Titanium dioxide with high weather resistance and preparation method thereof

A technology of titanium dioxide and weather resistance, applied in the field of titanium dioxide, can solve the problems of non-dense titanium dioxide film and poor weather resistance, and achieve the effect of reducing photocatalytic activity and improving weather resistance and dispersibility.

Inactive Publication Date: 2017-07-14
PANGANG GROUP RESEARCH INSTITUTE CO LTD
View PDF7 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: the titanium dioxide film prepared by the prior art is not dense, and the weather resistance is not good, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The invention provides a preparation method of high weather resistance titanium dioxide, comprising the following steps:

[0027] a. The first layer of aluminum oxide coating

[0028] Add a dispersant to the titanium dioxide slurry, heat to 50-90°C, add acid to adjust the pH value to 4.0-6.0 or add alkali to adjust the pH value to 8.0-10.0, add aluminum raw materials, and keep the pH value at 4.0-6.0 or 8.0- 10.0, aging for 0.5-2 hours to obtain a titanium dioxide slurry coated with alumina;

[0029] b. The second layer of silica coating

[0030] Add acid to the alumina-coated titania slurry obtained in step a to adjust the pH to 0.1-3.0, then add sodium silicate and acid to adjust the pH to 0.1-3.0, adjust the temperature to 50-100°C, and mature for 0.5 ~3h;

[0031] c. The third layer of aluminum oxide coating

[0032] Adjust the temperature of the titanium dioxide slurry aged in step b to 50-90°C, add aluminum raw materials, adjust the pH value to 2.0-10.0, and a...

Embodiment 1

[0046] Example 1 Preparation of high weather resistance titanium dioxide by the technical method of the present invention

[0047]Take 1000mL of sulfuric acid method titanium dioxide slurry before coating, the concentration is 300g / L, add sodium hexametaphosphate as a dispersant of 0.2% by weight of titanium dioxide, adjust the pH value to 4.0 with sulfuric acid, heat to 50°C, and add 100g at the same time while stirring / L sodium metaaluminate and 10% sulfuric acid, maintain the pH between 3.8-4.2, add sodium metaaluminate as 0.5% of the weight of untreated titanium dioxide, add 30 minutes, and mature for 30 minutes. Raise the temperature to 90°C, adjust the pH value to 2.0 with sulfuric acid, and add 100g / L sodium silicate solution (as SiO 2 ) and 10% dilute sulfuric acid to keep the pH value of the slurry between 1.8 and 2.2, the total amount of sodium silicate solution added dropwise is 3% of the weight of untreated titanium dioxide, and the dropwise addition is completed ...

Embodiment 2

[0049] Example 2 Preparation of high weather resistance titanium dioxide by the technical method of the present invention

[0050] Take 1000mL of chlorinated titanium dioxide before coating slurry, the concentration is 500g / L, add the dispersant monoisopropanolamine accounting for 0.3% of the weight of titanium dioxide, adjust the pH value to 7.0 with hydrochloric acid, heat to 70°C, and stir at the same time Add 100g / L sodium metaaluminate and 10% sulfuric acid to maintain the pH between 6.8-7.2. The amount of sodium metaaluminate added is 1.0% of the weight of the untreated titanium dioxide. The addition is completed in 30 minutes and matured for 30 minutes. Raise the temperature to 90°C, adjust the pH value to 0.8 with hydrochloric acid, add sodium silicate (calculated as SiO 2 meter), control the pH value of the slurry to be less than 3.0, and ripen for 120 minutes after the dropwise addition.

[0051] Add 100g / L sodium metaaluminate in 30min, add the amount of sodium met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of titanium dioxide, and in particular relates to a highly weather-resistant titanium dioxide and a preparation method thereof. Aiming at the problems that the titanium dioxide film prepared by the prior art is not dense and has poor weather resistance, the present invention provides a method for preparing titanium dioxide with high weather resistance, which comprises the following steps: a. adding a dispersant to the titanium dioxide slurry, and then adding The aluminum raw material is matured to obtain a titanium dioxide slurry coated with alumina; b, adding acid to the titanium dioxide slurry obtained in step a to adjust the pH value to 0.1 to 3.0, then adding sodium silicate and acid, and curing; c, the step b The obtained titanium dioxide slurry is added with aluminum raw material, matured, filtered, washed, dried, ultrafinely pulverized and organically treated to obtain titanium dioxide with high weather resistance. The invention prepares the titanium dioxide with a three-layer coating film, which has good film compactness and high weather resistance, and the preparation method is simple to operate and is convenient for popularization and implementation.

Description

technical field [0001] The invention belongs to the technical field of titanium dioxide, and in particular relates to a highly weather-resistant titanium dioxide and a preparation method thereof. Background technique [0002] Due to its semiconductor properties, titanium dioxide has strong photocatalytic activity, and can degrade organic matter in contact with it under sunlight, especially ultraviolet radiation, causing yellowing and pulverization of coatings. In order to improve the weather resistance of titanium dioxide pigments, titanium dioxide is usually coated with an inorganic surface to isolate titanium dioxide from the surrounding organic matter to improve its weather resistance. [0003] Commonly used coating materials are silica, alumina, zirconia, etc. Among them, titanium dioxide coated with dense silicon oxide has the best weather resistance. However, the current common practice is to deposit silicon oxide first, and then deposit aluminum oxide, and the dense...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/36C09C3/06C09C3/08C09C3/10
CPCC09C1/3661C09C1/3692C09C3/006C09C3/063
Inventor 刘勇吕波王海波吴小平
Owner PANGANG GROUP RESEARCH INSTITUTE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap