Heat-resistant steel based WC40 steel bond hard alloy guide roller and manufacturing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of steel-bonded hard alloy and manufacturing method, applied in the field of steel rolling guide rolls, to achieve excellent physical and mechanical properties, reduce production costs, and overcome the effects of easy breakage
Inactive Publication Date: 2017-06-30
DANYANG JIAWEI WEAR RESISTANT MATERIAL TECH CO LTD
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
There are also reports abroad about the application of steel-bonded hard alloys in hot work dies. For example, the United States and other countries have used steel-bonded hard alloys to make single-groove or double-groove rolls for hot-rolled threaded steel bars, and for manufacturing high-speed rolling mills. Guide roller; while there are fewer reports in this area in our country
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] The manufacturing process of the heat-resistant steel-based WC40 steel-bonded cemented carbide guide roller of the present invention generally includes the following steps:
[0032] (1) Guide roller material:
[0033] The mass percentage of the chemical composition of the material is C0.30%, Cr2.5%, Mo2.0%, W1.9%, V0.35%, Mn0.6%, Si0.4%, WC40%, and the balance is Fe
[0034] (2) Manufacture and processing of guide rollers:
[0035] 1) Forging the heat-resistant steel-based WC40 steel-bonded hard alloy manufactured by powder metallurgy;
[0036] 2) Spheroidizing and annealing the forged heat-resistant steel-based WC40 steel-bonded hard alloy to make the hardness of the steel-bonded hard alloy
[0037] 3) The steel-bonded cemented carbide after spheroidizing annealing is processed according to the size required by the guide roller product, and a certain amount of grinding is reserved for the outer size of the guide roller and the inner hole of the bearing;
[003...
Embodiment 2
[0044] The manufacturing process of the heat-resistant steel-based WC40 steel-bonded cemented carbide guide roller of the present invention generally includes the following steps:
[0045] (1) Guide roller material:
[0046] The mass percentage of the chemical composition of the material is C0.5%, Cr4.5%, Mo3.5%, W3.6%, V0.85%, Mn0.7%, Si0.6%, WC40%, and the balance is Fe;
[0047] (2) Manufacture and processing of guide rollers:
[0048] 1) Forging the heat-resistant steel-based WC40 steel-bonded hard alloy manufactured by powder metallurgy;
[0049] 2) Spheroidizing and annealing the forged heat-resistant steel-based WC40 steel-bonded hard alloy to make the hardness of the steel-bonded hard alloy
[0050] 3) The steel-bonded cemented carbide after spheroidizing annealing is processed according to the size required by the guide roller product, and a certain amount of grinding is reserved for the outer size of the guide roller and the inner hole of the bearing;
[0...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a heat-resistant steel based WC40 steel bond hard alloy guide roller and a manufacturing method thereof. The guide roller adopts heat-resistant steel based WC40 steel bond hard alloy comprising the chemical components of, by mass, 0.25-0.5% of C, 2.0-5.0% of Cr, 1.0-4.0% of Mo, 1.0-4.0% of W, 0.25-0.85% of V, 0.6-0.7% of Mn, 0.4-0.6% of Si, 40% of WC and the balance Fe. Then the heat-resistant steel based WC40 steel bond hard alloy is forged, annealed, machined, subjected to heated treatment, ground and inspected, and the final guide roller is obtained. The steel bond hard alloy guide roller prepared through the method has the excellent physical and mechanical properties such as high hardness, abrasion resistance, high-temperature-oxidation resistance and thermal shock resistance, the service life of the guide roller is prolonged, the steel rolling production efficiency and product quality are improved, the production cost is low, and the guide roller has quite high cost performance, economic benefits and social benefits.
Description
technical field [0001] The invention relates to a steel rolling guide roll, in particular to a heat-resistant steel-based WC40 steel-bonded hard alloy guide roll used for a rolling guide device of a continuous rolling system and a manufacturing method thereof. Background technique [0002] The guide device refers to an important part that guides and guards the rolled piece to enter and exit the rolling mill during the steel rolling production process. deformation. Whether the design and use of the guide device is appropriate will directly affect the quality of the product and the production capacity of the rolling mill. [0003] The rolling guide device is a guide device that guides the rolled piece into the roll pass of the rolling mill when the rolling mill is rolling profiles, bars or wires. The guide roller is mainly a guiding equipment device for rolling steel that guides and assists the rapid passage of rolling billets or finished products. The guide roller is the mo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more