Fiber filter felt for photocatalytic sewage treatment and preparation method of fiber filter felt

A technology for fiber filtration and sewage treatment, applied in the direction of light water/sewage treatment, water/sludge/sewage treatment, chemical instruments and methods, etc., can solve the problems of catalyst adsorption performance, light utilization rate reduction, and low catalytic activity, etc., to achieve Good visible light response, increased specific surface area, and good light transmittance

Inactive Publication Date: 2017-01-25
朱凤兮
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, once immobilized, the adsorption performance and light utilization rate of the catalyst will be reduced, resulting in low catalytic activity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A fiber filter mat for photocatalytic sewage treatment, which uses glass fiber as a base material and a photocatalytic material as a coating layer to obtain a photocatalytic fiber filter felt, and the photocatalytic material adopts a mixed modified photocatalyst.

[0030] The mixed modified photocatalyst adopts nitrogen modified mixed photocatalyst.

[0031] The mixed photocatalyst adopts the mixed photocatalyst of zinc oxide and titanium dioxide.

[0032] The preparation method of described fibrous filter felt, its steps are as follows:

[0033] Step 1, dispersing and weaving the glass fiber bundles to form a fiber mat;

[0034] Step 2, soak the fiberglass felt in water, add neutral detergent, ultrasonically clean, then clean with water, and dry naturally;

[0035] Step 3, soak the glass fiber mat into the lye, aerate and heat the reaction, and then dry it;

[0036] Step 4, after soaking the glass fiber mat in step 3 in acid solution, cleaning it with ultrasonic wat...

Embodiment 2

[0049] A fiber filter mat for photocatalytic sewage treatment, which uses glass fiber as a base material and a photocatalytic material as a coating layer to obtain a photocatalytic fiber filter felt, and the photocatalytic material adopts a mixed modified photocatalyst.

[0050] The mixed modified photocatalyst adopts nitrogen modified mixed photocatalyst.

[0051] The mixed photocatalyst adopts the mixed photocatalyst of zinc oxide and titanium dioxide.

[0052] The preparation method of described fibrous filter felt, its steps are as follows:

[0053] Step 1, dispersing and weaving the glass fiber bundles to form a fiber mat;

[0054] Step 2, soak the fiberglass felt in water, add neutral detergent, ultrasonically clean, then clean with water, and dry naturally;

[0055] Step 3, soak the glass fiber mat into the lye, aerate and heat the reaction, and then dry it;

[0056] Step 4, after soaking the glass fiber mat in step 3 in acid solution, cleaning it with ultrasonic wat...

Embodiment 3

[0069] A fiber filter mat for photocatalytic sewage treatment, which uses glass fiber as a base material and a photocatalytic material as a coating layer to obtain a photocatalytic fiber filter felt, and the photocatalytic material adopts a mixed modified photocatalyst.

[0070] The mixed modified photocatalyst adopts nitrogen modified mixed photocatalyst.

[0071] The mixed photocatalyst adopts the mixed photocatalyst of zinc oxide and titanium dioxide.

[0072] The preparation method of described fibrous filter felt, its steps are as follows:

[0073] Step 1, dispersing and weaving the glass fiber bundles to form a fiber mat;

[0074] Step 2, soak the fiberglass felt in water, add neutral detergent, ultrasonically clean, then clean with water, and dry naturally;

[0075] Step 3, soak the glass fiber mat into the lye, aerate and heat the reaction, and then dry it;

[0076] Step 4, after soaking the glass fiber mat in step 3 in acid solution, cleaning it with ultrasonic wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fiber filter felt for photocatalytic sewage treatment and a preparation method of the fiber filter felt. The photocatalytic fiber filter felt is prepared from glass fibers serving as a base material and a photocatalytic material serving as a coated layer; the photocatalytic material adopts a mixed modified photocatalyst. The fiber felt prepared through the preparation method has the characteristics of small wind resistance, high light transmittance and the like, has good visible light response and is excellent in photocatalytic degradability.

Description

technical field [0001] The invention belongs to the technical field of sewage treatment, and in particular relates to a fiber filter felt for photocatalytic sewage treatment and a preparation method thereof. Background technique [0002] Photocatalytic technology uses ultraviolet light to irradiate photocatalytically active semiconductor materials to generate photogenerated holes and photogenerated electrons on the surface. Photogenerated holes and the hydroxyl radicals generated after being captured have strong oxidizing ability and can almost All organic pollutants. Photocatalytic technology is characterized by effective use of light energy, easy operation, and no secondary pollution, and is widely used in the field of air purification. In terms of morphology, photocatalysts can be divided into two types: powder type and supported type. The former has relatively high catalytic activity, but the fine powder is easy to agglomerate in the process of air purification, which a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/30B01J23/06C02F101/30
CPCC02F1/30B01J23/06C02F2101/30B01J35/39
Inventor 朱凤兮
Owner 朱凤兮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com