A kind of multi-ion antibacterial ceramic filter material and preparation method thereof
A multi-ion, antibacterial ceramic technology, applied in the field of water purification materials, can solve the problems of high renewal cost and inconvenience, and achieve the effects of fast adsorption, improved antibacterial ability, and strong pollution interception ability.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] A multi-ion antibacterial ceramic filter material, its raw materials include the following components by weight: 100 parts of starch slurry, 75 parts of kaolin particles, 125 parts of synthetic zeolite, 100 parts of activated carbon, 50 parts of quartz sand, 100 parts of ammonium carbonate, multi-ion 75 parts of antibacterial agent and 125 parts of water.
[0040] The preparation method of the starch slurry is as follows: starch with a mass ratio of 1:1.5 and hot water at 90° C. are placed in a stirrer, and stirred until a uniform viscous slurry is formed to obtain the starch slurry.
[0041] The preparation method of the kaolin particles is as follows: take kaolin with a silicon dioxide content of not less than 99%, pulverize it, and then place it in a ball mill for ball milling for 45 minutes; take it out after ball milling, filter and screen, and select a particle size of 300-1000 mesh Kaolin granules.
[0042] The preparation method of the synthetic zeolite is as f...
Embodiment 2
[0052] A multi-ion antibacterial ceramic filter material, its raw materials include the following components by weight: 95 parts of starch slurry, 70 parts of kaolin particles, 120 parts of synthetic zeolite, 95 parts of activated carbon, 45 parts of quartz sand, 95 parts of ammonium carbonate, multi-ion 70 parts of antibacterial agent and 60 parts of water.
[0053] The preparation method of the starch slurry is as follows: starch with a mass ratio of 1:1 and hot water at 85° C. are placed in a stirrer, and stirred until a uniform viscous slurry is formed to obtain a starch slurry.
[0054] The preparation method of the kaolin particles is as follows: take kaolin with a silicon dioxide content of not less than 99%, pulverize it, and then place it in a ball mill for ball milling for 30 minutes; take it out after ball milling, filter and screen, and select a particle size of 300-1000 mesh Kaolin granules.
[0055] The preparation method of the synthetic zeolite is as follows: ...
Embodiment 3
[0065] A multi-ion antibacterial ceramic filter material, its raw materials include the following components by weight: 105 parts of starch slurry, 80 parts of kaolin particles, 130 parts of synthetic zeolite, 105 parts of activated carbon, 55 parts of quartz sand, 105 parts of ammonium carbonate, multi-ion 80 parts of antibacterial agent and 190 parts of water.
[0066] The preparation method of the starch slurry is as follows: starch with a mass ratio of 1:2 and hot water at 95° C. are placed in a stirrer, and stirred until a uniform viscous slurry is formed to obtain a starch slurry.
[0067] The preparation method of the kaolin particles is as follows: take kaolin with a silicon dioxide content of not less than 99%, pulverize it, and then place it in a ball mill for ball milling for 60 minutes; take it out after ball milling, filter and screen, and select a particle size of 300-1000 mesh Kaolin granules.
[0068]The preparation method of the synthetic zeolite is as follow...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size (mesh) | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
| particle size (mesh) | aaaaa | aaaaa |