A method for preparing iron-based inhibitors using converter steel slag as raw material and its application

A converter steel slag and inhibitor technology, applied in fuel, solid fuel, petroleum industry, etc., can solve the problems of unreported, low value-added steel slag, restrictions, etc., achieve obvious emission reduction effect, reduce emission cost, and well control emission effect of effect

Active Publication Date: 2019-05-07
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The former belongs to the utilization mode of low added value of steel slag; the latter belongs to the utilization mode of higher added value, but is limited due to the high amount of P in steel slag
Therefore, in view of the current dual problems of metallurgical steel slag solid waste discharge and coal-fired air pollution in my country, from the perspective of "pollution control with waste", it was found that the main component of the solid waste "metallurgical steel slag" discharged from the metallurgical industry is Fe 、 Al 、 Both Mg and trace transition metal elements are components of coal-fired Fe-based nitrogen oxide inhibitors. Since they act as catalysts for coal combustion, they interact with components that are prone to generate nitrogen oxides in coal to achieve synergistic inhibition of NO. The effect of emissions, and the application of this solid waste system to the field of controlling coal-fired nitrogen oxide emissions has not yet been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing iron-based inhibitors using converter steel slag as raw material and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Take 100g of converter slag with a particle size below 200 mesh, add sulfuric acid to adjust the pH value to 2, stir for 30 minutes, and make the Ca ions in the solution dissolve in the form of CaSO 4 Precipitate in the form of precipitation, filter with suction, wash the filter cake twice, and filter with suction until there is no suspended matter in the filtrate, so as to effectively remove CaSO 4 , and then dropwise add hydrogen peroxide in the filtrate, so that Fe in the solution 2+ Fully oxidized to Fe 3+ , and then add ammonia water dropwise to adjust the pH value to 5, so that Fe and traces of Al, Mg and other elements are precipitated in the form of hydroxide precipitation and filtered to obtain a precipitate. Finally, the precipitate is acidified with hydrochloric acid. The pH value of the acid solution is 2. Then heat to raise the solution temperature to 80°C, add evaporated water during the acidolysis process, keep the acidolysis liquid level unchanged, afte...

Embodiment 2

[0024] Take 100g of converter slag with a particle size below 200 mesh, add sulfuric acid to adjust the pH value to 3, stir for 30min, and make the Ca ions in the solution dissolve in the form of CaSO 4 Precipitate in the form of precipitation, filter with suction, wash the filter cake twice, and filter with suction until there is no suspended matter in the filtrate, so as to effectively remove CaSO 4 , and then dropwise add hydrogen peroxide in the filtrate, so that Fe in the solution 2+ Fully oxidized to Fe 3+ , and then add ammonia water dropwise to adjust the pH value to 6, so that Fe and traces of Al, Mg and other elements are precipitated in the form of hydroxide precipitation and filtered to obtain a precipitate. Finally, the precipitate is acidified with hydrochloric acid. The pH value of the acid solution is 3. Then heat to raise the solution temperature to 90°C, add evaporated water during the acidolysis process, keep the acidolysis liquid level unchanged, after 2 h...

Embodiment 3

[0026] Take 100g of converter slag with a particle size below 200 mesh, add sulfuric acid to adjust the pH value to 4, stir for 30 minutes, and make the Ca ions in the solution dissolve in the form of CaSO 4 Precipitate in the form of precipitation, filter with suction, wash the filter cake twice, and filter with suction until there is no suspended matter in the filtrate, so as to effectively remove CaSO 4, and then dropwise add hydrogen peroxide in the filtrate, so that Fe in the solution 2+ Fully oxidized to Fe 3+ , and then add ammonia water dropwise to adjust the pH value to 7, so that Fe and traces of Al, Mg and other elements are precipitated in the form of hydroxide precipitation and filtered to obtain a precipitate. Finally, the precipitate is acidified with hydrochloric acid. The pH value of the acid solution is 4. Then heat to raise the solution temperature to 100°C, add evaporated water during the acidolysis process, keep the acidolysis liquid level unchanged, afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing an iron-base inhibitor mainly from a metallurgical converter steel slag extract and application of the inhibitor in inhibiting coal NO emission, belonging to the technical fields of solid waste high-added-value utilization and pollution control. The method comprises the following steps: decomposing complex components in the converter slag by acidification-precipitation dissolution, firstly removing Ca, using the Fe, Al and other components capable of inhibiting NO generation, which exist in an acid hydrolysis solution in the form of ions, as element sources for preparing the NO inhibitor, and finally, adding hydrochloric acid to precipitate, thereby obtaining the target product. The method overcomes the limit of single dependence on chemical reagents and non-renewable resources in the prior art, fully utilizes the valuable components in the metallurgical solid waste, and provides a new way for high-added-value utilization of iron-containing metallurgical steel slag on the premise of lowering the preparation cost and reducing the oxynitride emission.

Description

technical field [0001] my country emits nitrogen oxides (NOx) into the atmosphere every year x ) of 60% comes from coal combustion, it can be seen that NO x It is one of the important pollutants produced in the process of coal combustion, among which NOx emitted by power plant boilers accounts for x More than 40% of the NO produced by coal combustion x More than 90% of them are NO. Therefore, it is of long-term significance to develop additives that can effectively suppress NO emissions from coal combustion. Background technique [0002] my country emits nitrogen oxides (NOx) into the atmosphere every year x ) of 60% comes from coal combustion, it can be seen that NO x It is one of the important pollutants produced in the process of coal combustion, among which NOx emitted by power plant boilers accounts for x More than 40% of the NO produced by coal combustion x More than 90% of them are NO. Therefore, it is of long-term significance to develop additives that can ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10L9/10
CPCC10L9/10C10L2230/08
Inventor 龙红明高志芳春铁军狄瞻霞孟庆民王平
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com