Composition for preparing catalyst having hydrocracking effect, catalyst, applications of catalyst, and hydrocracking method

A technology for hydrocracking and composition, applied in the directions of organic compound/hydride/coordination complex catalysts, chemical instruments and methods, physical/chemical process catalysts, etc. Corrosive and other problems

Active Publication Date: 2017-05-10
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using SiCl 4 The disadvantage of the isomorphic substitution method is that it is highly corrosive, the reaction is not easy to proceed uniformly, and the non-framework aluminum produced is difficult to elute, which reduces the pore smoothness of the zeolite. In addition, SiCl 4 The isomorphic substitution method produces little or no secondary pores
Use (NH 4 ) 2 SiF 6 Isomorphic substitution, although the reaction conditions are mild, the non-framework aluminum content in the prepared dealuminated zeolite is low, and there are few defect sites in the crystal structure, but when more than 50-60% of the zeolite framework aluminum is removed, the zeolite crystal structure is still seriously affected. Destruction, the insoluble fluoride mixed in the zeolite is not easy to wash off, and the residual fluoride will destroy the crystal structure of the zeolite at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for preparing catalyst having hydrocracking effect, catalyst, applications of catalyst, and hydrocracking method
  • Composition for preparing catalyst having hydrocracking effect, catalyst, applications of catalyst, and hydrocracking method
  • Composition for preparing catalyst having hydrocracking effect, catalyst, applications of catalyst, and hydrocracking method

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0130] (1) Disperse 100g (dry basis) NaY molecular sieve (produced by Sinopec Catalyst Changling Branch, whose physical and chemical property parameters are listed in Table 2 and Table 3 respectively) in 1500mL water, with stirring, at ambient temperature (25 ° C, The same below) was added dropwise at a constant speed to 200 mL of an aqueous solution containing 50 g of ammonium sulfate (purchased from Beijing Yili Chemical Reagent Factory) (the dropping time was controlled to be 30 min). After the ammonium sulfate aqueous solution was added dropwise, the stirring was stopped and the mixed solution was filtered, and the solid phase was washed with deionized water for 3 times, and then dried in an air atmosphere at 105° C. under normal pressure (1 standard atmospheric pressure, the same below) for 3 hours to obtain The sodium ion content of the exchanged molecular sieves is listed in Table 4.

[0131] (2) Place the exchanged molecular sieve prepared in step (1) in a tube furnace...

preparation Embodiment 2

[0157] (1) Disperse 100g (dry basis) NaY molecular sieve (same as Preparation Example 1) in 1500mL of water, and with stirring, add 300mL containing 50g of ammonium nitrate (purchased from Lee Chemical Reagent Factory) aqueous solution (control drop time is 50min). After the ammonium nitrate aqueous solution is added dropwise, stop stirring and filter the mixed solution, wash the solid phase with deionized water for 3 times, and dry it in an air atmosphere at 120°C for 3 hours under normal pressure to obtain an exchanged molecular sieve with a sodium ion content of Listed in Table 4.

[0158] (2) Mix the exchanged molecular sieve prepared in step (1) with water to obtain a slurry containing molecular sieve (55% by weight on a dry basis). Fill the slurry containing molecular sieves in a crucible (the specifications of the crucible: the inner diameter is 40 mm, the height is 40 mm, the same below), seal the crucible and place it in a muffle furnace, raise the temperature to 550...

preparation Embodiment 3

[0167] (1) Disperse 100g (dry basis) NaY molecular sieve (produced by Sinopec Catalyst Zhoucun Branch, whose physical and chemical properties are listed in Table 2 and Table 3 respectively) in 1300mL of water, and add dropwise at a constant speed at 35°C with stirring 100mL contains 45g of ammonium nitrate (purchased from Beijing Yili Chemical Reagent Factory) aqueous solution (controlling the dropping time to 40min). After the dropwise addition of the aqueous solution is completed, the stirring is stopped and the mixed solution is filtered. After the solid phase is washed with deionized water for 3 times, it is dried in an air atmosphere at 110°C for 3.5 hours under normal pressure, thereby obtaining an exchanged molecular sieve with a sodium ion content of Listed in Table 4.

[0168](2) Place 85g (dry basis) of the exchanged molecular sieve prepared in step (1) in a tube furnace, and continuously feed water vapor into the tube furnace (the rate of introduction of water vapor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a composition for preparing a catalyst having a hydrocracking effect, the catalyst prepared from the composition, and applications of the catalyst. The composition contains a carrier, a compound containing a group VIII metal element, a compound containing a group VIB metal and an organic additive, wherein the organic additive is selected from an organic acid and an organic amine, the carrier contains a dealuminzation Y-type molecular sieve and a heat-resistant inorganic oxide, the cell constant of the dealuminzation Y-type molecular sieve is 2.430-2.450 nm, the relative crystallinity is more than 65%, the secondary pore volume is 0.1-0.3 mL/g, the alkali metal element content is less than 0.2 wt% (calculated as the oxide), and the number of the non-skeleton aluminum in the unit cell is less than 3. The present invention further discloses a hydrocracking method using the catalyst. According to the present invention, the catalyst prepared from the composition has high catalyst activity and has high middle distillate selectivity, and the obtained tail oil has low BMCI value and high alkane content.

Description

technical field [0001] The present invention relates to the technical field of hydrocracking, in particular, the present invention relates to a composition for preparing a catalyst having a hydrocracking effect, and the catalyst prepared from the composition and its application. The present invention also relates to a method using the The hydrocracking catalyst of the catalyst. Background technique [0002] In recent years, the trend of heavy and inferior crude oil has become increasingly obvious worldwide. At the same time, the demand for middle distillates and reforming and steam cracking raw materials has continued to increase. This promotes the rapid development of heavy distillate processing technology, and catalyst is the most important and key factor. [0003] Hydrocracking technology can produce high-quality middle distillates, and the product variety and yield can be adjusted according to market demand. Through the combination and grading of various catalysts, naph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/16B01J31/34C10G47/20
Inventor 董松涛赵阳李明丰胡志海聂红辛靖赵广乐
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap