A kind of manufacturing method of cucr alloy with large size, high density and high uniformity

A manufacturing method and high-density technology, applied in the manufacturing field of copper-based vacuum contact materials, to achieve the effects of improving current density distribution, simple process, and accelerating gas emission

Active Publication Date: 2018-03-09
HEFEI UNIV OF TECH +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from this that the method of patent 106086493A adopting rapid heating (heating rate of 50-300°C / min) is not suitable for preparing large-sized CuCr alloys with high density and high uniformity (diameter greater than 50mm)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of cucr alloy with large size, high density and high uniformity
  • A kind of manufacturing method of cucr alloy with large size, high density and high uniformity
  • A kind of manufacturing method of cucr alloy with large size, high density and high uniformity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The large-scale CuCr alloy of present embodiment is carried out as follows:

[0034] Step 1. Weigh 7.0kg of Cu powder and 3.0kg of Cr powder respectively, and mix them for 10 hours by mechanical mixing method to obtain uniform CuCr mixed powder; weigh 3.35kg of CuCr mixed powder for sintering;

[0035] Step 2. Fill the weighed CuCr mixed powder into the graphite mold; use a manual hydraulic press to pre-press the graphite mold filled with the CuCr mixed powder, and the pressure is ~ 10MPa;

[0036] Step 3. Wrap ~5mm thick carbon felt on the periphery of the graphite mold with CuCr mixed powder, then place it in the furnace of the spark plasma sintering system, evacuate it to below 5Pa, and feed DC pulse current to mix CuCr The powder is consolidated and formed, and the process conditions are:

[0037] The axial pressure is 30MPa;

[0038] The heating rate is 15°C / min (≤300°C) and 35°C / min (>300°C);

[0039] The sintering temperature is 850°C;

[0040] The holding ti...

Embodiment 2

[0043] The large-scale CuCr alloy of present embodiment is carried out as follows:

[0044] Step 1. Weigh 14.0kg of Cu powder and 6.0kg of Cr powder respectively, and mix them by mechanical mixing method for 10h to obtain uniform CuCr mixed powder; weigh 5.66kg of CuCr mixed powder for sintering;

[0045] Step 2. Fill the weighed CuCr mixed powder into the graphite mold; use a manual hydraulic press to pre-press the graphite mold filled with the CuCr mixed powder, and the pressure is ~ 10MPa;

[0046] Step 3. Wrap ~5mm thick carbon felt on the periphery of the graphite mold with CuCr mixed powder, then place it in the furnace of the spark plasma sintering system, evacuate it to below 5Pa, and feed DC pulse current to mix CuCr The powder is consolidated and formed, and the process conditions are:

[0047] The axial pressure is 60MPa;

[0048] The heating rate is 10°C / min (≤300°C) and 30°C / min (>300°C);

[0049] The sintering temperature is 800°C;

[0050] The holding time i...

Embodiment 3

[0053] The large-scale CuCr alloy of present embodiment is carried out as follows:

[0054] Step 1. Weigh 7.0kg of Cu powder and 3.0kg of Cr powder respectively, and mix them for 10 hours by mechanical mixing method to obtain uniform CuCr mixed powder; weigh 655g of CuCr mixed powder for sintering;

[0055] Step 2. Fill the weighed CuCr mixed powder into the graphite mold; use a manual hydraulic press to pre-press the graphite mold filled with the CuCr mixed powder, and the pressure is ~ 10MPa;

[0056] Step 3. Wrap ~5mm-thick carbon felt around the graphite mold with CuCr mixed powder, then place it in the furnace of the spark plasma sintering system, evacuate it to below 5Pa, and then pass a DC pulse current to the CuCr The mixed powder is consolidated and formed, and the process conditions are:

[0057] The axial pressure is 10MPa;

[0058] The heating rate is 20°C / min (≤300°C) and 50°C / min (>300°C);

[0059] The sintering temperature is 880°C;

[0060] The holding time...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method for a large-size high-density high-uniformity CuCr alloy. The manufacturing method is characterized in that CuCr mixed powder is solidified and formed through discharge plasma sintering, by optimizing a sintering die structure, the temperature is increased to 800 DEG C to 880 DEG C through a step heating manner at 10 DEG C / min to 50 DEG C / min and then kept for 2 minutes to 8 minutes while axial mechanical pressure is applied, and a sintered cylinder ingot with the diameter not smaller than 50 mm, the long diameter ratio of 0.04-1.0, the density larger than 99.0%, axial and radial fluctuation less than 1% and an uniform component structure can be obtained. According to the manufacturing method, different sintering conditions can be selected according to the size demand of the CuCr alloy, the process is simple, the period is short, the production efficiency is high, and the obtained CuCr alloy can be made into a finished product through a small amount of subsequent machining and then used as a part of a vacuum circuit breaker in large-power transmission and transformation equipment.

Description

technical field [0001] The invention relates to a method for manufacturing a copper-based vacuum contact material, in particular to a method for manufacturing a CuCr alloy with large size, high density and high uniformity. Background technique [0002] CuCr alloy is widely used as a contact material in medium and high voltage vacuum circuit breakers because of its good arc corrosion resistance and good breaking current capability. The performance of CuCr alloy mainly depends on the compactness and uniformity of its structure. Because the mutual solubility between Cu and Cr is very low and the wettability is poor, for a long time in the development of CuCr alloys, the powder metallurgy method was first used to prepare a porous Cr skeleton with a certain shape, and then infiltrated Cu to obtain CuCr. Alloy products; if necessary, cold or hot repress the infiltrated CuCr alloy to make the product meet the required density and strength. [0003] So far, the manufacturing metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/04C22C9/00B22F3/14
CPCB22F3/14B22F2998/10C22C1/0425C22C9/00B22F1/0003B22F3/02
Inventor 张久兴韩翠柳胡可杨新宇刘凯王小军师晓云杨平
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka