A kind of hydrophobic stiffening agent and its preparation method and use method

A stiffening agent and hydrophobic type technology, which is applied in the field of hydrophobic stiffening agent and its preparation, can solve the problems affecting the waterproof effect of textiles, etc., and achieve the effect of improving printing and dyeing efficiency, reducing procedures, and good elasticity

Active Publication Date: 2019-02-12
苏州联胜化学有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The purpose of the present invention is to provide a hydrophobic stiffening agent to solve the technical problem that the environmental-friendly stiffening agent and the organic fluorine water repellent are treated in the same bath in the prior art, which will affect the waterproof effect of textiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophobic stiffening agent and its preparation method and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Step S101) Add 2 parts of dispersion stabilizer and 52.45 parts of deionized water into the reaction vessel; the dispersion stabilizer includes 1 part of polyvinyl alcohol 0599 and 1 part of modified polyvinyl alcohol RS-1717.

[0062] Step S102) heating up to 88° C., stirring at a speed of 180 rpm to 220 rpm for 30 minutes to form a mixed solution.

[0063] Step S103) After the dispersion stabilizer is completely dissolved in deionized water, the temperature is lowered to 70°C.

[0064] Step S104) Add 0.4 parts of the regulating acid to the reaction container, and continuously stir at a speed of 120 rpm to 150 rpm, and adjust the pH value of the mixed solution to 6; The regulating acid is formic acid.

[0065] Step S105) Adding 0.05 parts of an initiator into the reaction vessel; the initiator is ammonium persulfate.

[0066] Step S106) Keep the temperature at 70°C, add 45 parts of comonomer dropwise to the reaction vessel, and drop it in 3.5 hours; the 45 parts of c...

Embodiment 2

[0072] Step S201) Add 3 parts of dispersion stabilizer and 50.1 parts of deionized water into the reaction vessel; the dispersion stabilizer includes 1.5 parts of polyvinyl alcohol 1799 and 1.5 parts of modified polyvinyl alcohol RS-1717.

[0073] Step S202) heating up to 90° C., stirring at a speed of 180 rpm to 220 rpm for 40 minutes to form a mixed solution.

[0074] Step S203) After the dispersion stabilizer is completely dissolved in deionized water, the temperature is lowered to 75°C.

[0075] Step S204) Add 0.6 parts of the adjusting acid to the reaction container, and continuously stir at a speed of 120rpm-150rpm, and adjust the pH value of the mixed solution to 5; The regulating acid is acetic acid.

[0076] Step S205) adding 0.1 part of initiator into the reaction container; the initiator is sodium persulfate.

[0077] Step S206) Keep the temperature at 75°C, add 46 parts of comonomer dropwise to the reaction vessel, and drop it in 4 hours; the 46 parts of comonome...

Embodiment 3

[0083] Step S301) Add 4 parts of dispersion stabilizer and 46.6 parts of deionized water into the reaction vessel; the dispersion stabilizer includes 2 parts of polyvinyl alcohol 1799 and 2 parts of modified polyvinyl alcohol RS-1717.

[0084] Step S302) heating up to 92° C., stirring at a speed of 180 rpm to 220 rpm for 50 minutes to form a mixed solution.

[0085] Step S303) After the dispersion stabilizer is completely dissolved in deionized water, the temperature is lowered to 80°C.

[0086] Step S304) Add 0.8 parts of the regulating acid to the reaction container, and continuously stir at a speed of 120rpm-150rpm, and adjust the pH value of the mixed solution to 4; The regulating acid is citric acid.

[0087] Step S305) adding 0.2 part of initiator into the reaction container; the initiator is potassium persulfate.

[0088] Step S306) Keeping the temperature at 80° C., 48 parts of comonomers were added dropwise to the reaction vessel, and the drops were completed in 4.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a hydrophobic stiffening agent and a preparation method and a use method thereof. The hydrophobic stiffening agent is prepared from the following raw materials and components in percentage by weight: 2 to 5% of dispersive stabilizer, 45 to 50% of comonomer, 0.05 to 0.3% of initiator, 0.4 to 1% of adjusting acid, 0.1 to 0.6% of neutralizing alkaline, and 43 to 53% of deionized water.

Description

technical field [0001] The invention belongs to dyeing and finishing auxiliaries of textile products, and in particular relates to a hydrophobic stiffening agent and a preparation method and a use method thereof. Background technique [0002] Stiffening agent refers to a kind of textile auxiliary agent used for stiffening and finishing of textiles. Its main function is to improve the appearance of textiles, increase the elasticity and fullness of textiles, and endow textiles with stiffness, so that textiles can obtain rigidity, stiffness, elasticity, Thick feel. It has a wide range of applications in the textile industry, and can be used in curtains, mosquito nets, bags, tooling, interlinings and non-woven fabrics, etc. [0003] At present, the common stiffening agent products on the market mainly include: [0004] (1) Thermosetting type: such as (etherified) melamine resin, urea aldehyde resin, etc.; [0005] (2) Thermoplastic type: such as polyacrylate emulsion, polysty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/333C08F218/08C08F220/18C08F220/34
CPCC08F218/08D06M15/333D06M2200/12C08F220/1804C08F220/18C08F220/1818C08F220/34
Inventor 蔡润之涂胜宏
Owner 苏州联胜化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com