A kind of hydrophobic association type polymer and its preparation method and application

A hydrophobic association, polymer technology, applied in drilling compositions, chemical instruments and methods, etc., can solve the problems affecting the water solubility of the copolymer, economic pressure, construction difficulties, etc., and increase the resistance to divalent metal ions. , high viscosity, good water solubility

Active Publication Date: 2018-08-17
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Firstly, due to the introduction of hydrophobic monomers, the water solubility of the copolymer is greatly affected, which brings economic pressure and construction difficulties to the oil field distribution site

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophobic association type polymer and its preparation method and application
  • A kind of hydrophobic association type polymer and its preparation method and application
  • A kind of hydrophobic association type polymer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The present invention also provides a method for preparing a hydrophobic association polymer, the method comprising: in the presence of an initiator and water as a solvent, monomer D, monomer E and monomer F undergo a polymerization reaction, wherein, The monomer D is a monomer having a structure shown in formula (4), the monomer E is a monomer having a structure shown in formula (5), and the monomer F is a monomer having a structure shown in formula (6). Based on the total weight of the monomer D, the monomer E and the monomer F, the amount of the monomer D is 4-50% by weight, and the amount of the monomer E is 40-95% by weight, the amount of the monomer F is 0.05-10% by weight; the conditions of the polymerization reaction are such that the viscosity-average molecular weight of the polymer obtained after the polymerization reaction is 12 million-30 million;

[0028]

[0029] Among them, R 1 , R 5 and R 6 Each is independently H or C1-C4 alkyl, R 2 C1-C4 alkylen...

Embodiment approach

[0047] According to a preferred embodiment of the present invention, the preparation method of the hydrophobic association type polymer may specifically include the following steps:

[0048] (1) Under the condition that the pH value is 6-10, the monomer represented by the formula (4) and the monomer represented by the formula (5) are contacted with water, and nitrogen gas is blown in for 30 minutes to obtain a mixture solution;

[0049] (2) Under the protection of nitrogen, the mixture solution is contacted with the monomer represented by formula (6), a surfactant and an auxiliary agent, and mixed uniformly at 20-50° C. to obtain a micellar solution;

[0050] (3) Contacting the to-be-micellar solution with the initiator under the protection of nitrogen under the polymerization conditions, wherein the polymerization conditions are as follows: the polymerization temperature is 20-50°C; the polymerization time is 10-12h.

[0051] (4) After the polymerization reaction is completed...

Embodiment 1

[0061] This example is used to illustrate the hydrophobic association polymer and its preparation method provided by the present invention.

[0062] 1. Add 11.8g acrylamide (59% by mass ratio) and 8.0g 2-acrylamide-2-methylpropanesulfonic acid (40% by mass ratio) into a three-necked polymerization reaction bottle (ie, a polymerization bottle), Add 80.0 g of deionized water to dissolve to form an aqueous solution, then add sodium hydroxide to adjust the pH to 6.5, and blow nitrogen gas for 30 minutes;

[0063] 2. Under the protection of nitrogen, add 3.0g sodium lauryl sulfate, 0.2g hydrophobic monomer (n=1, mass ratio is 1%), 1.0g urea , placed in a 40°C water bath, stirred to disperse uniformly and form stable micelles;

[0064] 3. Under nitrogen protection, add 3.0 g of 0.1% potassium persulfate aqueous solution and 1.5 g of 0.1% sodium bisulfite aqueous solution, and maintain the polymerization reaction at 40° C. for 10 hours;

[0065] 4. After the polymerization is compl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear viscosityaaaaaaaaaa
surface tensionaaaaaaaaaa
shear viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrophobic associative polymer and preparing method and application thereof. The polymer comprises a structural unit A, a structural unit B and a structural unit C. The structural unit A is shown in the formula I, the structural unit B is shown in the formula II, and the structural unit C is shown in the formula III. With the weight of the polymer as a datum, the content of the structural unit A is 4%-50% by weight, the content of the structural unit B is 40%-95% by weight, and the content of the structural unit C is 0.05%-10% by weight; the viscosity average molecular weight of the polymer is 12,000,000 to 30,000,000. The provided hydrophobic associative polymer has the advantages of being good in water solubility, strong in viscosifying capacity, resistant to temperature and salt and good in surface activity, so that the polymer has a good oil displacement effect. The formula is shown in the description.

Description

technical field [0001] The invention relates to a hydrophobic association polymer and a preparation method, and the application of the hydrophobic association polymer as an oil displacement agent. Background technique [0002] Hydrophobic associative polymers refer to a class of water-soluble polymers obtained by introducing a small amount of hydrophobic structural units into the main chain of hydrophilic polymers by means of copolymerization or modification. This type of polymer has its unique solution properties , which is very different from conventional water-soluble polymers in terms of solution properties, has developed into one of the hotspots in the research of water-soluble polymer materials. [0003] Due to the small amount of hydrophobic units contained in the hydrophobic association polymer structure, the properties of the original polymer solution are greatly changed. In the dilute solution of the polymer, the intramolecular association occurs due to the hydrop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/56C08F220/58C08F220/70C08F4/40C08F2/26C09K8/588
Inventor 赵方园王晓春于芳杨捷
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com