Wear-resistant leather and preparation method thereof

A technology of wear-resistant leather and parts by weight, used in textiles and paper making, etc., can solve the problems of wear resistance and unsatisfactory sewing resistance, and achieve better wear resistance and high-strength mechanical fatigue resistance. Effect of wear resistance and high strength mechanical fatigue resistance

Inactive Publication Date: 2017-05-24
广西鑫深科技有限公司
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] One of the objectives of the present invention is to provide a wear-resistant leather, which can solve the problems of unsatisfactory wear-resistant and sewing-resistant performance of ordinary polyvinyl chloride artificial leather.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1——wear-resisting leather and preparation method thereof

[0022] A. Scrape the surface layer slurry with a thickness of 0.15mm on the release paper, enter the oven, and dry at a temperature of 150°C; wherein, the surface layer slurry is made of 100kg of polyvinyl chloride paste with a polymerization degree of 1600-2000 Resin powder, 60kg of plasticizer, 1.5kg of heat stabilizer and 3kg of color paste were mixed, stirred for 20 minutes, and defoamed at -0.1MPa for 30 minutes with a vacuum stirring defoamer to obtain;

[0023] B. Scrape foaming layer slurry with a thickness of 0.6mm on the surface layer obtained in step A, enter the oven, and foam and dry at a temperature of 160°C; wherein, the foaming layer slurry has a polymerization degree of 100kg 800-1200 PVC paste resin powder, 70kg plasticizer, 1kg foaming agent, 2kg heat stabilizer and 2kg color paste are mixed and stirred for 30 minutes, then defoamed at 0.8MPa for 30 minutes with a vacuum stirring ...

Embodiment 2

[0027] Embodiment 2——wear-resisting leather and preparation method thereof

[0028] A. Scrape the surface layer slurry with a thickness of 0.2mm on the release paper, enter the oven, and dry at a temperature of 160°C; wherein, the surface layer slurry is made of 100kg of polyvinyl chloride paste with a polymerization degree of 1600-2000 Resin powder, 70kg of plasticizer, 2kg of heat stabilizer and 4kg of color paste were mixed, stirred for 20 minutes, and defoamed at -0.1MPa for 35 minutes with a vacuum stirring defoamer to obtain;

[0029] B. Scrape foaming layer slurry with a thickness of 0.7mm on the surface layer obtained in step A, enter the oven, and foam and dry at a temperature of 180°C; wherein, the foaming layer slurry has a polymerization degree of 100kg 800-1200 polyvinyl chloride paste resin powder, 80kg plasticizer, 2kg foaming agent, 2.5kg heat stabilizer and 3kg color paste are mixed and stirred for 30 minutes, then defoamed at 0.8MPa for 35 minutes with a va...

Embodiment 3

[0033] Embodiment 3——wear-resisting leather and preparation method thereof

[0034] A. Scrape the surface layer slurry with a thickness of 0.3mm on the release paper, enter the oven, and dry at a temperature of 180°C; wherein, the surface layer slurry is made of 100kg of polyvinyl chloride paste with a polymerization degree of 1600-2000 Resin powder, 80kg plasticizer, 3kg heat stabilizer and 5kg color paste were mixed and stirred for 20 minutes, and then defoamed for 40 minutes at 0.8MPa with a vacuum stirring defoamer to obtain;

[0035] B. Scrape foaming layer slurry with a thickness of 0.8mm on the surface layer obtained in step A, enter the oven, and foam and dry at a temperature of 185°C; wherein, the foaming layer slurry has a polymerization degree of 100kg 800-1200 PVC paste resin powder, 60kg plasticizer, 1.5kg foaming agent, 3kg heat stabilizer and 4kg color paste are mixed, stirred for 40 minutes, and defoamed at -0.1MPa with a vacuum stirring defoamer 40 minutes,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses wear-resistant leather and a preparation method thereof. The wear-resistant leather comprises a base fabric, an adhesive layer, a foaming layer, a surface layer and a surface treatment layer, wherein the surface layer comprises the following raw materials in parts by weight: 100 parts of polyvinyl chloride paste resin powder having a polymerization degree of 1600-2000, 60-80 parts of a plasticizer, 1-3 parts of a heat stabilizer and 3-5 parts of color paste; the surface treatment layer comprises the following raw materials in parts by weight: 80-90 parts of water-based polycarbon type PU resin, 15-20 parts of aliphatic polyurethane, 4-6 parts of an aziridine crosslinking agent, 3-5 parts of an isocyanate-based crosslinking agent, 15-20 parts of water-based silicone hand feeling agent, 6-8 parts of an acrylic thickening agent and 2-3 parts of a pH adjusting agent. The wear resistance and the mechanical fatigue resistance of the wear-resistant leather provided by the invention are improved by mainly improving the surface layer, the surface treatment layer, the foaming layer and the preparation method of the original polyvinyl chloride artificial leather.

Description

technical field [0001] The invention relates to the technical field of leather, in particular to leather with high abrasion resistance and a preparation method thereof. Background technique [0002] At present, most of the leather products on the market are ordinary polyvinyl chloride artificial leather. However, with the continuous progress of the automobile industry, its requirements for the required leather are getting higher and higher. The common PVC artificial leather on the market can no longer meet the high-strength wear resistance and sewing fatigue resistance of medium and high-end automotive interior fabrics. requirements. Therefore, how to improve properties such as wear resistance and sewing resistance on the basis of the original polyvinyl chloride artificial leather has become one of the technical problems urgently to be solved for the current polyvinyl chloride artificial leather. Contents of the invention [0003] One of the objectives of the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/06D06N3/14D06N3/00
CPCD06N3/0059D06N3/0077D06N3/0097D06N3/06D06N3/141D06N2209/103D06N2209/1685D06N2211/28
Inventor 黄燕双陈龙李志海黄国华卓李传杨开沈
Owner 广西鑫深科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com