Quick-drying high temperature dry film lubricant

A dry film lubricant, high temperature technology, used in lubricating compositions, petroleum industry, etc., can solve problems such as easy to be wiped off, loose lubricant, etc., achieve high economic use value, prolong life, good oxidation resistance and anti-oxidation. high temperature effect

Active Publication Date: 2019-05-10
中建材光芯科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is also a lubricant in the prior art, which uses liquid (such as alcohol) to make boron nitride into suspended lubricant particles, and then sprays or brushes it on the friction surface of the mold or mechanical parts, but this lubricant is loosely located in the mold Or on the surface of mechanical parts, and is very easy to be wiped off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The components of the quick-drying high-temperature dry film lubricant are as follows:

[0026] The quality of nano boron nitride powder is 60g,

[0027] Cellulose nitrate 6g (nitrogen content is 12.4wt%),

[0028] Polyurethane 1.5g,

[0029] Acetone 480mL,

[0030] Ethyl acetate 60mL;

[0031] 6g of cellulose nitrate with a nitrogen content of 12.4wt% was completely dissolved in 480mL of acetone, and after 1.5g of polyurethane was completely dissolved in 60mL of ethyl acetate, the two were mixed to obtain a mixed solution, and then 60g of cellulose with a particle size of 25nm The nano boron nitride powder was added to the above mixed solution, and after stirring at 1000rpm for 5 minutes, a quick-drying high-temperature dry film lubricant was obtained.

[0032] Use a bristle painting brush to soak in the above-mentioned quick-drying high-temperature dry film lubricant for 5 seconds, gently brush it on the friction surface of the mold twice, and wipe it lightly with...

Embodiment 2

[0034] The components of the quick-drying high-temperature dry film lubricant are as follows:

[0035] The composition of the quick-drying high-temperature dry film lubricant is as follows:

[0036] The quality of nano boron nitride powder is 50g,

[0037] Cellulose nitrate 5g (nitrogen content is lower than 8.0wt%),

[0038] Polyurethane 1.25g,

[0039] Acetone 500mL,

[0040] Ethyl acetate 50mL;

[0041] 5g of cellulose nitrate with a nitrogen content of 8.0wt% is completely dissolved in 500ml of acetone, 1.5g of polyurethane is completely dissolved in 50mL of ethyl acetate, and the two are mixed to obtain a mixed solution, and then 60g of cellulose with a particle size of 5nm The nano boron nitride powder was added to the above mixed solution, and after stirring at 1000rpm for 6 minutes, a quick-drying high-temperature dry film lubricant was obtained.

[0042] Use a bristle painting brush to soak in the above-mentioned quick-drying high-temperature dry film lubricant f...

Embodiment 3

[0044] The components of the quick-drying high-temperature dry film lubricant are as follows:

[0045] The quality of nano boron nitride powder is 40g,

[0046] Cellulose nitrate 4g (nitrogen content is lower than 12.3wt%),

[0047] Polyurethane 1g,

[0048] Acetone 540ml,

[0049] Ethyl acetate 33ml;

[0050] 4g of cellulose nitrate with a nitrogen content of 12.3wt% was completely dissolved in 540ml of acetone, and after 1.5g of polyurethane was completely dissolved in 33mL of ethyl acetate, the two were mixed to obtain a mixed solution, and then 40g of cellulose with a particle size of 10nm The nano boron nitride powder was added to the above mixed solution, and after stirring at 1000rpm for 5 minutes, a quick-drying high-temperature dry film lubricant was obtained.

[0051] Use a pig bristle painting brush to soak in the above-mentioned quick-drying high-temperature dry film lubricant for 5 seconds, gently brush it on the friction surface of the mold twice, and wipe it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
coating thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a quick drying type high-temperature dry-film lubricant. The lubricant is prepared from the following components in percentage by weight: 8%-12% of nano-boron nitride powder, 0.8%-1.2% of cellulose nitrate, 0.2%-0.3% of polyurethane, 75%-85% of acetone and 5%-12% of ethyl acetate. The dry-film lubricant is mainly used for lubrication protection and service life prolonging of a mold; the dry-film lubricant can be air-dried after covering the mold for 1-2 minutes; by the aid of the nano-boron nitride powder, the dry-film lubricant can have good oxidation resistance and high-temperature resistance and quite high economic use value, and the high-temperature resistance reaches 1000 DEG C.

Description

technical field [0001] The invention relates to a dry film lubricant, in particular to a quick-drying high temperature dry film lubricant. Background technique [0002] Lubricants are widely used on the friction surfaces of molds and mechanical parts to reduce friction and wear of materials. Compared with conventional grease lubrication, dry film lubricants can be effectively used under environmental conditions such as high temperature, high load, and high vacuum. [0003] In the prior art, the solid lubricant (molybdenum disulfide, graphite powder, etc.) is dispersed in an organic or inorganic bond, coated on the friction surface with the mold and mechanical parts, and dried to obtain a dry film lubricant coating , the film lubricant can reduce the friction and wear of materials, but its working temperature usually does not exceed 450°C. There is also a lubricant in the prior art, which uses liquid (such as alcohol) to make boron nitride into suspended lubricant particles...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M157/04C10M169/04C10N30/08C10N30/10C10N50/08
CPCC10M157/04C10M169/041C10M2201/003C10M2217/045C10M2217/06C10N2030/08C10N2030/10C10N2050/08C10N2020/06
Inventor 黄康胜冯跃冲宋普光石钰
Owner 中建材光芯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com