectively forming a rubber-plastic compound layer and a rubber layer; (4) polishing the surface of the rubber-plastic compound layer, and finally spraying a layer of polyurethane resin to form a polyamine particle layer on the surface of the rubber-plastic compound layer, thus obtaining the colorful compounded rubber floor. A pavement paved by the colorful compounded rubber floor prepared by the method is particularly suitable for being regarded as a road used by pedestrians or non-motor vehicles, so that the phenomenon that the the pedestrians slip and fall easily in rainy days when walking on current pavement bricks is avoided.

Description

technical field [0001] The invention relates to a processing method of an artificial colored pavement, in particular to a processing method of an artificial colored composite rubber floor, and the product obtained by the method is used for laying the pavement. Background technique [0002] At present, the most common pavement includes asphalt pavement, cement pavement and pavement pavement. Among them, the construction period of asphalt pavement and cement pavement is long, and the color is single, while the pavement paved with pavement can have multiple colors, but The service life is short, the weight is large and the anti-skid performance is not good. Contents of the invention [0003] The object of the present invention is exactly to aim at the above-mentioned deficiencies in the prior art, and provides a kind of brightly colored, long service life, antiskid and wear-resisting, the processing method of the colored composite rubber floor that is easy to maintain and rep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29D99/00C08L9/02C08L27/06C08K13/02C08K3/36C08K3/22C08L7/00C08L9/06C08L9/00C08K3/04C08K3/26
CPCB29D99/0057C08L7/00C08L9/00C08L9/02C08L9/06C08L2205/02C08L2205/03C08L27/06C08K13/02C08K3/36C08K2003/222C08K3/04C08K2003/265
Inventor 刘浩杰
Owner 刘浩杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com