Antibacterial, low-odor and flame-retardant polypropylene composite material and preparation method for same

A technology of flame-retardant polypropylene and composite materials, applied in the field of plastics, can solve the problems of continuous fire accidents and economic losses, and achieve the effects of good thermal stability, reduced odor, and stable physical and chemical properties

Inactive Publication Date: 2017-06-13
ORINKO NEW MATERIAL CO LTD
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, fire accidents caused by household appliances have continued, causing huge economic losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial, low-odor and flame-retardant polypropylene composite material and preparation method for same
  • Antibacterial, low-odor and flame-retardant polypropylene composite material and preparation method for same
  • Antibacterial, low-odor and flame-retardant polypropylene composite material and preparation method for same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Take various raw materials respectively by formula ratio;

[0035]

[0036]

[0037] (2) Add the above-mentioned polypropylene resin, barium sulfate, high-efficiency antimony-free and non-precipitating flame retardant, deodorant masterbatch, antibacterial agent, antioxidant, lubricant, and nucleating agent into a high-speed mixer and mix at high speed for 2 minutes;

[0038] (3) Put the mixed components into a parallel twin-screw extruder to melt, extrude and granulate. The barrel temperature of the extruder is: 190°C, the screw speed is 500r / min, and the melt pressure is 1.6MPa ; The vacuum degree is -0.04~-0.06MPa, that is, the antibacterial, low-odor and flame-retardant polypropylene composite material can be obtained.

Embodiment 2

[0040] (1) Take various raw materials respectively by formula ratio;

[0041]

[0042] (2) Add the above-mentioned polypropylene resin, barium sulfate, high-efficiency antimony-free and non-precipitating flame retardant, deodorant masterbatch, antibacterial agent, antioxidant, lubricant, and nucleating agent into a high-speed mixer and mix at high speed for 3 minutes;

[0043] (3) Put the mixed components into a parallel twin-screw extruder to melt, extrude and granulate. The barrel temperature of the extruder is: 200°C, the screw speed is 550r / min, and the melt pressure is 1.8MPa ; The vacuum degree is -0.06~-0.08MPa, that is, the antibacterial, low-odor and flame-retardant polypropylene composite material can be obtained.

Embodiment 3

[0045] (1) Take various raw materials respectively by formula ratio;

[0046]

[0047] (2) Add the above-mentioned polypropylene resin, barium sulfate, high-efficiency antimony-free and non-precipitating flame retardant, deodorant masterbatch, antibacterial agent, antioxidant, lubricant, and nucleating agent into a high-speed mixer and mix at high speed for 2 minutes;

[0048] (3) Put the mixed components into a parallel twin-screw extruder to melt, extrude and granulate. The barrel temperature of the extruder is: 200°C, the screw speed is 600r / min, and the melt pressure is 1.7MPa ; The vacuum degree is -0.07~-0.09MPa, that is, the antibacterial, low-odor and flame-retardant polypropylene composite material is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial, low-odor and flame-retardant polypropylene composite material and a preparation method for the same. The polypropylene composite material is prepared from the following components in parts by weight: 60 to 85 parts of polypropylene, 5 to 15 parts of barium sulfate, 5 to 10 parts of an efficient antimony-free and precipitate-free flame retardant, 5 to 15 parts of a deodorization masterbatch, 0.5 to 1.5 parts of an antibacterial agent, 0.3 to 0.6 part of an antioxidant, 0.1 to 0.5 part of a nucleating agent and 0.5 to 1.0 part of a lubricant. The prepared antibacterial, low-odor and flame-retardant polypropylene composite material has efficient antibacterial performance, and the antibacterial rate is over 99 percent. In addition, the odor level of the prepared antibacterial, low-odor and flame-retardant polypropylene composite material is lower than the 3.5 level, and the flame retardancy reaches the UL94 V-2 level.

Description

technical field [0001] The invention relates to the technical field of plastics, in particular to an antibacterial, low-odor, flame-retardant polypropylene compound and a preparation method thereof. Background technique [0002] Polypropylene is a thermoplastic resin obtained by polymerizing propylene. It is usually a translucent, colorless solid, odorless and non-toxic. Due to its regular structure and high degree of crystallization, its melting point is as high as 167°C, which has the advantages of heat resistance and corrosion resistance; in addition, polypropylene has a low density and is the lightest general-purpose plastic, but PP has poor low-temperature impact and large molding shrinkage. [0003] Antibacterial plastic is a kind of plastic that can inhibit or kill bacteria, mold, yeast, algae and even viruses that contaminate itself in the use environment. It is a well-known new type of material that is suitable for health and hygiene. With the increasing awareness ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/06C08L101/00C08K13/02C08K3/30C08K3/00C08K5/20C08J3/22
CPCC08J3/223C08L23/12C08L23/14C08J2323/14C08J2323/12C08L2205/24C08L2201/08C08L2201/02C08L2205/03C08J2400/00C08K2201/011C08L23/06C08L101/00C08K13/02C08K2003/3045C08K3/015C08K5/20
Inventor 邢纪普范保林宋钰吕游任东方
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com