Plugging agent containing nano-particles and preparation method of plugging agent

A technology of nano-particles and plugging agents, applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of increasing the risk of shale well wall collapse, insufficient rock micro-pore and micro-fracture sealing ability, and filter cake Insufficient compactness and other problems, to achieve the effects of strong compactness, improved plugging ability, and improved stability

Inactive Publication Date: 2017-05-10
SINOPEC SSC +2
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the shortcomings or deficiencies of these technologies are: the formed filter cake is not dense enough, and the ability to seal the micropores and micro-cracks of the rock is not enough, resultin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] The plugging agent used in this embodiment includes the following components in 100 parts by weight:

[0023] 90 parts by weight of nanoemulsion;

[0024] 8 parts by weight of nano materials;

[0025] System stabilizer 2 parts by weight.

[0026] The preparation method of the nano material used in this embodiment includes:

[0027] First, the nano-silica, nano-titanium dioxide, and nano-graphite are mixed at a weight ratio of 6:1:3, and then used for later use. Then put stearic acid and NaOH with a weight ratio of 1:1 in a container, add water, and heat and stir at 40°C and 8000r / min. After the stearic acid and NaOH are all dissolved, add it to the nanoparticle mixture (with hard The weight ratio of fatty acid is 8-15:1). Stir at a constant temperature of 25°C and 5000 r / min for 30 min to 120 min, filter with suction, wash the organic matter on the surface with absolute ethanol, wash with water once, and dry to obtain the nanomaterial.

[0028] The preparation...

Example Embodiment

[0030] Example 2

[0031] The plugging agent used in this embodiment includes the following components in 100 parts by weight:

[0032] 80 parts by weight of nanoemulsion;

[0033] 14 parts by weight of nano materials;

[0034] System stabilizer 6 parts by weight.

[0035] The preparation method of the nano material used in this embodiment includes:

[0036] First, the nano-silica, nano-titanium dioxide, and nano-graphite are mixed in a weight ratio of 8:2:5, and then set aside. Then put stearic acid and NaOH with a weight ratio of 1:1 in a container, add water, and heat and stir at 40°C and 8000r / min. After the stearic acid and NaOH are all dissolved, add the nanoparticle mixture (with stearin The weight ratio of acid is 8-15:1). Stir at a constant temperature at 25°C and 5000 r / min for 30 to 120 minutes, filter with suction, wash the organic matter on the surface with absolute ethanol, wash again with water, and dry to obtain the nanomaterial.

[0037] The preparation method of the p...

Example Embodiment

[0039] Example 3

[0040] The plugging agent used in this embodiment includes the following components in 100 parts by weight:

[0041] 85 parts by weight of nanoemulsion;

[0042] 12 parts by weight of nano materials;

[0043] System stabilizer 3 parts by weight.

[0044] The preparation method of the nano material used in this embodiment includes:

[0045] Firstly, the nano-silica, nano-titanium dioxide, and nano-graphite are mixed in a weight ratio of 6:1:4, and then set aside. Then put stearic acid and NaOH with a weight ratio of 1:1 in a container, add water, and heat and stir at 40°C and 8000r / min. After the stearic acid and NaOH are all dissolved, add the nanoparticle mixture (with stearin The weight ratio of acid is 8-15:1). Stir at a constant temperature at 25°C and 5000 r / min for 30 to 120 minutes, filter with suction, wash the organic matter on the surface with absolute ethanol, wash again with water, and dry to obtain the nanomaterial.

[0046] The preparation method of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a plugging agent containing nano-particles and a preparation method. The plugging agent containing the nano-particles comprises, by weight, 80-90 parts of nano-emulsion, 8-14 parts of nano-materials and 2-6 parts of system stabilizers. The preparation method includes the steps: adding the nano-particles into the nano-emulsion at the temperature ranging from 20 DEG C to 40 DEG C; stirring the nano-particles at a high speed for 20-30 minutes by a magnetic stirrer; gradually adding the system stabilizers under low-speed stirring; stirring the materials at a high speed for 20-30 minutes to obtain the plugging agent. Other nano-particles are further added based on the nano-emulsion, the plugging capacity of the nano-emulsion is improved, pores and micro-cracks are plugged, a formed filter cake is compact, the quality of the filter cake can be improved, filter loss of drilling fluid is reduced, stability of the wall of a well is improved, the lubricating property of the drilling fluid can be improved, and penetration rate is increased.

Description

technical field [0001] The invention relates to the technical field of chemical materials for petroleum drilling, in particular to a nano-blocking agent for drilling fluid. Background technique [0002] In the process of oil and gas drilling, wellbore stability is a common problem. Wellbore instability can easily lead to downhole complex situations and accidents such as wellbore collapse, diameter shrinkage, leakage, pipe sticking and reservoir pollution, which will not only delay the drilling cycle, increase drilling costs, but also affect subsequent oil recovery operations. In severe cases, some wellbores may be scrapped or even the entire wellbore may be scrapped. It is estimated that the direct economic losses caused by wellbore instability in the world amount to hundreds of millions of dollars every year, seriously affecting the economic benefits of oilfield development. Therefore, it is of great significance to keep the wellbore stable during oil and gas drilling, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K8/03
CPCC09K8/03C09K2208/10C09K2208/12C09K2208/28C09K2208/34
Inventor 刘振东李公让侯业贵周守菊蓝强
Owner SINOPEC SSC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap