Hydroxycucurbituril/graphene oxide composite material and preparation method thereof
The technology of a hydroxyl cucurbit ring and a composite material is applied in the field of materials, and can solve the problems of complicated operation and complicated preparation method, and achieve the effects of simple preparation method, convenient operation and short production cycle.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0042] (1) Graphene oxide was prepared by the Hummers method
[0043] Under ice bath, in a three-neck flask, stir and mix 3 g of flake graphite and 90 mL of concentrated sulfuric acid, then add 9 g of potassium permanganate in batches (10 additions), stir for 1 h, and then heat up the solution Keep at 35 °C for 2 h, then add 250 mL of deionized water to the system, then raise the temperature of the solution to 95 °C, keep for 30 min, then add 10 mL of hydrogen peroxide to the solution, and centrifuge the obtained solution. The solid obtained by centrifugation was washed 5 times with 5% hydrochloric acid, and finally, washed once with ethanol, and the product was dried in an oven at 50 °C for later use to obtain graphene oxide.
[0044] (2) Preparation of hydroxyl cucurbit ring / graphene oxide composites
[0045] 0.25 g of graphene oxide prepared by the Hummers method was ultrasonically dispersed in 150 mL of DMSO until completely dispersed and exfoliated to obtain the first so...
Embodiment 2
[0049] 0.25 g of graphene oxide prepared by the Hummers method was ultrasonically dispersed in 150 mL of DMF until it was completely dispersed and exfoliated to obtain the first solution.
[0050] Weigh 0.1 g of hydroxyl six-membered cucurbit rings and add them into the first solution, and stir at room temperature for 24 h to obtain the second solution. The second solution is subjected to centrifugation, and the separated solid is washed and dried to obtain a hydroxyl cucurbit ring / graphene oxide composite material.
[0051] Elemental analysis found that in the hydroxyl cucurbit ring / graphene oxide composite material prepared in this example, the proportion of the six-membered hydroxy cucurbit ring was about 5.0%.
Embodiment 3
[0053] 0.25 g of graphene oxide prepared by the Hummers method was ultrasonically dispersed in 150 mL of DMSO until completely dispersed and exfoliated to obtain the first solution.
[0054] Weighed 0.25 g of hydroxyl six-membered cucurbit rings and added them to the first solution, and stirred at room temperature for 24 h to obtain the second solution. The second solution is subjected to centrifugation, and the separated solid is washed and dried to obtain a hydroxyl cucurbit ring / graphene oxide composite material.
[0055] Elemental analysis found that in the hydroxyl cucurbit ring / graphene oxide composite material prepared in this example, the proportion of the six-membered hydroxy cucurbit ring was about 10.5%.
PUM
Property | Measurement | Unit |
---|---|---|
quality score | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap