PVC crusting foaming building template and preparation method thereof

A technology for PVC formwork and building formwork, applied in the field of building materials, can solve the problems of becoming brittle and easy to deform, and achieve the effect of clear ratio, increased toughness and improved quality

Inactive Publication Date: 2017-03-01
宝鸡航翔新型建材科技有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a PVC crust foam building formwork and its preparation method, in which an appropriate amou

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] In order to make the technical means, creative features, goals and effects achieved by the present invention easy to understand, the present invention will be further described below in conjunction with specific embodiments.

[0016] A PVC crust foaming building template and a preparation method thereof, comprising the following raw materials: 100kg of PVC template recycled material; 75kg of rubbish milled material; 6kg of foam regulator; 2.5kg of stabilizer; 0.3kg of PE wax; Black 1kg; NBR 1kg; yellow foam 0.3kg; white foam 1kg; ZB 600.2kg.

[0017] Wherein, the stabilizer is one of barium-zinc composite stabilizer, calcium-zinc composite stabilizer and lead salt composite stabilizer.

[0018] Wherein, the foam regulator is an acrylate processing aid.

[0019] Wherein, the garbage grinding material is plant straw grinding.

[0020] Its preparation method is as follows:

[0021] 1) Put the recycled PVC formwork material into a pulverizer and pulverize it into powder;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVC crusting foaming building template and a preparation method thereof. The PVC crusting foaming building template is prepared from the following raw materials: 100 kg of a PVC template recycled material, 75 kg of a waste ground material, 6 kg of a foaming regulator, 2.5 kg of a stabilizing agent, 0.3 kg of PE wax, 1 kg of white carbon black, 1 kg of nitrile rubber, 0.3 kg of a yellow foaming agent, 1 kg of a white foaming agent and 2 kg of ZB600, wherein the stabilizing agent is one selected from the group consisting of a barium-zinc composite stabilizing agent, a calcium-zinc composite stabilizing agent and a lead-salt composite stabilizing agent; the foaming regulator is an acrylate processing additive; and the waste ground material is a plant straw ground powder. According to the invention, a proper amount of the nitrile rubber is adding into a formula, so the toughness of the template can be increased, and the problem of brittleness of the template in winter is solved; the white carbon black is added into the formula, so ultraviolet ray can be resisted, and the problem of easy deformation of the template in summer is solved; in addition, the plant straw ground powder is used as a filling material, so the themes of energy conservation and environmental protection at present are met.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a PVC-skinned foamed building formwork and a preparation method thereof. Background technique [0002] In the construction industry, the traditionally used formwork is basically wood formwork, but wood formwork is a loss of natural resources, and it is easy to rot, and the number of times of reuse is small, so it cannot be recycled again. Therefore, now wood formwork has basically been replaced by plastic formwork. replaced. In the initial stage of plastic formwork research, new raw materials such as resins and additives were basically used, resulting in high material and manufacturing costs. PVC crust foam building formwork is a representative of new materials. PVC crust foam building formwork is also called Chevron board and Andy board, its chemical composition is polyvinyl chloride, widely used in passenger cars, train car roof, box core layer, interior...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L97/02C08L23/06C08L9/02C08K3/36
Inventor 马文兵
Owner 宝鸡航翔新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap