Coating method of composite toughened slender rod

A composite material and thin rod technology, which is applied in the coating field of composite material toughened thin rods, can solve the problems of unsuitable composite material thin rod modification and difficult to find, and achieves simple method, improved interface performance and high efficiency. Effect

Active Publication Date: 2017-02-15
江苏德晴新材股份有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When conventional coating methods are used to modify toughened thin rods, it is difficult to find a reagent that can bond to both the cured thin rod surface and the uncured laminate
Therefore, traditional coating methods are not suitable for the modification of composite thin rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating method of composite toughened slender rod
  • Coating method of composite toughened slender rod
  • Coating method of composite toughened slender rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Further describe the present invention below in conjunction with embodiment and accompanying drawing thereof:

[0032] It is 0.55mm, the coating process of the coated thin rod of 400 order carbon fiber powder that adopt coating method of the present invention to prepare diameter to provide below:

[0033] Thin rod coating process such as figure 1 shown. A bundle of T300-3k carbon fiber enters the resin tank 2 to impregnate the resin, and then enters the initial forming mold 3, the initial forming mold 3, such as figure 2As shown, there is a circular through-hole mold cavity 301 with a length of 7 mm and a diameter of 0.50 mm.

[0034] Thin rod 10 enters in the coating chamber 4 that fills 400 mesh carbon fiber powders immediately after being pulled out from mold 3, and the total stroke (inner cavity length) of uncured thin rod in coating chamber 4 is 300mm, and the drawing of thin rod 10 The pulling speed is 1m / min. The length direction of the coating chamber 4 is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a coating method of a composite toughened slender rod, and belongs to the technical field of composite surface modification. The coating method comprises the following steps that firstly, fiber bundles soaked in resin penetrate through a small hole primary forming mold, and the circular section shape is formed; secondly, the fiber bundles penetrate through a coating chamber with carbon fiber powder coating stored inside; thirdly, the slender rod passes through a dust collection device which does not make direct contact with the slender rod, and carbon fiber powder which bonded to the surface infirmly are removed; fourthly, the slender rod passes through a preheating device and a heating device for preheating and gelling; fifthly, the slender rod passes through a shaping mold for shaping; sixthly, the slender rod is solidified through the heating device; and finally, the slender rod passes through a dust collector with fine bristle brushes, and fiber powder bonded to the surface of the slender rod infirmly is removed. The coating method can be achieved in the production process of the slender rod, the fiber powder is used as the coating, the bonding performance of coated composites is used, chemical residues are avoided, a separated coating procedure is omitted, the method is simple, and the efficiency is high.

Description

technical field [0001] The invention relates to the surface modification technology of composite materials, in particular to a coating technology for toughened thin rods of composite materials. The coating technology is mainly used to improve the interface performance between toughened thin rods of composite materials and laminated plates. Background technique [0002] Traditional two-dimensional laminated composite materials have good in-plane mechanical properties, but there is no fiber reinforcement between the layers, and only the matrix resin plays the role of bonding and transmitting loads, so it is perpendicular to the direction of the layup and between the layups. performance is relatively weak. When subjected to external loads, the laminated composite material often produces interlaminar damage first, and the low interlaminar strength of the composite material also leads to poor damage resistance of the composite material. In order to improve these shortcomings of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/52B29C70/54
CPCB29C70/521B29C70/525B29C70/528
Inventor 王晓旭陈利房倩倩
Owner 江苏德晴新材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap