Preparation method for high-oil absorption microsphere-shaped white carbon black
A white carbon black and high oil absorption technology, applied in chemical instruments and methods, inorganic chemistry, and other chemical processes, can solve problems such as poor fluidity, poor slow-release effect, and low oil absorption value, and achieve easy-to-obtain raw materials and flow Good properties and dispersibility, less dust effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Specific steps are as follows:
[0017] 1. Refining of sodium silicate solution
[0018] Take water glass with a modulus of 3.40-3.50 and dissolve it in a static autoclave. After standing for clarification, take the supernatant to make a sodium silicate solution with a mass ratio concentration of 23%.
[0019] 2. Synthesis reaction
[0020] at 120m 3 The reactor was charged with 50 m 3 water, while adding 23% sodium silicate solution 5-6 m 3 , warming up to 85 o C, start the reaction after the temperature stabilizes, set the stirring frequency, add water glass and concentrated sulfuric acid dropwise at the same time, water glass drops 18.5-19.6 m per hour 3 , adding 0.8-1.1 m of concentrated sulfuric acid dropwise per hour 3 , monitor the pH value every 10 minutes to keep it at 10-11, the reaction is over for 105 minutes, continue to stir for 15 minutes, add acid until the pH is 4.5-5.0, and put it into the slurry tank after aging for 30 minutes.
[0021] 3. Filt...
Embodiment 2
[0028] The specific operation steps are as follows:
[0029] 1. Refining of sodium silicate solution
[0030] Take water glass with a modulus of 3.40-3.50 and dissolve it in a static autoclave. After standing for clarification, take the supernatant to make a sodium silicate solution with a mass ratio concentration of 20%.
[0031] 2. Synthesis reaction
[0032] at 120m 3 The reactor was charged with 50 m 3 Water, while adding 20% concentration of sodium silicate solution 5 ~ 6 m³, heated to 82 o C, start the reaction after the temperature stabilizes, add water glass and concentrated sulfuric acid dropwise at the same time under the condition of setting the stirring intensity, water glass drops 18.5-19.6 m per hour 3 , concentrated sulfuric acid is added dropwise at about 0.8-1.1 m per hour 3 , monitor the pH value every 10 minutes to keep it at 10-11, the reaction is over for 120 minutes, continue to stir for 15 minutes to bring the pH value of the peracid to 4.5-5.0, s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com